Method for producing Guerbet alcohol
A method for producing a Guerbet alcohol, including reacting a raw material alcohol having 8 or more and 22 or less carbon atoms, in the presence of a catalyst (A) containing a first component and a second component below, having a molar ratio of the second component with respect to the first component (second component/first component) of 0.0001 or more and 0.005 or less: first component: copper, and second component: one kind selected from the group consisting of elements that are elements belonging to Groups 9 to 13 in the fourth to sixth periods of the periodic table, except copper.
1 . A method for producing a Guerbet alcohol, comprising reacting a raw material alcohol having 8 or more and 22 or less carbon atoms, in the presence of a catalyst (A) consisting of a first component and a second component below, having a molar ratio of the second component with respect to the first component (second component/first component) of 0.0001 or more and 0.004 or less:
first component: copper, and
second component: one kind selected from the group consisting of elements that are elements belonging to Groups 9 to 13 in the fourth to sixth periods of the periodic table, except copper.
2 . The method for producing a Guerbet alcohol according to claim 1 , wherein the second component of the catalyst (A) is one kind selected from gallium (Ga), rhodium (Rh), palladium (Pd), iridium (Ir), and platinum (Pt).
3 . The method for producing a Guerbet alcohol according to claim 1 , wherein the catalyst (A) is a catalyst (A) including a carrier having the first component and the second component supported thereon.
4 . The method for producing a Guerbet alcohol according to claim 3 , wherein the carrier of the catalyst (A) is at least one kind selected from the group consisting of aluminum oxide, activated carbon, titanium oxide, zirconium oxide, zeolite, cerium oxide, and hydrotalcite.
5 . The method for producing a Guerbet alcohol according to claim 1 , wherein a content of the first component contained in the catalyst (A) is 6% by mass or more and 50% by mass or less.
6 . The method for producing a Guerbet alcohol according to claim 1 , wherein in suspended bed reaction, an amount of the catalyst (A) per 100 parts by mass in total of the amount of the raw material alcohol is 0.01 part by mass or more and 10 parts by mass or less.
7 . The method for producing a Guerbet alcohol according to claim 1 , wherein a base catalyst (B) is used with the catalyst (A).
8 . The method for producing a Guerbet alcohol according to claim 7 , wherein an amount of the base catalyst (B) per 100 parts by mol in total of the amount of the raw material alcohol is 0.1 part by mol or more and 7 parts by mol or less.
9 . The method for producing a Guerbet alcohol according to claim 1 , wherein the raw material alcohol is a saturated linear primary aliphatic alcohol having 8 or more and 18 or less carbon atoms.
10 . A catalyst used for a method for producing a Guerbet alcohol, comprising a first component and a second component below, having a molar ratio of the second component with respect to the first component (second component/first component) of 0.0001 or more and 0.004 or less:
first component: copper, and
second component: gallium (Ga), palladium (Pd), iridium (Ir), or platinum (Pt).