Composite reverse osmosis membrane and preparation method therefor
The present disclosure relates to a composite reverse osmosis membrane and a preparation method therefor. The preparation method of the present disclosure can realize the preparation of a composite reverse osmosis membrane having a high flux, a high desalinization rate, a high deboration rate and high contamination resistance in a simple operation and high reaction efficiency manner.
1 . A composite reverse osmosis membrane, comprising:
a non-woven fabric layer, a polymer porous support layer, an amphiphilic block copolymer modification layer, and a hybrid polyamide functional layer:
wherein the polymer porous support layer is disposed on the non-woven fabric layer, the amphiphilic block copolymer modification layer is disposed on the surface of the polymer porous support layer, and the hybrid polyamide functional layer is disposed on the amphiphilic block copolymer modification layer;
wherein the amphiphilic block copolymer contains hydrophilic blocks and lipophilic blocks, the hybrid polyamide functional layer contains an ether having a cyclic structure present in the hybrid polyamide functional layer in a physical doping mode or a chemical bonding mode, and the amphiphilic block copolymer modification layer contains one or more of the following block copolymers: polystyrene-b-polyethylene glycol, DL-polylactic acid-b-polyacrylic acid, polyglycolide-b-polyethylene glycol-polyglycolide, polystyrene-b-DL-polylactic acid, polystyrene-b-L-polylactic acid, polyethylene glycol-b-polyethyleneimine, polycaprolactone-b-polyethyleneimine, polylactic acid-glycolic acid-b-polylysine, polyethylene glycol-b-polylactic acid-polycaprolactone, polylactic acid-polycaprolactone-b-polyethylene glycol-maleimide, polylactic acid-polycaprolactone-b-polyethylene glycol-amino, polylactic acid-polycaprolactone-b-polyethylene glycol-carboxyl, polylactic acid-polycaprolactone-b-polyethylene glycol-activated ester, polylactic acid-b-polyethylene glycol amino, polylactic acid-b-polyethylene glycol carboxyl, polylactic acid-b-polyethylene glycol hydroxyl, polylactic acid-polycaprolactone-b-polyethylene glycol-folic acid, polylactic acid-polyallyl lactide-b-polyethylene glycol-amino, polylactic acid-polyallyl lactide-b-polyethylene glycol, polylactic acid-polyallyl lactide-b-polyethylene glycol-maleimide, polylactic acid-polycaprolactone-b-polyethylene glycol, polyacrylic acid-b-polyacrylamide, polyacrylic acid-b-polymethyl methacrylate, poly(n-butyl acrylate)-b-polyacrylic acid, poly(n-butyl acrylate)-b-polyacrylamide, poly(tert-butyl methacrylate)-b-polyoxyethylene, polymethyl methacrylate-b-polyacrylic acid, polyneopentyl ester-b-polymethacrylic acid, polyoxyethylene-b-polyacrylic acid, polyoxyethylene-b-polyacrylamide, polytetrahydrofuran-b-polyoxybutylene, polyoxyethylene-b-polycaprolactone, polyoxyethylene-b-polylactic acid, polyoxyethylene-b-polypropylene oxide, polyoxyethylene-b-poly(nitrobenzyl methacrylate), polyoxyethylene-b-poly (N-isopropylacrylamide), polyoxyethylene-b-poly(tert-butyl acrylate), polyoxyethylene-b-poly (tert-butyl methacrylate), polyoxyethylene-b-polymethyloxazoline, polyoxyethylene-b-polylactide, polyisobutylene-b-polyacrylic acid, polyisobutylene-b-polyoxyethylene, polystyrene-b-polyacrylamide, polystyrene sulfonic acid-b-polymethylbutene, poly(sodium 4-styrene sulfonate)-b-polyoxyethylene, polydimethylsiloxane-b-polyoxyethylene, polydimethylsiloxane-b-polymethacrylic acid, polyvinylpyridine-b-polyoxyethylene, polymethacrylic acid-b-polyneopentyl ester, polymethacrylic acid-b-poly(hydroxyethyl methacrylate), polymethacrylic acid-b-polycaprolactone, polystyrene-b-polylactic acid, poly(lactic acid glycolic acid)-b-polyethylene glycol maleimide, poly(lactic acid glycolic acid)-b-polyethylene glycol carboxyl, poly lactic acid glycolic acid)-b-polyethylene glycol amino, poly(lactic acid glycolic acid) copolymer-b-polyethylene glycol hydroxyl, poly(lactic acid glycolicacid) copolymer-b-polyethylene glycol active ester, poly(lactic acid glycolic acid) copolymer-b-polyethylene glycol biotin, poly(lactic acid glycolic acid) copolymer-b-polyethylene glycol azide, poly(lactic acid glycolic acid) copolymer-b-polyethylene glycol phospholipid, poly(lactic acid glycolic acid) copolymer-b-polyethylene glycol aldehyde group, poly(lactic acid glycolic acid) copolymer-b-polyethylene glycol propylene ester, and poly(lactic acid glycolic acid) copolymer-b-polyethyleneimine.
2 . The composite reverse osmosis membrane according to claim 1 , wherein the polymer porous support layer is one or more of polysulfone porous support layer, polyethersulfone porous support layer, polyacrylonitrile porous support layer, polyethyleneimine porous support layer, polyarylethersulfone ketone porous support layer, polyvinylidene fluoride porous support layer, and sulfonated polyethersulfone porous support layer; the polyamide is aromatic polyamide and/or aliphatic polyamide.
3 . The composite reverse osmosis membrane according to claim 1 , wherein the amphiphilic block copolymer has an HLB value of 3 to 40.
4 . The composite reverse osmosis membrane according to claim 1 , wherein the ether having a cyclic structure is a cyclic ether containing a structural unit (CH 2 CH 2 Y) n , wherein Y is at least one selected from heteroatoms O, N, S, and P, n is an integer and 3≤n≤10.
5 . A preparation method for a composite reverse osmosis membrane, comprising steps of:
preparing a base membrane, wherein the base membrane comprises a polymer porous support layer on a non-woven fabric layer;
preparing an amphiphilic block copolymer solution as a first solution and coating the solution on the polymer porous support layer to form an amphiphilic block copolymer modification layer, wherein the amphiphilic block copolymer modification layer contains one or more of the following block copolymers: polystyrene-b-polyethylene glycol, DL-polylactic acid-b-polyacrylic acid, polyglycolide-b-polyethylene glycol-polyglycolide, polystyrene-b-DL-polylactic acid, polystyrene-b-L-polylactic acid, polyethylene glycol-b-polyethyleneimine, polycaprolactone-b-polyethyleneimine, polylactic acid-glycolic acid-b-polylysine, polyethylene glycol-b-polylactic acid-polycaprolactone, polylactic acid-polycaprolactone-b-polyethylene glycol-maleimide, polylactic acid-polycaprolactone-b-polyethylene glycol-amino, polylactic acid-polycaprolactone-b-polyethylene glycol-carboxyl, polylactic acid-polycaprolactone-b-polyethylene glycol-activated ester, polylactic acid-b-polyethylene glycol amino, polylactic acid-b-polyethylene glycol carboxyl, polylactic acid-b-polyethylene glycol hydroxyl, polylactic acid-polycaprolactone-b-polyethylene glycol-folic acid, polylactic acid-polyallyl lactide-b-polyethylene glycol-amino, polylactic acid-polyallyl lactide-b-polyethylene glycol, polylactic acid-polyallyl lactide-b-polyethylene glycol-maleimide, polylactic acid-polycaprolactone-b-polyethylene glycol, polyacrylic acid-b-polyacrylamide, polyacrylic acid-b-polymethyl methacrylate, poly(n-butyl acrylate)-b-polyacrylic acid, poly(n-butyl acrylate)-b-polyacrylamide, poly (tert-butyl methacrylate)-b-polyoxyethylene, polymethyl methacrylate-b-polyacrylic acid, polyneopentyl ester-b-polymethacrylic acid, polyoxyethylene-b-polyacrylic acid, polyoxyethylene-b-polyacrylamide, polytetrahydrofuran-b-polyoxybutylene, polyoxyethylene-b-polycaprolactone, polyoxyethylene-b-polylactic acid, polyoxyethylene-b-polypropylene oxide, polyoxyethylene-b-poly(nitrobenzyl methacrylate), polyoxyethylene-b-poly (N-isopropylacrylamide), polyoxyethylene-b-poly(tert-butyl acrylate), polyoxyethylene-b-poly (tert-butyl methacrylate), polyoxyethylene-b-polymethyloxazoline, polyoxyethylene-b-polylactide, polyisobutylene-b-polyacrylic acid, polyisobutylene-b-polyoxyethylene, polystyrene-b-polyacrylamide, polystyrene sulfonic acid-b-polymethylbutene, poly(sodium 4-styrene sulfonate)-b-polyoxyethylene, polydimethylsiloxane-b-polyoxyethylene, polydimethylsiloxane-b-polymethacrylic acid, polyvinylpyridine-b-polyoxyethylene, polymethacrylic acid-b-polyneopentyl ester, polymethacrylic acid-b-poly(hydroxyethyl methacrylate), polymethacrylic acid-b-polycaprolactone, polystyrene-b-polylactic acid, poly(lactic acid glycolic acid)-b-polyethylene glycol maleimide, poly(lactic acid glycolic acid)-b-polyethylene glycol carboxyl, poly lactic acid glycolic acid)-b-polyethylene glycol amino, poly(lactic acid glycolic acid) copolymer-b-polyethylene glycol hydroxyl, poly lactic acid glycolic acid) copolymer-b-polyethylene glycol active ester, poly lactic acid glycolic acid) copolymer-b-polyethylene glycol biotin, poly(lactic acid glycolic acid) copolymer-b-polyethylene glycol azide, poly (lactic acid glycolic acid) copolymer-b-polyethylene glycol phospholipid, poly (lactic acid glycolic acid) copolymer-b-polyethylene glycol aldehyde group, poly(lactic acid glycolic acid) copolymer-b-polyethylene glycol propylene ester, and poly(lactic acid glycolic acid) copolymer-b-polyethyleneimine;
contacting the non-woven fabric formed with the amphiphilic block copolymer modification layer and the polymer porous support layer with an aqueous solution containing an amine monomer as a second solution and an oil-phase solution containing an acyl chloride monomer as a third solution in sequence, wherein at least one of the second solution and the third solution contains an ether having a cyclic structure to form a hybrid polyamide functional layer containing the ether having a cyclic structure, and the hybrid polyamide functional layer is formed on the amphiphilic block copolymer modification layer; and
performing post-treatment and drying to obtain a composite reverse osmosis membrane.
6 . The preparation method for a composite reverse osmosis membrane according to claim 5 , wherein the polymer porous support layer is one or more of polysulfone porous support layer, polyethersulfone porous support layer, polyacrylonitrile porous support layer, polyethyleneimine porous support layer, polyarylethersulfone ketone porous support layer, polyvinylidene fluoride porous support layer, and sulfonated polyethersulfone porous support layer; the polyamide is aromatic polyamide and/or aliphatic polyamide.
7 . The preparation method for a composite reverse osmosis membrane according to claim 5 , wherein the first solution comprises an amphiphilic block copolymer and a first solvent, the amphiphilic block copolymer contains hydrophilic blocks and lipophilic blocks, the amphiphilic block copolymer has an HLB value of 3 to 40, and the first solvent is one or more of methanol, ethanol, propanol, butanol, acetone, tetrahydrofuran, dimethyl sulfoxide, sulfolane, N,N-dimethylformamide, N,N-dimethylacetamide, water, toluene, xylene, chloroform, ISOPAR-G, ISOPAR-E, ISOPAR-L, n-butane, n-heptane, cyclohexane, and ethyl cyclohexane; or, the concentration of the amphiphilic block copolymer in the first solution is 0.01 wt. % to 10 wt. %.
8 . The preparation method for a composite reverse osmosis membrane according to claim 5 , wherein the ether having a cyclic structure is a cyclic ether containing a structural unit (CH 2 CH 2 Y) n , wherein Y is at least one selected from heteroatoms O, N, S, and P, n is an integer and 3≤n≤10; or, the concentration of the ether having a cyclic structure in at least one of the second solution and the third solution is 0.01 wt. % to 10 wt. %.
9 . The preparation method for a composite reverse osmosis membrane according to claim 5 , wherein the amine monomer is one or more of aniline, m-phenylenediamine, p-phenylenediamine, o-phenylenediamine, 1,3,5-triaminobenzene, 1,2,4-triaminobenzene, 3,5-diaminobenzoic acid, 2,4-diaminotoluene, 2,4-diaminoanisole, 2,4-diaminophenol dihydrochloride, dimethyl phenylenediamine, 1,4-cyclohexanediamine, 1,2-cyclohexanediamine, piperazine, ethylene glycol amine, ethylenediamine, propanediamine, butanediamine, hexamethylenediamine, ethanolamine, polyethyleneimine, triethylamine, tri (2-aminoethyl) amine, diethylenetriamine, N-(2-hydroxyethyl) ethylenediamine, 1,3-cyclohexanediamine, 1,3-dipiperidylpropane, 4-aminomethylpiperazine, ethanolamine, diethanolamine, hexanediol amine, and diglycolamine, and in the second solution, the concentration of the amine monomer is 0.5 wt. % to 10 wt. %;
the acyl chloride monomer is one or more of phthaloyl chloride, isophthaloyl chloride, terephthaloyl chloride, biphenyl-4,4′-dicarbonyl dichloride, trimesoyl chloride, and a ternary acyl chloride having a structure represented by the following general formula (1):
wherein R 1 , R 2 , R 3 are each independently at least one of the following groups:
in the third solution, the concentration of the acyl chloride monomer is 0.05 wt. % to 5 wt. %.
10 . The composite reverse osmosis membrane according to claim 2 , wherein the amphiphilic block copolymer has an HLB value of 3 to 40.
11 . The composite reverse osmosis membrane according to claim 2 , wherein the ether having a cyclic structure is a cyclic ether containing a structural unit (CH 2 CH 2 Y) n , wherein Y is at least one selected from heteroatoms O, N, S, and P, n is an integer and 3≤n≤10.
12 . The preparation method for a composite reverse osmosis membrane according to claim 6 , wherein the first solution comprises an amphiphilic block copolymer and a first solvent, the amphiphilic block copolymer contains hydrophilic blocks and lipophilic blocks, the amphiphilic block copolymer has an HLB value of 3 to 40, and the first solvent is one or more of methanol, ethanol, propanol, butanol, acetone, tetrahydrofuran, dimethyl sulfoxide, sulfolane, N,N-dimethylformamide, N,N-dimethylacetamide, water, toluene, xylene, chloroform, ISOPAR-G, ISOPAR-E, ISOPAR-L, n-butane, n-heptane, cyclohexane, and ethyl cyclohexane; or, the concentration of the amphiphilic block copolymer in the first solution is 0.01 wt. % to 10 wt. %.
13 . The preparation method for a composite reverse osmosis membrane according to claim 7 , wherein the ether having a cyclic structure is a cyclic ether containing a structural unit (CH 2 CH 2 Y) n , wherein Y is at least one selected from heteroatoms O, N, S, and P, n is an integer and 3≤n≤10; or, the concentration of the ether having a cyclic structure in at least one of the second solution and the third solution is 0.01 wt. % to 10 wt. %.
14 . The preparation method for a composite reverse osmosis membrane according to claim 6 , wherein the amine monomer is one or more of aniline, m-phenylenediamine, p-phenylenediamine, o-phenylenediamine, 1,3,5-triaminobenzene, 1,2,4-triaminobenzene, 3,5-diaminobenzoic acid, 2,4-diaminotoluene, 2,4-diaminoanisole, 2,4-diaminophenol dihydrochloride, dimethyl phenylenediamine, 1,4-cyclohexanediamine, 1,2-cyclohexanediamine, piperazine, ethylene glycol amine, ethylenediamine, propanediamine, butanediamine, hexamethylenediamine, ethanolamine, polyethyleneimine, triethylamine, tri (2-aminoethyl) amine, 1,3-diethylenetriamine, N-(2-hydroxyethyl) ethylenediamine, cyclohexanediamine, 1,3-dipiperidylpropane, 4-aminomethylpiperazine, ethanolamine, diethanolamine, hexanediol amine, and diglycolamine, and in the second solution, the concentration of the amine monomer is 0.5 wt. % to 10 wt. %;
the acyl chloride monomer is one or more of phthaloyl chloride, isophthaloyl chloride, terephthaloyl chloride, biphenyl-4,4′-dicarbonyl dichloride, trimesoyl chloride, and a ternary acyl chloride having a structure represented by the following general formula (1):
wherein R 1 , R 2 , R 3 are each independently at least one of the following groups:
in the third solution, the concentration of the acyl chloride monomer is 0.05 wt. % to 5 wt. %.