Membranes containing sulfonated polyetherketone and another polymer, method for the production and use thereof
View Patent ↗Membranes comprising sulfonated polyether ketone and another polymer, process for their production, and their use, Membranes comprising from 30 to 99.5% by weight of a sulfonated, strictly alternating polyether ketone (A) having repeat units of the formula (I) —Ar—O—Ar′—CO—, where Ar and Ar′, independently of one another, are bivalent aromatic radicals, with an ion exchange capacity of from 1.3 to 4.0 meq of —SO 3 H/g of polymer and from 0.5 to 70% by weight of a partially fluorinated, nonfluorinated or perfluorinated polymer (B) are described. The membranes may be used in fuel cells.
1. A membrane comprising a blend comprising
from 30 to 99.5% by weight of a sulfonated, strictly alternating polyether ketone (A) having repeat units of the formula (I)—Ar—O—Ar′—CO—, where Ar and Ar′, independently of one another, are bivalent aromatic radicals, with an ion-exchange capacity of from 1.3 to 4.0 meq of —SO 3 H/g of polymer and from 0.5 to 70% by weight of a partially fluorinated, nonfluorinated or perfluorinated polymer (B) which is a polyether sulfone of the formula —Ar—O—Ar′—SO 2 —, where Ar and Ar′ are as defined above.
2. A membrane as claimed in claim 1 , where Ar is a phenylene radical having para bonds and/or meta bonds and Ar′ is a phenylene, naphthylene, biphenylene or anthrylene radical.
3. The membrane as claimed in claim 1 , wherein the partially fluorinated, nonfluorinated or perfluorinated polymer (B) is a polymer soluble in organic solvents.
4. The membrane as claimed in claim 1 , wherein the membrane has mechanical properties which remain almost unchanged even after boiling in water for at least 50 hours.
5. A membrane as claimed in claim 1 , wherein the modulus of elasticity in the dry state at 23° C. and 50% relative humidity is ≧600 MPa.
6. A membrane as claimed in claim 1 , wherein the modulus of elasticity (determined as gradient of the tangent at 1.2 MPa) in water at 60° C. is at least 90 MPa and the ultimate elongation is ≧200%.
7. A process for producing (a) the membrane as claimed in claim 1 , which comprises reacting a sulfonated polyether ketone (A) with a polymer (B) in a weight ratio in the range from 0.01 to 0.5 (B/A) in a solvent, filtering off, spreading the solution on a sheet-like support and then drying at a temperature of from 25 to 140° C.
8. A fuel cell which comprises the membrane the claimed in claim 1 .
9. The fuel cell as claimed in claim 8 , wherein the fuel cell is a direct methanol fuel cell.
10. A high performance capacitor which comprises the membrane as claimed in claim 1 .
11. The membrane as claimed in claim 1 , wherein the membrane has a thickness of at least 30 μm.
12. The fuel cell as claimed in claim 9 , wherein polymer (B) is present in an amount from 5 to 50% wt.
13. The membrane as claimed in claim 1 , wherein the modulus of elasticity in the dry state at 23° C. is from 600 to 3,000 MPa with an ultimate elongation in a range from 30 to 200%.
14. The membrane as claimed in claim 6 , wherein the ultimate elongation is from 200 to 800% and has a modulus of elasticity from 100 to 700 MPa.
15. The membrane as claimed in claim 1 , wherein polymer (B) is present in an amount up to 40% by weight.
16. The membrane as claimed in claim 1 , wherein polymer (B) is present in an amount up to 20% by weight.