Gel electrolyte supercapacitor
A supercapacitor including a gel electrode and two electrodes is described. Each of the two electrodes include a second mixture of 5-10 wt. % conductive additive, 5-10 wt. % binding compound, and 80-90 wt. % activated carbon. Further, the second mixture is at least partially coated on an inner surface of a substrate, and where the inner surfaces of the two electrodes are separated by and in physical contact with the gel electrolyte to form the supercapacitor. The gel electrolyte includes a polyol compound, a base with a molarity (M) of 1-5 in the polyol compound, and 1-10 wt. % of boric acid relative to the weight of the polyol compound. The boric acid intercalates with a first mixture of the polyol compound and the base, creating a gel.
1 . A gel electrolyte supercapacitor, comprising:
two electrodes; and
a gel electrolyte;
wherein the gel electrolyte comprises:
a polyol compound that is selected from the group consisting of glycerol and ethylene glycol;
a base with a molarity (M) of 1-5 in the polyol compound; and
1-10 wt % of boric acid relative to the weight of the polyol compound;
wherein the boric acid intercalates with a first mixture of the polyol compound and the base, creating a gel;
wherein
the base is selected from a group consisting of lithium hydroxide, sodium hydroxide, and potassium hydroxide;
wherein the two electrodes each comprise:
a second mixture comprising 5-10 wt % of a conductive additive, 5-10 wt % of a binding compound, and 80-90 wt % of an activated carbon, based on the total weight of the conductive additive, the binding compound, and the activated carbon; and
wherein the second mixture is at least partially coated on an inner surface of a substrate, wherein the substrate is formed from at least one material selected from the group consisting of copper, aluminum and nickel;
wherein an outer surface of the substrate is not coated with the second mixture; and
wherein the inner surfaces of the two electrode substrates are separated by and in physical contact with the gel electrolyte to form the gel electrolyte supercapacitor.
2 . The gel electrolyte supercapacitor of claim 1 , wherein
the polyol compound is glycerol; and
the base is potassium hydroxide.
3 . The gel electrolyte supercapacitor of claim 1 , wherein the gel electrolyte has
a glass transition temperature of −90 to −60° C.;
wherein the gel electrolyte comprises 2-4 wt % boric acid.
4 . The gel electrolyte supercapacitor of claim 1 , wherein the gel electrolyte has
an ionic conductivity of 2×10 −3 -4×10 −3 S/cm.
5 . The gel electrolyte supercapacitor of claim 1 , wherein
the gel electrolyte produces no fire after treatment with a flame.
6 . The gel electrolyte supercapacitor of claim 1 , wherein the gel electrolyte is made by a method comprising:
mixing the base and the polyol compound at a temperature of 40-60° C. to form a mixture;
cooling the mixture to 23-26° C. and adding the boric acid to form the gel electrolyte.
7 . The gel electrolyte supercapacitor of claim 1 , wherein:
the binding compound is at least one selected from the group consisting of polyvinylidene fluoride and n-methylpyrrolidone;
the conductive additive is at least one selected from the group consisting of graphite, activated carbon, reduced graphene oxide, carbon nanotubes, carbon nanofibers, and carbon black.
8 . The gel electrolyte supercapacitor of claim 1 , wherein
the binding compound is polyvinylidene fluoride;
the conductive additive is carbon black; and
the substrate is an aluminum current collector.
9 . The gel electrolyte supercapacitor of claim 1 , wherein
the inner surface is precoated with at least one boronic acid-containing polymer selected from the group consisting of poly(styreneboronic acid)-b-polystyrene, and poly(ethylene glycol)-b-poly(styrene boronic acid).
10 . The gel electrolyte supercapacitor of claim 1 , wherein the first mixture further comprises:
1-15 wt. % of at least one boronic acid-containing polymer selected from the group consisting of poly(styreneboronic acid)-b-polystyrene, and poly(ethylene glycol)-b-poly(styrene boronic acid), based on the total weight of the polyol compound and the boronic acid-containing polymer.
11 . The gel electrolyte supercapacitor of claim 1 , wherein the second mixture further comprises:
1-10 wt % of at least one boronic acid-containing polymer selected from the group consisting of poly(styreneboronic acid)-b-polystyrene, and poly(ethylene glycol)-b-poly(styrene boronic acid), based on the total weight of the conductive additive, the binding compound, the activated carbon, and the boronic acid-containing polymer.
12 . The gel electrolyte supercapacitor of claim 1 , having
a specific capacitance of 300-350 F/g at 1 A/g;
wherein the gel electrolyte comprises 2-4 wt % of the boric acid.
13 . The gel electrolyte supercapacitor of claim 12 , wherein
at least 90% of the initial capacitance is maintained up to 10,000 cycles.
14 . The gel electrolyte supercapacitor of claim 12 , wherein
at least 90% of the initial capacitance is maintained after at least 30 days under ambient conditions.
15 . The gel electrolyte supercapacitor of claim 12 , having
a specific energy of 40-55 Wh/kg at a power of 900-950 W/kg.
16 . The gel electrolyte supercapacitor of claim 12 , having
having an equivalent series resistance of 4-8Ω.
17 . The gel electrolyte supercapacitor of claim 1 , having
an open voltage window of 0-3 V.
18 . The gel electrolyte supercapacitor of claim 1 , having
a specific capacitance of 150-200 F/g at 1 A/g;
wherein the gel electrolyte comprises 5-7 wt % of the boric acid and 1M base.
19 . A wearable device comprising the gel electrolyte supercapacitor of claim 1 , wherein
the supercapacitor is electrically connected to a sensor; and
the supercapacitor functions as a battery.
20 . The gel electrolyte supercapacitor of claim 1 , comprising:
2-10 of the gel electrolyte supercapacitors connected in parallel and/or series.