Halogen-free flame-retardant polyamide (PA) composite and preparation method thereof
A halogen-free flame-retardant polyamide (PA) composite includes the following components in parts by weight: 20 to 50 parts of an aliphatic PA, 10 to 30 parts of an aromatic PA, 20 to 30 parts of a halogen-free flame retardant, 10 to 50 parts of a glass fiber, 1 to 5 parts of a char-forming agent, and 0 to 5 parts of an additive, where the aromatic PA is at least one selected from the group consisting of PA66/6T, PA MXD6, and PA6T/6I and the char-forming agent is at least one selected from the group consisting of dipentaerythritol (DPE) and tripentaerythritol (TPE). In the halogen-free flame-retardant PA composite, the aromatic PA itself has high-temperature resistance and aging resistance and exhibits a synergistic effect with a dense carbon layer formed by the char-forming agent during aging. The present disclosure discloses a preparation method of the halogen-free flame-retardant PA composite.
1 . A halogen-free flame-retardant polyamide (PA) composite, comprising the following components in parts by weight: 20 to 50 parts of an aliphatic PA, 10 to 30 parts of an aromatic PA, 20 to 30 parts of a halogen-free flame retardant, 10 to 50 parts of a glass fiber, 1 to 5 parts of a char-forming agent, and 0 to 5 parts of an additive, wherein the aromatic PA is at least one selected from the group consisting of PA66/6T, PA MXD6, and PA6T/6I; and the char-forming agent is at least one selected from the group consisting of dipentaerythritol (DPE) and tripentaerythritol (TPE); and
wherein the halogen-free flame retardant is a mixture of aluminum diethylphosphinate (ADP), boehmite, and zinc borate, and the ADP, the boehmite, and the zinc borate are in a weight ratio of (15-16): (4-5): (2-3).
2 . The halogen-free flame-retardant PA composite according to claim 1 , wherein the aromatic PA is at least one selected from the group consisting of PA66/6T and PA6T/6I; and the char-forming agent is DPE.
3 . The halogen-free flame-retardant PA composite according to claim 1 , wherein the aliphatic PA is at least one selected from the group consisting of PA6, PA 46, PA 66, PA56, and PA610.
4 . The halogen-free flame-retardant PA composite according to claim 3 , wherein the aliphatic PA is PA 66.
5 . The halogen-free flame-retardant PA composite according to claim 1 , wherein the glass fiber is at least one selected from the group consisting of E-glass fiber, H-glass fiber, R,S-glass fiber, D-glass fiber, C-glass fiber, and a quartz glass fiber.
6 . The halogen-free flame-retardant PA composite according to claim 1 , comprising the following components in parts by weight: 20 to 50 parts of the aliphatic PA, 15 to 25 parts of the aromatic PA, 20 to 30 parts of the halogen-free flame retardant, 10 to 50 parts of the glass fiber, 1.5 to 3 parts of the char-forming agent, and 0 to 5 parts of the additive.
7 . The halogen-free flame-retardant PA composite according to claim 1 , wherein the additive is at least one selected from the group consisting of an antioxidant and a lubricant; the antioxidant is a hindered phenol antioxidant; and the lubricant is at least one selected from the group consisting of a higher fatty acid, a higher fatty acid metal salt, a higher fatty acid ester, and a higher fatty acid amide.
8 . A preparation method of the halogen-free flame-retardant PA composite according to claim 1 , comprising: pre-mixing the components other than the glass fiber in a high-speed mixer to obtain a premix, subjecting the premix to melt-mixing with the glass fiber in a twin-screw extruder, and conducting extrusion granulation; and subjecting a PA material obtained from the extrusion granulation to injection-molding to obtain the halogen-free flame-retardant PA composite, wherein a screw of the twin-screw extruder has a length-to-diameter ratio of 40:1 to 48:1; a temperature of a screw cylinder is 240° C. to 300° C.; and a rotational speed of the screw is 300 rpm to 500 rpm.
9 . A preparation method of the halogen-free flame-retardant PA composite according to claim 2 , comprising: pre-mixing the components other than the glass fiber in a high-speed mixer to obtain a premix, subjecting the premix to melt-mixing with the glass fiber in a twin-screw extruder, and conducting extrusion granulation; and subjecting a PA material obtained from the extrusion granulation to injection-molding to obtain the halogen-free flame-retardant PA composite, wherein a screw of the twin-screw extruder has a length-to-diameter ratio of 40:1 to 48:1; a temperature of a screw cylinder is 240° C. to 300° C.; and a rotational speed of the screw is 300 rpm to 500 rpm.
10 . A preparation method of the halogen-free flame-retardant PA composite according to claim 3 , comprising: pre-mixing the components other than the glass fiber in a high-speed mixer to obtain a premix, subjecting the premix to melt-mixing with the glass fiber in a twin-screw extruder, and conducting extrusion granulation; and subjecting a PA material obtained from the extrusion granulation to injection-molding to obtain the halogen-free flame-retardant PA composite, wherein a screw of the twin-screw extruder has a length-to-diameter ratio of 40:1 to 48:1; a temperature of a screw cylinder is 240° C. to 300° C.; and a rotational speed of the screw is 300 rpm to 500 rpm.
11 . A preparation method of the halogen-free flame-retardant PA composite according to claim 4 , comprising: pre-mixing the components other than the glass fiber in a high-speed mixer to obtain a premix, subjecting the premix to melt-mixing with the glass fiber in a twin-screw extruder, and conducting extrusion granulation; and subjecting a PA material obtained from the extrusion granulation to injection-molding to obtain the halogen-free flame-retardant PA composite, wherein a screw of the twin-screw extruder has a length-to-diameter ratio of 40:1 to 48:1; a temperature of a screw cylinder is 240° C. to 300° C.; and a rotational speed of the screw is 300 rpm to 500 rpm.
12 . A preparation method of the halogen-free flame-retardant PA composite according to claim 6 , comprising: pre-mixing the components other than the glass fiber in a high-speed mixer to obtain a premix, subjecting the premix to melt-mixing with the glass fiber in a twin-screw extruder, and conducting extrusion granulation; and subjecting a PA material obtained from the extrusion granulation to injection-molding to obtain the halogen-free flame-retardant PA composite, wherein a screw of the twin-screw extruder has a length-to-diameter ratio of 40:1 to 48:1; a temperature of a screw cylinder is 240° C. to 300° C.; and a rotational speed of the screw is 300 rpm to 500 rpm.
13 . A preparation method of the halogen-free flame-retardant PA composite according to claim 7 , comprising: pre-mixing the components other than the glass fiber in a high-speed mixer to obtain a premix, subjecting the premix to melt-mixing with the glass fiber in a twin-screw extruder, and conducting extrusion granulation; and subjecting a PA material obtained from the extrusion granulation to injection-molding to obtain the halogen-free flame-retardant PA composite, wherein a screw of the twin-screw extruder has a length-to-diameter ratio of 40:1 to 48:1; a temperature of a screw cylinder is 240° C. to 300° C.; and a rotational speed of the screw is 300 rpm to 500 rpm.
14 . A preparation method of the halogen-free flame-retardant PA composite according to claim 8 , comprising: pre-mixing the components other than the glass fiber in a high-speed mixer to obtain a premix, subjecting the premix to melt-mixing with the glass fiber in a twin-screw extruder, and conducting extrusion granulation; and subjecting a PA material obtained from the extrusion granulation to injection-molding to obtain the halogen-free flame-retardant PA composite, wherein a screw of the twin-screw extruder has a length-to-diameter ratio of 40:1 to 48:1; a temperature of a screw cylinder is 240° C. to 300° C.; and a rotational speed of the screw is 300 rpm to 500 rpm.