Sag resistant acoustical ceiling panel with a filled latex binder system that enhances strength and durability
Described herein is a building panel comprising a body, the body comprising: a fiber; a latex binder present in an amount ranging from about 3 wt. % to about 10 wt. % based on the total weight of the body; and an inorganic particle having an average particle size ranging from about 1 micron to about 13 microns; wherein the inorganic particle and the binder are present in a weight ratio ranging from about greater than 1:1 to about 6:1.
1. A building panel comprising a body, the body comprising:
a fiber;
a latex binder present in an amount ranging from about 3 wt. % to about 10 wt. % based on the total weight of the body;
calcium carbonate particle having an average particle size ranging from about 4 microns to about 6 microns; and
an ionic charge-modifying component present in an amount ranging from about 30 wt. % to about 60 wt. % based on the total weight of the latex binder;
wherein the ionic charge-modifying component comprises aluminum sulfate;
wherein the calcium carbonate particle and the latex binder are present in a weight ratio of 3:1; and
wherein the body comprises a first major surface opposite a second major surface and a plurality of side surfaces extending between the first major surface and the second major surface, wherein the body has a porosity ranging from about 80% to about 98% as measured between the first major surface, the second major surface, and the plurality of side surfaces.
2. The building panel according to claim 1 , wherein the average particle size of the inorganic particle ranges is about 5 microns.
3. The building panel according to claim 1 , wherein the fiber is present in an amount ranging from about 65 wt. % to about 95 wt. % based on the total weight of the body.
4. The building panel according to claim 1 , wherein the amount of latex binder ranges from about 4 wt. % to about 7 wt. % based on the total weight of the body.
5. The building panel according to claim 1 , wherein the fiber is an inorganic fiber selected from the group consisting of mineral wool, fiberglass, and combinations thereof.
6. The building panel according to claim 1 , wherein the body has an airflow resistance less than about 200 MKS rayls as measured between the first major surface and the second major surface.
7. The building panel according to claim 1 , wherein the body has a bulk density ranging from about 0.15 g/cm 3 to about 0.3 g/cm 3 as measured between the first major surface, the second major surface, and the plurality of side surfaces.
8. The building panel according to claim 1 , wherein the ionic charge-modifying component comprises hydrated potassium aluminum sulfate.
9. A building panel comprising a body, the body comprising:
an inorganic fiber in an amount ranging from about 70 wt. % to about 95 wt. % based on the total weight of the body;
a latex binder in an amount ranging from about 3 wt. % to about 10 wt. %; and
an inorganic particle comprising kaolin present in an amount ranging from about 3 wt. % to about 30 wt. % based on the total weight of the body, wherein the kaolin particle has an average size ranging from about 8 micron to about 13 microns; and
wherein the body comprises a first major surface opposite a second major surface and a plurality of side surfaces extending between the first major surface and the second major surface, wherein the body has a porosity ranging from about 80% to about 98% as measured between the first major surface, the second major surface, and the plurality of side surfaces; and
wherein the body has an airflow resistance less than about 200 MKS rayls as measured between the first major surface and the second major surface.
10. The building panel according to claim 9 , wherein the amount of the inorganic particle ranges from about 6 wt. % to about 25 wt. % based on the total weight of the body.
11. The building panel according to claim 9 , wherein the latex binder comprises a polymer having a glass transition temperature ranging between about 60° C. and about 120° C.
12. The building panel according to claim 9 , wherein the inorganic fiber is selected from the group consisting of mineral wool, fiberglass, and combinations thereof.
13. The building panel according to claim 9 , wherein the inorganic particle further comprises calcium carbonate.
14. The building panel according to claim 9 , wherein the body further comprises an ionic charge-modifying component selected from aluminum sulfate, poly(diallyldimethylammonium chloride), or a combination thereof.
15. The building panel according to claim 14 , wherein the ionic charge-modifying component is present in an amount ranging from about 20 wt. % to about 70 wt. % based on the total weight of the latex binder.
16. A building panel comprising a body having a first major surface opposite a second major surface, the body comprising:
an inorganic fiber;
a latex binder comprising a copolymer of poly(styrene-acrylate);
calcium carbonate particle having an average size of about 5 microns;
an ionic charge-modifying component comprising poly(diallyldimethylammonium chloride) present in an amount ranging from about 0.1 wt. % to about 4.0 wt. % based on the total dry-weight of the body; and
wherein the calcium carbonate particle and the latex binder are present in a weight ratio of about 3:1, and wherein the body has an airflow resistance less than about 200 MKS rayls as measured between the first major surface and the second major surface.
17. The building panel according to claim 16 having an NRC ranging from about 0.6 to about 0.99.
18. The building panel according to claim 1 having an NRC ranging from about 0.6 to about 0.99.