Honeycomb structure and method for manufacturing same
A honeycomb structure which is an aggregate of a plurality of microtubes comprising a cellulose nanofiber, wherein the microtubes have an opening shape which is polygonal, wherein the ratio of an average long diameter μ2 (μm) to an average short diameter μ1 (μm) (μ2/μ1) is 2.0 or less, when the average long diameter μ2 (μm) is an average of longest diameters of the opening diameters of the individual microtubes, and the average short diameter μ1 (μm) is an average of shortest diameters of the opening diameters of the individual microtubes, and wherein both standard deviations σ1, σ2 for the respective frequency distributions of the short diameter and long diameter in the opening shape of the microtubes are 20.0 μm or less.
1 . A method for producing a honeycomb structure of a cellulose nanofiber, the method comprising the steps of:
slowly inserting a vessel, which contains therein a dispersion having the cellulose nanofiber dispersed in a solvent, into a coolant to cause the solvent to freeze and grow vertically and upward with respect to the surface of the coolant (freezing step); and
removing the solvent from the dispersion (drying step),
wherein the dispersion has a cellulose nanofiber concentration of 1.0 wt % or more,
wherein the dispersion having a cellulose nanofiber concentration of 1.0 wt % has a light transmittance of 20 to 80% at a wavelength of 550 nm.
2 . The method for producing a honeycomb structure according to claim 1 , wherein the dispersion has a pH of 4.0 to 13.9.
3 . The method for producing a honeycomb structure according to claim 1 , wherein the cellulose nanofiber has an average fiber length of 0.15 μm or more.
4 . The method for producing a honeycomb structure according to claim 1 , wherein the drying step has the steps of:
allowing the dispersion obtained after the freezing step to stand in an environment at 0° C. or lower under a reduced pressure for a predetermined time (first drying step); and
allowing the dispersion to stand in an environment at room temperature under a reduced pressure, removing the solvent (second drying step).
5 . The method for producing a honeycomb structure according to claim 1 , wherein the dispersion has a cellulose nanofiber concentration of 2.0 wt. % or more.
6 . The method for producing a honeycomb structure according to claim 1 , wherein the dispersion has a pH of 4.0 to 7.8.