Low-odor, cold-curing (METH) acrylate reaction resin for floor coating, a floor coating containing the reaction resin, and a process for the preparation of the floor coating

1. A low-odor, cold-curing (meth)acrylate reaction resin for a floor coating, comprising:

(A) at least one methacrylate selected from the group consisting of hexyl methacrylate, cyclohexyl methacrylate, and benzyl methacrylate; and 3–10 wt % of a multifunctional (meth)acrylate;

wherein the sum of all components in (A) is 100 wt %;

(B) 0–2 parts by weight per 1 part by weight of Component (A) of a pre-polymer that dissolves or swells in (A);

(C) 2–5 parts by weight per 100 parts by weight based on Components (A)+(B) of at least one paraffin and/or wax;

(D) a redox system, containing an accelerator and a peroxide catalyst or initiator in an amount that is adequate for cold-curing of Component (A); and

(E) optionally, at least conventional additive.

2. The reaction resin according to claim 1 , wherein said multifunctional (meth)acrylate is 1,4-butanediol dimethacrylate; component (B) is a polymer based on butyl methacrylate and methyl methacrylate.

3. The reaction resin according to claim 1 , wherein the multifunctional (meth)acrylate and component (C) are together present in an amount effective for the reaction resin, when applied to concrete at a thickness of approximately 1 cm and set at ambient temperature for 90 minutes, to be non-tacky.

4. A low-odor, cold-curing (meth)acrylate reaction resin for a floor coating, comprising:

(A) (a) 50–100 wt % of a (meth)acrylate comprised of

0–5 wt % of a methyl (meth)acrylate;

0–5 wt % of an ethyl (meth)acrylate;

0–97 wt % of a C 3 –C 6 (meth)acrylate;

0–50 wt % of ≧C 7 (meth)acrylate;

3–10 wt % of a multifunctional (meth)acrylate; and

(b) 0–50 wt % of a comonomer, comprised of

0–30 wt % of a vinyl aromatic; and

0–30 wt % of a vinyl ester

wherein the sum of all components of (a) and (b) in (A) is 100 wt %, and wherein component (A) includes at least one (meth)acrylate selected from the group consisting of methacrylates of unsaturated alcohols, nitrogen-containing methacrylates, carbonyl-containing methacrylates, cycloalkyl methacrylates, halogenated methacrylates, oxiranyl methacrylates, phosphorus-containing methacrylates, boron-containing methacrylates, silicon-containing methacrylates, sulfur-containing methacrylates, and corresponding acrylates having a boiling point greater than 120° C.;

(B) 0–2 parts by weight per 1 part by weight of Component (A) of a pre-polymer that dissolves or swells in (A); and wherein the proportion of methyl (meth)acrylate or ethyl (meth)acrylate is less than 5 wt %, based on Component (B);

(C) 2–5 parts by weight per 100 parts by weight based on Components (A)+(B) of at least one paraffin and/or wax;

(D) a redox system, containing an accelerator and a peroxide catalyst or initiator in an amount that is adequate for cold-curing of Component (A); and

(E) optionally, at least one conventional additive.