Heat treatment for cold worked nitinol to impart a shape setting capability without eventually developing stress-induced martensite
View Patent ↗Cold worked nickel-titanium alloys that have linear pseudoelastic behavior without a phase transformation or onset of stress-induced martensite as applied to a medical device having a strut formed body deployed from a sheath. In one application, an embolic protection device that employs a linear pseudoelastic nitinol self-expanding strut assembly with a small profile delivery system for use with interventional procedures. The expandable strut assembly is covered with a filter element and both are compressed into a restraining sheath for delivery to a deployment site downstream and distal to an interventional procedure. Once at the desired site, the restraining sheath is retracted to deploy the embolic protection device, which captures flowing emboli generated during the interventional procedure. Linear pseudoelastic nitinol is used in the medical device as distinct from non-linear pseudoelastic (i.e., superelastic) nitinol.
1. A method of making an intralumen device, comprising:
receiving tubing made from a nickel-titanium alloy that is in a substantially fully martensitic state;
forming a plurality of struts in the received tubing to form a body;
cold working the body at least about 38 percent as measured by reduction in cross-sectional area, the nickel-titanium alloy remaining in the substantially fully martensitic state following the cold working;
heat treating the cold-work body under conditions so that the cold-work body remains in the substantially fully martensitic state; and
incorporating the heat-treated cold-worked body into the intralumen device.
2. The method of claim 1 wherein forming a plurality of struts in the received tubing to form a body comprises laser cutting the received tubing to form the plurality of struts.
3. The method of claim 1 wherein forming a plurality of struts in the received tubing to form a body comprises etching the received tubing to form the plurality of struts.
4. The method of claim 1 wherein the nickel-titanium comprises at least one additional alloying element selected from the group consisting of palladium, platinum, tungsten, and tantalum.
5. The method of claim 1 wherein incorporating the heat-treated cold-worked body into the intralumen device comprises incorporating the heat-treated cold-worked body into an embolic filter.
6. A method of making an intralumen device, comprising:
receiving tubing made from a nickel-titanium alloy that is in a substantially fully martensitic state;
forming a plurality of struts in the received tubing to form a body;
cold working the body at least about 38 percent as measured by reduction in cross-sectional area, the nickel-titanium alloy remaining in the substantially fully martensitic state following the cold working;
incorporating the cold-worked body into the intralumen device; and
wherein an accumulated heat treatment that the received tubing and the cold-worked body receives is up to 300° C. for up to 5 minutes.
7. The method of claim 6 wherein forming a plurality of struts in the received tubing to form a body comprises laser cutting the received tubing to form the plurality of struts.
8. The method of claim 6 wherein forming a plurality of struts in the received tubing to form a body comprises etching the received tubing to form the plurality of struts.
9. The method of claim 6 wherein the nickel-titanium comprises at least one additional alloying element selected from the group consisting of palladium, platinum, tungsten, and tantalum.
10. The method of claim 6 wherein incorporating the cold-worked body into the intralumen device comprises incorporating the cold-worked body into an embolic filter.