Pump and method of manufacturing a sealing

1 . A method of coating a pump-active component of a pump, comprising the following steps:

Step A) providing the pump-active component composed of a light metal workpiece and having a porous oxide layer on a surface,

Step B) exposing the pump-active component to a negative pressure,

Step C) contacting the porous oxide layer with a solution comprising at least one polymerizable sealing precursor and/or at least one sol-gel-based sealing precursor,

wherein a voltage is applied to the pump-active part during at least one of the steps A) to C).

2 . The method in accordance with claim 1 ,

wherein the polymerizable precursor is fluorine-free.

3 . The method in accordance with claim 1 ,

wherein, in step C), the solution includes ions and/or ionic compounds.

4 . The method in accordance with claim 1 ,

wherein at least one compound having functional groups from the families of the organic anions, and/or from the family of inorganic ions is included in the solution of step C).

5 . The method in accordance with claim 4 ,

wherein the families of the organic anions comprise substituted acrylates and/or substituted acetates and/or substituted styrenes and/or substituted isocyanates and/or carboxyls and/or sulfonic acid.

6 . The method in accordance with claim 4 ,

wherein the family of inorganic ions comprise silicates and aluminates.

7 . The method in accordance with claim 1 ,

wherein the voltage is successively increased during the treatment of the pump-active component.

8 . The method in accordance with claim 1 ,

wherein the voltage is between 50 and 300 V.

9 . The method in accordance with claim 1 ,

wherein the voltage is applied to the pump-active component using a direct current.

10 . The method in accordance with claim 1 ,

wherein the pump-active component is heat-treated after completion of the electrochemical treatment.

11 . The method in accordance with claim 10 ,

wherein the heat treatment step is carried out at 100° C. to 300° C.

12 . The method in accordance with claim 1 ,

wherein the sealing precursor is precipitated in the pores during the electrochemical treatment.

13 . The method in accordance with wherein the sealing precursor is polymerized in the pore of the porous oxide layer.

14 . A pump comprising a pump-active component, the pump active component having been formed in by a method comprising the following steps:

Step A) providing the pump-active component composed of a light metal workpiece and having a porous oxide layer on a surface,

Step B) exposing the pump-active component to a negative pressure,

Step C) contacting the porous oxide layer with a solution comprising at least one polymerizable sealing precursor and/or at least one sol-gel-based sealing precursor,

wherein a voltage is applied to the pump-active part during at least one of the steps A) to C).

15 . The pump in accordance with claim 14 ,

wherein the pump comprises a pump-active component having a coating,

wherein the coating comprises an oxide layer, the oxide layer having pores, and a fluorine-free polymer-based and/or sol-gel-based sealing, and

wherein the pores of the oxide layer are at least partly covered by the sealing and/or impregnated with the sealing and/or filled with the sealing.

16 . The pump in accordance with claim 14 ,

wherein the oxide layer is formed by anodic oxidation in an acidic electrolyte.

17 . The pump in accordance with claim 14 ,

wherein it is a spiral pump or scroll pump, comprising conveying elements formed as spiral elements, wherein the sealing is at least regionally applied to at least one of the conveying elements formed as spiral elements.

18 . The pump in accordance with claim 17 ,

wherein it is a spiral vacuum pump or a scroll vacuum pump.

19 . The pump in accordance with claim 14 ,

wherein it is a piston pump, comprising at least one cylinder, which has an inner cylinder wall, and a piston movable in the cylinder, wherein the sealing is at least regionally applied to the inner cylinder wall and/or the piston.

20 . The pump in accordance with claim 19 ,

wherein it is a piston vacuum pump.

21 . The pump in accordance with claim 14 ,

wherein it is a turbomolecular pump, wherein the sealing is at least regionally applied to rotor disks and/or stator disks.