The present disclosure relates to coated articles with a low-E coating and their preparation methods. The coated article comprises a low-E coating which is supported by a substrate and comprises a metallic IR reflective layer, a protective layer in contact with the metallic IR reflective layer, and a dielectric layer.
1 . A coated article comprising a low-E coating supported by a substrate, wherein the low-E coating comprises a metallic IR reflective layer, a protective layer in contact with the metallic IR reflective layer, a dielectric layer, and a hard coat as the outermost layer, and wherein the metallic IR reflective layer is sandwiched between only two adjacent protective layers.
2 . The coated article according to claim 1 , wherein the coated article has a visible transmittance of >about 60% and/or a visible reflectance of >about 60%.
3 . The coated article according to claim 1 , wherein the low-E coating supported by the substrate has a total thickness in the range of about 90 nm to about 120 nm.
4 . The coated article according to claim 1 , wherein the metallic IR reflective layer comprises Ag, Al, Cu, Zn, Nb, TiN, Ag/Au alloys, Ag/Cu alloys, Ag/Al alloys, NbN x , NbCr, NbCrN x , NbZrO x , and/or Au.
5 . The coated article according to claim 1 , wherein the low-E coating comprises one metallic IR reflective layer.
6 . The coated article according to claim 5 , wherein the metallic IR reflective layer has a thickness of about 5 nm to about 25 nm.
7 . The coated article according to claim 1 , wherein the protective layer in contact with the metallic IR reflective layer comprises one or more selected from the group consisting of nickel-chromium alloys (NiCr), NiCrO x , NiCrN x , NiCrO x N y , Ni x Ti y O z , Ni, Cr, CrN x , NiO x , Ti, TiO x , NbO x , ZnO, Al 2 O 3 , and ZnAlO x .
8 . The coated article according to claim 7 , wherein the protective layer has a thickness of about 1 nm to about 5 nm.
9 . The coated article according to claim 1 , wherein the low-E coating comprises one or more dielectric layers.
10 . The coated article according to claim 9 , wherein each of the dielectric layers has a thickness of from about 10 nm to about 45 nm.
11 . The coated article according to claim 1 , wherein the dielectric layer comprises one or more selected from the group consisting of TiO 2 , Ta 2 O 5 , Nb 2 O 5 , ZrO 2 , ZnO, ZnS, ZnSe, HfO 2 , LaTiO 3 , Al 2 O 3 , La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Sc 2 O 3 , Si 3 N 4 , SiO 2 , LiF, MgF 2 , Na 3 AlF 6 , SnO 2 , indium tin oxide (ITO), Al-doped SiO 2 , Al-doped zinc oxide (AZO), WO 3 , SiAlO x N y and SiO x N y .
12 . The coated article according to claim 1 , wherein a metallic IR reflective layer is sandwiched between two adjacent protective layers, each of the protective layers comprises NiCr and is about <5 nm thick, the metallic IR reflective layer comprises Ag and is about 20 nm thick.
13 . The coated article according to claim 1 , wherein the coated article comprises a low-E coating supported by a substrate, and the low-E coating comprises, in order outward from the substrate, a dielectric layer comprising TiO 2 , a protective layer comprising NiCr, a metallic IR reflective layer comprising Ag, a protective layer comprising NiCr, and a dielectric layer comprising TiO 2 .
14 . The coated article according to claim 13 , wherein the coated article comprises a low-E coating supported by a substrate, and the low-E coating comprises, in order outward from the substrate, a dielectric layer of TiO 2 in about 25 nm to about 45 nm, a protective layer of NiCr in about <5 nm, a metallic IR reflective layer of Ag in about 10 nm to about 20 nm, a protective layer of NiCr in about <5 nm, and a dielectric layer of TiO 2 in about 25 nm to about 45 nm.
15 . The coated article according to claim 14 , wherein the coated article comprises a low-E coating supported by a substrate, and the low-E coating comprises, in order outward from the substrate, a dielectric layer of TiO 2 in about 40 nm, a protective layer of NiCr in about <5 nm, a metallic IR reflective layer of Ag in about 20 nm, a protective layer of NiCr in about <5 nm, and a dielectric layer of TiO 2 in about 40 nm.
16 . The coated article according to claim 1 , wherein the metallic IR reflective layer comprises a frequency selective surface configured to reduce attenuation of telecommunication frequency signal transmission.
17 . The coated article according to claim 1 , wherein the substrate for the coated article is substantially made from plastic or glass.
18 . A method for preparing the coated article according to claim 1 , which includes introducing the dielectric layer, the protective layer in contact with the metallic IR reflective layer, the metallic IR reflective layer, and the hard coat as the outermost layer onto the substrate.
19 . The method according to claim 18 , wherein the dielectric layer, the protective layer in contact with the metallic IR reflective layer, the metallic IR reflective layer, and the hard coat as the outermost layer are introduced onto the substrate by magnetron sputtering deposition.