Condensation cross-linking polysiloxane masses, a process for preparing the same and surface-modified fillers

1. Polysiloxane compositions which cross-link by condensation and which comprise:

a) at least one cross-linkable polysiloxane comprising as a reactive terminal group at least one of the following groups

—O—SiR 1 2 OH,

—O—SiR 1 (OR 2 ) 2 , or

—O—Si(OR 2 ) 3 ,

wherein

R 1 denotes optionally substituted C 1 –C 8 -alkyl, C 6 –C 14 -aryl or C 2–C 8 -alkenyl groups and

R 2 denotes optionally substituted linear or branched C 1 –C 8 -alkyl or C 2 –C 8 -alkoxyalkyl groups, and R 1 and R 2 can be the same or different within the molecule,

b) at least one basic filler and optionally other fillers,

c) at least one phosphorus compound selected from the group consisting of

i) orthophosphoric acid esters of the following formula

O═P(OR 3 ) 3-n OH n

in which

n=0, 1 or 2 and

R 3 =an optionally substituted linear or branched C 1 –C 30 -alkyl, C 1 –C 30 -acyl, C 2 –C 3 -alkenyl, C 2 –C 30 -alkoxyalkyl, C 5 –C 14 -cycloalkyl or C 6 –C 10 -aryl group or a triorganosilyl or diorganoalkoxysilyl group and each R 3 can be the same or different within the molecule, and wherein when, n denotes 0, at least one of the substituents R 3 is a triorganosilyl or diorganoalkoxysilyl radical, and

ii)esters of polyphosphoric acid,

d) at least one alkoxysilane cross-linking agent selected from the group consisting of tetraethoxysilane, tetra-n-propoxysilane, methyltriethoxysilane, methyltrimethoxysilane, methyltri(2-methoxyethoxy)silane, vinyltrimethoxysilane, vinyltriethoxysilane and partial hydrolyzates thereof,

e) at least one organometallic compound selected from the group consisting of organic titanium compounds and organic tin compounds and

f) optionally other auxiliary substances selected from the group consisting of plasticizers, bonding agents, pigments and fungicides, wherein the phosphorus compound c) is an ester of orthophosphoric acid containing at least one optionally substituted linear or branched C 4 –C 30 -alkyl group R 3 .

2. Polysiloxane compositions which cross link by condensation, according to claim 1 , wherein the cross-linkable polysiloxane a) has a viscosity of between 0.1 and 1000 Pa·s.

3. Polysiloxane compositions according to claim 1 , wherein the basic fillers b) are precipitated or ground chalks.

4. Polysiloxane compositions according to claim 1 , wherein the organometallic compound e) is an organic titanium or tin compound.

5. Polysiloxane compositions according to claim 1 consisting essentially of

100 parts by, weight of a),

10 to 250 parts by weight of b),

0.1 to 25 parts by weight of c),

1 to 30 parts by weight of d),

0.1 to 20 parts by weight of e) and

0 to 240 parts by weight of f).

6. Polysiloxane compositions according to claim 1 , wherein the auxiliary substance f) has the following composition:

0–100 parts by weight of plasticizers,

0–20 parts by weight of bonding agents,

0–100 parts by weight of pigments,

0–20 parts by weight of fungicides,

the sum of all the components f) in the mixture amounting to a maximum of 240 parts by weight.

7. Process for the production of the polysiloxane compositions of claim 1 , wherein the basic fillers b) and the phosphorus compound c), optionally dissolved in a solvent, are mixed in a preliminary operation.

8. Sealants, adhesives or coating compositions, comprising a composition of claim 1 .