Solventless quantum dot composition, preparation method therefor, and cured film, color filter and display device which comprise same
A quantum dot composition, a preparation method therefor, and a cured film, a color filter and a display device that comprise the same are described. Specifically, a solventless quantum dot composition comprises quantum dots, which are surface-treated with two types of ligands. As a result, the quantum dot composition exhibits low viscosity, excellent optical properties, and high storage stability.
1 . A solventless quantum dot composition, comprising:
a quantum dot; and
a photopolymerizable monomer, the quantum dot being surface-modified with a first ligand represented by Chemical Formula 1 and a second ligand of 3 to 40 carbon atoms containing a carboxylic group, wherein:
Chemical Formula 1 is as follows:
M is a divalent to tetravalent metal,
X is an organic group of 3 to 20 carbon atoms, and
n is an integer of 2 to 4.
2 . The solventless quantum dot composition of claim 1 , wherein the second ligand is represented by Chemical Formula 2, wherein:
Chemical Formula 2 is as follows:
L is a single bond or is selected from the group consisting of a substituted or unsubstituted alkylene of C1 to C20 and a substituted or unsubstituted alkenylene of C1 to C20,
A is a single bond or is selected from the group consisting of an alkylene of C1 to C20 and alkenylene of C1 to C20 containing at least one functional group selected from the group consisting of ester (—C(═O)O—), ether (—O—), carbonyl (—C(═O)—), sulfonyl (—SO 2 —), sulfide (—S—), and sulfoxide (—SO—), and
R is a hydrogen atom or is selected from the group consisting of a substituted or unsubstituted alkyl of C1 to C20 and a substituted or unsubstituted alkenyl of C1 to C20.
3 . The solventless quantum dot composition of claim 1 , wherein M is selected from the group consisting of Mg, Ca, Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Ge, Sr, Mo, Pd, Cd, In, or Sn.
4 . The solventless quantum dot composition of claim 1 , wherein X in Chemical Formula 1 is an organic group of 4 to 15 carbon atoma containing an ester (—COO—) functional group.
5 . The solventless quantum dot composition of claim 1 , wherein the second ligand does not contain any thiol group.
6 . The solventless quantum dot composition of claim 2 , wherein A in Chemical Formula 2 an alkylene or alkenylene of C2 to C15 containing ester (—COO—), ether (—CO—), or a combination thereof.
7 . The solventless quantum dot composition of claim 1 , wherein the first ligand and the second ligand are mixed at a molar ratio of 1:0.1 to 20.
8 . The solventless quantum dot composition of claim 1 , wherein the quantum dot and the ligands are mixed at a weight ratio of 1:0.05 to 0.5.
9 . The solventless quantum dot composition of claim 1 , wherein the quantum dot is contained in an amount of 1 to 60% by weight, based on a total weight of the solventless quantum dot composition.
10 . The solventless quantum dot composition of claim 1 , wherein the photopolymerizable monomer is a (meth)acrylate-based monomer.
11 . The solventless quantum dot composition of claim 1 , further comprising a photoinitiator, a light diffuser, a polymerization inhibitor, or a combination thereof.
12 . The solventless quantum dot composition of claim 1 , being 30 cps or less in viscosity.
13 . The solventless quantum dot composition of claim 1 , wherein the solventless quantum dot composition is used for ink-jet printing.
14 . A cured film, prepared using the solventless quantum dot composition of claim 1 .
15 . The cured film of claim 14 , having a light absorptivity of 75% or greater and a photoconversion efficiency of 25% or greater.
16 . A color filter, comprising the solventless quantum dot composition of claim 1 .
17 . A display device, comprising the color filter of claim 16 .
18 . A method for preparing a solventless quantum dot composition, the method comprising:
(a) surface modifying quantum dots with a first ligand represented by Chemical Formula 1 and a second ligand of 3 to 40 carbon atoms containing a carboxyl group, wherein:
Chemical Formula 1 is as follows:
M is a divalent to tetravalent metal,
X is an organic group of 3 to 20 carbon atoms, and
n is an integer of 2 to 4;
(b) centrifuging a reaction mixture of step (a) to obtain surface-modified quantum dots; and
(c) dispersing the surface-modified quantum dots in a photopolymerizable monomer.
19 . The method of claim 18 , wherein step (a) comprises one of:
(a-1) introducing a first ligand into the quantum dot dispersion and reacting to modify the surface of the quantum dots, followed by introducing a second ligand and reacting to further modify the surface of the quantum dots; or
(a-2) simultaneously introducing the first ligand and the second ligand and reacting to modify the surface of the quantum dots.
20 . A method for manufacturing a cured film, the method comprising:
forming a pattern by inkjet spray-coating the solventless quantum dot composition of claim 1 onto a substrate; and
curing the pattern.