In-press process for coating composite substrates
View Patent ↗An improved process for manufacture of polymer coated composite substrates is described. A coated composite substrate is prepared in the press by applying a layer of a primer coating composition to the surface of a compressible mat comprising fibers and/or particles and a resin binder. The primer coating composition is formulated preferably as a fast setting polymer latex capable of forming a chemically crosslinked polymer matrix when applied to the surface of a compressible mat. A thermosetting top coat composition can be applied directly over the primer coating composition before heat-processing the mat to improve surface quality and release characteristics. Compressing and heating the coated mat produces a finished composite substrate directly out of the press.
1. A process comprising:
applying directly on a surface of a wood composite material selected from one of hardboard, medium density fiberboard, oriented strand board, particle board or plywood a formaldehyde-free, chemically crosslinkable primer coating composition, wherein the wood composite material comprises at least one of wood chips, flakes, fibers and particles in a resin binder composition, and wherein the crosslinkable primer coating composition comprises:
95 to 99% by weight, based on weight of dry materials in the composition, of an anionically stabilized aqueous emulsion of a copolymer with a T g of −10° C. to 50° C., the polymer comprising in polymerized form a polymerization mixture containing two or more ethylenically unsaturated monomers; 0.2 to 5% by weight of a polyimine compound having a number average molecular weight from 250 to 20,000; and 0.2 to 5% by weight of a volatile base;
wherein the chemically crosslinkable composition forms a chemically crosslinked polymer matrix when, or as, the composition is being applied to the wood composite material;
applying on the crosslinked polymer matrix a top coat composition comprising a thermoplastic or a thermosetting polymer latex composition to form a top coat layer; and
compressing and heating the crosslinked polymer matrix, the top coat layer, and the wood composite material.
2. The process of claim 1 , wherein the chemically crosslinkable composition has a solids content from about 30% to about 80% by weight.
3. The process of claim 1 , wherein the chemically crosslinkable composition has a solids content from about 20% to about 70% by weight.
4. The process of claim 1 , wherein the primer coating composition has a pH of about 8 to about 11.
5. The process of claim 1 , wherein up to up to 5 wt % of the monomers in the polymerization mixture are α-β-ethylenically unsaturated aliphatic carboxylic acid monomers.
6. The process of claim 1 , wherein the monomers comprise (meth)acrylate monomers.
7. The process of claim 1 , wherein the volatile base comprises ammonium hydroxide.
8. A process comprising:
applying directly on a surface of a wood composite material selected from one of hardboard, medium density fiberboard, oriented strand board, particle board or plywood a formaldehyde-free, chemically crosslinkable primer coating composition, wherein the wood composite material comprises at least one of wood chips, flakes, fibers and particles in a resin binder composition, and wherein the crosslinkable primer coating composition comprises:
95 to 99% by weight, based on weight of dry materials in the composition, of an anionically stabilized aqueous emulsion of a copolymer with a T g of −10° C. to 50° C., the polymer comprising in polymerized form a polymerization mixture containing two or more ethylenically unsaturated monomers; 0.2 to 5% by weight of a polyimine compound having a number average molecular weight from 250 to 20,000; and 0.2 to 5% by weight of a volatile base;
wherein the chemically crosslinkable composition forms a chemically crosslinked polymer matrix when, or as, the composition is being applied to the wood composite material;
applying on the crosslinked polymer matrix a top coat composition comprising a thermoplastic or a thermosetting polymer latex composition to form a top coat layer;
applying a release coat composition on the top coat composition; and
compressing and heating the crosslinked polymer matrix, the top coat layer, and the wood composite material.
9. The process of claim 1 , wherein the compressing and heating step forms a construction material selected from a finished door skin or an exterior hardboard siding product.
10. The process of claim 8 , wherein the compressing and heating step forms a construction material selected from a finished door skin or an exterior hardboard siding product.
11. A process consisting of the following steps, in order:
applying directly on a surface of a wood composite material selected from one of hardboard, medium density fiberboard, oriented strand board, particle board or plywood a formaldehyde-free, chemically crosslinkable primer coating composition, wherein the wood composite material comprises at least one of wood chips, wood flakes, wood fibers and wood particles in a resin binder composition, and wherein the primer coating composition comprises a polymer latex that forms a chemically crosslinked polymer matrix when, or as, the primer coating composition is being applied to the wood composite material;
applying on the crosslinked polymer matrix a top coat composition comprising a polymer latex composition to form a top coat layer; and
compressing and heating the crosslinked polymer matrix, the top coat layer, and the wood composite material.
12. The process of claim 11 , wherein the compressing and heating step forms a construction material selected from is a finished door skin or an exterior hardboard siding product.
13. A process consisting of the following steps, in order:
placing in a mold a wood composite material selected from one of hardboard, medium density fiberboard, oriented strand board, particle board or plywood, wherein the wood composite material comprises at least one of wood chips, wood flakes, wood fibers and wood particles in a resin binder composition, and wherein the mold is sized to form a door or an exterior hardboard siding product;
applying directly on a surface of the wood composite material a formaldehyde-free, chemically crosslinkable primer coating composition, wherein the primer coating composition comprises a polymer latex that forms a chemically crosslinked polymer matrix when, or as, the primer composition is being applied to the compressible mat;
applying on the crosslinked polymer matrix a top coat composition comprising a polymer latex composition to form a top coat layer; and
compressing and heating the crosslinked polymer matrix, the top coat layer, and the wood composite material in the mold to form a finished door or a finished exterior hardboard siding product.