Flexible food packaging laminates
Described herein are adhesive compositions, and in particular to solventless adhesive compositions, which can be used to construct laminates, such as flexible laminate materials used to construct flexible packaging (among other things). In another aspect, the solventless adhesive materials are essentially monomer and/or catalyst free, making them well suited for use in making laminates for packaged foods, beverages, and other sensitive materials, e.g., materials which should not be contaminated or not contaminated to unacceptable levels. Also described are laminates made with the adhesive compositions. Laminates made with the adhesive compositions exhibit sufficient bond strength to be slit after 4-8 hours after formation and even 4-5 hours after formation.
1 . An adhesive composition comprising:
a) 10 wt % to 40 wt % of amine-free polyol;
b) 0.5 wt % to 10 wt % of polyol including one or more tertiary amine groups; and
c) 40 wt % to 90 wt % of polyurethane prepolymer,
wherein the adhesive composition is free or essentially free of isocyanate monomers, and wherein free or essentially free of isocyanate monomer is an amount of monomer extractable from the adhesive composition that is 0 wt % to 0.1 wt %.
2 . The adhesive composition of claim 1 , wherein the adhesive composition is free or is essentially free of solvent.
3 . The adhesive composition of claim 1 , wherein the monomer is toluene diisocyanate.
4 . The adhesive composition of claim 1 , further comprising one or more of: a plurality of amine-free polyols; a plurality of polyols including one or more tertiary amine groups; or a plurality of polyurethane prepolymers.
5 . The adhesive composition of claim 1 , wherein the adhesive composition is free of catalyst.
6 . The adhesive composition of claim 1 , further comprising catalyst.
7 . The adhesive composition of claim 6 , wherein the catalyst is present in an amount of 0.05 wt % to 0.5 wt %.
8 . The adhesive composition of claim 1 , wherein the polyol including one or more tertiary amine groups is present in an amount of 0.5 wt % to 5.0 wt %.
9 . The adhesive composition of claim 1 , wherein the amine-free polyol is present in an amount of 15 wt % to 35 wt %.
10 . The adhesive composition of claim 1 , wherein the polyurethane prepolymer is present in an amount of 50 wt % to 90%.
11 . A laminate comprising:
first and second substrate layers, adhered together with the adhesive composition of claim 1 .
12 . The laminate of claim 11 , wherein the substrate layers are flexible polymeric materials.
13 . A roll of laminate sheet, comprising the laminate of claim 11 .
14 . Flexible packaging comprised of the laminate of claim 11 .
15 . A method of forming laminate material suitable for slitting comprising the steps of:
forming a laminate comprising first and second substrate layers adhered together with the adhesive composition of claim 1 ; and
curing the laminate for 4 to 8 hours, in which 4 to 8 hours bond strength sufficient to slit the laminate develops.
16 . The method of claim 15 , further comprising the step of slitting the laminate into slit laminate material 4 to 8 hours after forming the laminate.
17 . The method of claim 15 , wherein the laminate comprises a long continuous formed laminate sheet.
18 . The method of claim 15 , further comprising the step of rolling the long continuous formed laminate sheet onto a roll.