Radiopaque nitinol alloys for medical devices
View Patent ↗A radiopaque nitinol medical device such as a stent for use with or implantation in a body lumen is disclosed. The stent is made from a superelastic alloy such as nickel-titanium or nitinol, and includes a ternary element selected from the group of chemical elements consisting of iridium, platinum, gold, rhenium, tungsten, palladium, rhodium, tantalum, silver, ruthenium, or hafnium. The added ternary element improves the radiopacity of the nitinol stent comparable to that of a stainless steel stent of the same size and strut pattern coated with a thin layer of gold. The nitinol stent has improved radiopacity yet retains its superelastic and shape memory behavior and further maintains a thin strut/wall thickness for high flexibility.
1. A method for providing a superelastic, radiopaque metallic stent for medical applications, comprising:
providing a tubular-shaped body having a thin wall, wherein the body includes a superelastic nickel-titanium alloy and the alloy further includes a ternary element selected from the group of chemical elements consisting of: iridium, platinum, gold, rhenium, tungsten, palladium, rhodium, tantalum, silver, ruthenium, or hafnium;
wherein the step of providing a tubular-shaped body includes melting nickel, titanium, and the ternary element, cooling to form an alloy ingot, hot forming the alloy ingot, forming the alloy ingot into a cylinder, drilling the cylinder to form tubing, drawing the tubing, and annealing the tubing, forming a strut pattern;
wherein the stent is radiopaque.
2. The method of claim 1 , wherein the atomic percent of platinum is greater than 2.5 and less than or equal to 15.
3. The method of claim 1 , wherein the atomic percent of palladium is greater than 2.5 and less than or equal to 20.
4. The method of claim 1 , wherein an austenite finish temperature (A f ) of the superelastic alloy in the stent is greater than or equal to about zero and less than or equal to about 37 degrees C.
5. The method of claim 1 , wherein the ingot after melting includes an austenite finish temperature (A f ) of greater than or equal to about 0 degrees C. and less than or equal to about 40 degrees C.
6. The method of claim 1 , wherein the tubing includes an austenite finish temperature (A f ) of greater than or equal to about −15 degrees C. and less than or equal to about 15 degrees C.
7. The method of claim 1 , wherein the ingot is remelted.
8. The method of claim 1 , wherein the alloy includes a quaternary element.