Glass ceramics and methods of making such
The present invention relates to a glass ceramic material comprising a core-rim structure, wherein the core-rim structure comprises an amorphous SiO 2 matrix, ZrO 2 crystals, and hardness-enhancing additive, the ZrO 2 crystals are present in cores that are at least partly surrounded by a rim comprising hardness-enhancing additive.
1 . A glass ceramic material comprising zirconium dioxide crystals embedded in an amorphous silicon dioxide matrix and at least one hardness enhancing additive, wherein the zirconium dioxide crystals form cores and the cores are at least partly surrounded by rims, wherein the rims comprise an intergranular phase, and wherein the intergranular phase comprises at least silicon dioxide, zirconium dioxide and at least one hardness-enhancing additive, and wherein the concentration in weight percent of the hardness-enhancing additive is higher in the rims than in the amorphous silica matrix and in the cores.
2 . The glass ceramic material according to claim 1 , wherein at least a portion of the cores are connected with at least one adjacent other core forming a grain boundary between the cores, and wherein the concentration of hardness-enhancing additive is higher in the grain boundaries than in the parts of the rim in contact with the silicon dioxide matrix.
3 . The glass ceramic material according to claim 1 , wherein the material comprises 2-10 weight % of hardness-enhancing additive.
4 . The glass ceramic material according to claim 1 , wherein the intergranular phase is amorphous.
5 . The glass ceramic material according to claim 1 , wherein at least 90%, or at least 95% of the zirconium dioxide crystals have an average crystal size of 100 nm or less.
6 . The glass ceramic material according to claim 1 , wherein the zirconium dioxide crystals have an ellipsoidal shape.
7 . The glass ceramic material according to claim 1 , wherein the zirconium dioxide comprises either tetragonal zirconium dioxide or a mixture of tetragonal zirconium dioxide and monoclinic zirconium dioxide, wherein at least 80% of the zirconium dioxide crystals are tetragonal zirconium dioxide, as determined by Rietveld refinement.
8 . The glass ceramic material according to claim 1 , wherein the hardness-enhancing additive comprises at least one of aluminum oxide and yttrium oxide.
9 . The glass ceramic material according to claim 8 , wherein the material comprises 2-10 weight % hardness-enhancing additive in the form of at least one of yttrium oxide or aluminum oxide.
10 . A method of forming a glass ceramic according to claim 1 , wherein the method comprises the following steps:
(11): mixing of two sols, the first sol comprises a zirconium dioxide precursor material and the second sol comprises a silicon dioxide precursor material, adding a catalyst to the mixture of two sols, and wherein said step comprises adding a precursor material for a hardness-enhancing additive;
(12): drying and forming of a xerogel;
(13): calcination of the formed xerogel; and
(14): sintering of the calcined xerogel, wherein the method comprises a fractionation step reducing the particle size of a material obtained in step 11.
11 . The method according to claim 10 , wherein, in step 11, the first or the second sol comprises the precursor material for the hardness-enhancing additive.
12 . The method according to claim 11 , wherein the precursor material for the hardness-enhancing additive is added to the two sols after they are mixed in step 11.
13 . The method according to claim 10 , wherein 3-20 molar %, based on the total molar amount of the material, of the precursor material for the hardness-enhancing additive, calculated as the content of at least one of Y 3+ or Al 3+ is added.
14 . The method according to claim 10 , wherein the sintering in step (14) of the method is performed using hot pressing (HP), hot isostatic pressure (HIP) or spark plasma sintering (SPS).
15 . A densified material comprising the glass ceramic according to claim 1 .
16 . A dental restorative material comprising the densified material according to claim 15 .