Polypropylene resin composition and non-woven fabric prepared using the same
In the present disclosure, there are provided a polypropylene resin composition including an ethylene propylene copolymer, and a nonwoven fabric produced therefrom. In particular, the polypropylene resin composition of the present disclosure may be prepared by using a continuous reactor in the presence of a metallocene compound having a specific structure. The polypropylene resin composition of the present disclosure can maintain high strength together with excellent processability. Thus, the polypropylene resin composition of the present disclosure can produce a soft nonwoven fabric, as compared to the existing products, by optimizing xylene soluble, the content of ethylene, a melt index, a crystallization temperature, a tensile strength and a flexural modulus, together with the narrow molecular weight distribution.
1 . A polypropylene resin composition having:
a molecular weight distribution (Mw/Mn) of 2.6 to 3.2,
a xylene soluble (X.S.) of 4.5% by weight to 7.5% by weight,
a content of ethylene of 1.0% by weight to 5.0% by weight,
a tensile strength of 275 kg/cm 2 to 285 kg/cm 2 , as measured according to the ASTM D 638 method,
a flexural modulus of 11500 kg/cm 2 to 12500 kg/cm 2 , as measured according to the ASTM D 790 method,
a melt index (MI 2.16 , measured according to the ASTM D 1238 at 230° C. under a load of 2.16 kg) of 10 g/10 min to 45 g/10 min, and
a crystallization temperature (Tc) of 95° C. to 115° C.,
wherein the polypropylene resin composition comprises a propylene homopolymer and an ethylene propylene copolymer, wherein the ethylene propylene copolymer is dispersed in the propylene homopolymer.
2 . The polypropylene resin composition of claim 1 , wherein the molecular weight distribution (Mw/Mn) is 2.6 to 2.8.
3 . The polypropylene resin composition of claim 1 , wherein the xylene soluble (X.S.) is 4.5% by weight to 7.0% by weight.
4 . The polypropylene resin composition of claim 1 , wherein the content of ethylene is 2.0% by weight to 3.2% by weight.
5 . The polypropylene resin composition of claim 1 , wherein the tensile strength is 278 kg/cm 2 to 283 kg/cm 2 , as measured according to the ASTM D 638 method.
6 . The polypropylene resin composition of claim 1 , wherein the flexural modulus is 11800 kg/cm 2 to 12300 kg/cm 2 , as measured according to the ASTM D 790 method.
7 . The polypropylene resin composition of claim 1 , wherein the melt index (MI 2.16 , measured according to ASTM D 1238 at 230° C. under a load of 2.16 kg) is 20 g/10 min to 45 g/10 min.
8 . The polypropylene resin composition of claim 1 , wherein the crystallization temperature (Tc) is 108° C. to 112° C.
9 . The polypropylene resin composition of claim 1 , which has a melting temperature of 150° C. to 158° C.
10 . A polypropylene nonwoven fabric composed of a fiber produced from the polypropylene resin composition of claim 1 .
11 . The polypropylene nonwoven fabric of claim 10 , which has a mean diameter of the fiber of 5.7 micrometers to 8.6 micrometers.
12 . The polypropylene nonwoven fabric of claim 10 , which has a handle-O-meter of 24 g or less, as measured according to the NWSP 090.3.R0 standard when a basis weight of the nonwoven fabric is 72 g/m 2 to 76 g/m 2 .
13 . The polypropylene resin composition of claim 1 , which has a flexural strength of 375 kg/cm 2 to 385 kg/cm, as measured according to the ASTM D 790 method.
14 . The polypropylene resin composition of claim 1 , which does not include a nucleating agent.
15 . The polypropylene resin composition of claim 1 , wherein the ethylene propylene copolymer is 3% by weight to 9% by weight, based on a total weight of the propylene homopolymer.