Laminated film and flexible device
Provided is a laminated film having a high level of surface hardness and excellent bendability, and also having antifouling performance that hardly deteriorates. A laminated film 1 of the present disclosure includes: a support 10 ; and a resin layer 11 laminated on at least one surface of the support, in which the resin layer satisfies the following Conditions 1, 2 and 3: Condition 1: in a pencil hardness test with a load of 750 g, a pencil hardness is F or greater on a surface of the resin layer of the laminated film; Condition 2: in a cylindrical mandrel test, where the surface of the resin layer of the laminated film is bent into a convex shape, no cracks occur on the surface of the resin layer with a curvature radius of 5 mm; and Condition 3: a surface of the resin layer of the laminated film has a water contact angle of 95° or greater before subjected to a steel wool abrasion test, and a water contact angle on tested areas of the surface is 90° or greater after subjected to the test.
1 . A laminated film comprising:
a support; and
a resin layer laminated on at least one surface of the support, the resin layer, or one of the resin layers when the resin layers are laminated on both surfaces of the support, satisfying the following Conditions 1, 2, and 3:
Condition 1:
in a pencil hardness test specified in JIS K5600 5-4 (1999) at a load of 750 g, a pencil hardness is F or greater on a surface of the resin layer of the laminated film;
Condition 2:
in a cylindrical mandrel test according to a method specified in JIS K5600-5-1 (1999), where the surface of the resin layer of the laminated film is bent into a convex shape, no cracks occur on the surface of the resin layer with a curvature radius of 5 mm; and
Condition 3:
a surface of the resin layer of the laminated film has a water contact angle of 95° or greater before subjected to a steel wool abrasion test where the surface of the resin layer is rubbed back and forth 1000 times with #0000 steel wool while a load of 1 kg/cm 2 is applied, and a water contact angle on tested areas of the surface is 90° or greater after subjected to the test;
wherein the resin layer is a cured product of a curable composition;
wherein the curable composition comprises a polyorganosilsesquioxane, a compound A, and an aliphatic compound B;
wherein the compound A contains a group selected from a hydroxyl group, an epoxy group, an oxetanyl group, and a vinyl ether group, and a group selected from (meth) acryloyl group and vinyl group; and
wherein the aliphatic compound B excludes compounds corresponding to compound A and contains two or more groups selected from epoxy group, oxetanyl group, and vinyl ether group;
wherein a content of the compound A is from 1 to 100 parts by weight relative to 100 parts by weight of the polyorganosilsesquioxane; and
wherein a content of the aliphatic compound B is 1 to 50 parts by weight per 100 parts by weight of the polyorganosilsesquioxane.
2 . The laminated film according to claim 1 , wherein the resin layer, or one of the resin layers when the resin layers are laminated on both surfaces of the support, further satisfies the following Condition (Condition 4):
Condition 4: in the following bending resistance test, a number of operations it takes for cracks to occur in the resin layer is 10000 times or more:
bending resistance test:
when an operation of bending the laminated film from an unbent state to a direction where the surface of the resin layer is bent by 180° into a convex shape with a curvature radius (R) of 4.0 mm and unbending the bent laminated film again is defined as one cycle, the operation is performed at a rate of 30 to 60 cycles/min.
3 . The laminated film according to claim 1 , wherein the resin layer, or one of the resin layers when the resin layers are laminated on both surfaces of the support, further satisfies the following Condition (Condition 5):
Condition 5: no scratches are visually observed in a steel wool abrasion test where the surface of the resin layer is rubbed back and forth 1000 times with #0000 steel wool while a load of 1 kg/cm 2 is applied.
4 . The laminated film according to claim 1 , wherein the resin layer, or one of the resin layers when the resin layers are laminated on both surfaces of the support, has a haze of 1.0% or less.
5 . The laminated film according to claim 1 , having a haze of 7% or less.
6 . The laminated film according to claim 1 , wherein the curable composition further comprises a curing catalyst.
7 . The laminated film according to claim 6 , wherein the curing catalyst comprises a cationic polymerization initiator.
8 . The laminated film according to claim 6 , wherein the curing catalyst comprises a radical polymerization initiator.
9 . The laminated film according to claim 1 , wherein the curable composition further comprises a fluorine-containing radically polymerizable compound.
10 . The laminated film according to claim 1 , wherein the support comprises a transparent support.
11 . An image display device comprising the laminated film described in claim 1 .
12 . The image display device according to claim 11 , which is a flexible display.
13 . The image display device according to claim 11 , which is an organic electroluminescent display device.
14 . A flexible device comprising the image display device described claim 11 .