Solid polymer electrolyte and use thereof
View Patent ↗A polyether copolymer having a weight-average molecular weight of 10 4 to 10 7 , formed from 3 to 30% by mol of a repeating unit derived from propylene oxide, 96 to 69% by mol of a repeating unit derived from ethylene oxide, and 0.01 to 15% by mol of a crosslinkable repeating unit derived from a reactive oxirane compound, gives a provide a crosslinked solid polymer electrolyte which is superior in processability, moldability, mechanical strength, flexibility and heat resistance, and has markedly improved ionic conductivity.
1. A solid polymer electrolyte comprising: (I) a crosslinked material of a polyether copolymer; (II) an electrolyte salt compound; and (III) a plasticizer which may be added if necessary and is selected from the group consisting of an aprotic organic solvent, a derivative or a metal salt of a linear or branched polyalkylene glycol, and a metal salt of said derivative,
wherein the polyether copolymer having a weight-average molecular weight of 10 5 to 10 7 , comprises as a main chain:
A) 3 to 30% by mol of a repeating unit (I′), derived from propylene oxide;
B) 96 to 69% by mol of a repeating unit (II′), derived from ethylene oxide; and
CH 2 —CH 2 —O (II′)
C) 0.01 to 15% by mol of a repeating unit (III′-1) and/or (III′-2), derived from a crosslinkably reactive monomer;
wherein R 1 and R 2 are groups each having a reactive functional group.
2. The solid polymer electrolyte according to claim 1 , wherein the reactive functional group in the repeating unit (C) is (a) an ethylenically unsaturated group, (b) a reactive silicon group, (c) an epoxy group or (d) a halogen atom.
3. The solid polymer electrolyte according to claim 2 , wherein the monomer having the ethylenicallyunsaturated groupwhichconstitutes the repeating unit (C) is selected from the group consisting of allyl glycidyl ether, 4-vinylcyclohexyl glycidyl ether, α-terpenyl glycidyl ether, cyclohexenyl methyl glycidyl ether, p-vinylbenzyl glycidyl ether, allyl phenyl glycidyl ether, vinyl glycidyl ether, 3,4-epoxy-1-butene, 3,4-epoxy-1-pentene, 4,5-epoxy-2-pentene, 1,2-epoxy-5,9-cyclododecadiene, 3,4-epoxy-1-vinylcyclohexene, 1,2-epoxy-5-cyclooctene, glycidyl acrylate, glycidyl methacrylate, glycidyl sorbate, glycidyl cinnamate, glycidyl crotonate and glycidyl-4-hexenoate.
4. The solid polymer electrolyte according to claim 2 , wherein the monomer having the reactive silicon group which constitutes the repeating unit (C) is selected from the group consisting of 3-glycidoxy propyl trimethoxy silane, 3-glycidoxypropyl methyl dimethoxy silane, 4-(1,2-epoxy) butyl trimethoxy silane and 2-(3,4-epoxycyclohexyl) ethyl trimethoxy silane.
5. The solid polymer electrolyte according to claim 2 , wherein the monomer having two epoxy groups which constitutes the repeating unit (C) is 2,3-epoxypropyl-2′,3′-epoxy-2′-methylpropyl ether or ethyleneglycol-2,3-epoxypropyl-2′,3′-epoxy-2′-methylpropyl ether.
6. The solid polymer electrolyte according to claim 2 , wherein the monomer having the halogen atom which constitutes the repeating unit (C) is selected from the group consisting of epichlorohydrin, epibromohydrin and epiiodohydrin.
7. The solid polymer electrolyte according to claim 2 , wherein the polyether copolymer comprises: 5 to 25% by mol of the repeating unit (A); 94 to 74% by mol of the repeating unit (B); and 0.01 to 10% by mol of the repeating unit (C).
8. The solid polymer electrolyte according to claim 1 , wherein the electrolyte salt compound (II) is a compound composed of a cation selected from metal cation, ammonium ion, amidinium ion and guanidium ion, and an anion selected from chloride ion, bromide ion, iodide ion, perchlorate ion, thiocyanate ion, tetrafluoroborate ion, nitrate ion, AsF 6 − , PF 6 − , stearylsulfonate ion, octylsulfonate ion, dodecylbenzenesulfonate ion, naphthalenesufonate ion, dodecylnaphthalenesulfonate ion, 7,7,8,8-tetracyano-p-quinodimethane ion, X 1 SO 3 − , [(X 1 SO 2 )(X 2 SO 2 )N] + , [(X 1 SO 2 )(X 2 SO 2 ) (X 3 SO 2 )C] + and [(X 1 SO 2 )(X 2 SO 2 ) YC] + (wherein X 1 , X 2 , X 3 and Y respectively represent an electron attractive group).
9. The solid polymer electrolyte according to claim 8 , wherein X 1 , X 2 and X 3 independently represent a perfluoroalkyl group having 1 to 6 carbon atoms or a perfluoroaryl group having 6 to 20 carbon atoms, and Y represents a nitro group, a nitroso group, a carbonyl group, a carboxyl group or a cyano group.
10. The solid polymer electrolyte according to claim 8 , wherein the metal cation is a cation of a metal selected from Li, Na, K, Rb, Cs, Mg, Ca, Ba, Mn, Fe, Co, Ni, Cu, Zn and Ag.
11. The solid polymer electrolyte according to claim 1 , wherein the aprotic organic solvent is an aprotic organic solvent selected from ethers or esters.
12. The solid polymer electrolyte according to claim 1 , wherein the polyalkylene glycol is polyethylene glycol or polypropylene glycol.
13. The solid polymer electrolyte according to claim 1 , wherein the derivative of the polyalkylene glycol is an ether derivative or an ester derivative.
14. The solid polymer electrolyte according to claim 1 , wherein the metal salt of the polyalkylene glycol is selected from the group consisting of a sodium salt of the polyalkylene glycol, a lithium salt of the polyalkylene glycol, and a dialkyl aluminum salt of the polyalkylene glycol.
15. A battery comprising:
a solid polymer electrolyte according to claim 1 ;
a positive electrode; and
a negative electrode.