Structure comprising a binder layer non-delaminable with respect to a metallized substrate and peelable with respect to a polypropylene substrate
View Patent ↗A multilayer structure of, in succession, a metal layer or a metallized-substrate layer, a layer of a polypropylene-based binder extrusion-coated at a rate of more than 100 m/min. and optionally a polypropylene layer, the metal or metallized layer and the binder layer being made non-delaminable by heat treating the structure. The extrudable binder contains by weight: (A) 5 to 30% of a copolymer of ethylene and one or more comonomers chosen from the group of carboxylic acid esters, vinyl esters and dienes in particular the ethylene/alkyl (meth)acrylate/maleic anhydride terpolymer; (B) 40 to 93% of a stretchable polypropylene; and (C) 2 to 30% of a polypropylene functionalized by an unsaturated carboxylic acid anhydride, especially maleic anhydride; the MFI of the composition being between 10 and 50 g/10 min. (at 230° C./2.16 kg). the multi-layer structure is useful for the production of packages.
1. A multilayer structure comprising a metal layer or a metallized-substrate layer ( 5 ) and a binder layer ( 6 ) comprising polypropylene, extrusion-coated at a rate of more than 100 m/min. onto the metal or metallized-substrate layer, said layers ( 6 , 5 ) being made non-delaminable by heat treating the said structure to a temperature above the melting point of the binder layer ( 6 ), and a polypropylene layer ( 2 ) having a melting point above the melting point of the binder, the binder layer ( 6 ) being sandwiched between the metal layer or metallized-substrate layer ( 5 ) and the polypropylene layer ( 2 ), wherein said structure is peelable between binder layer ( 6 ) and polypropylene layer ( 2 ), and said binder layer ( 6 ) comprises by weight:
5 to 30% of a copolymer (A) based on ethylene and one or more comonomers chosen from the group consisting of carboxylic acid esters, vinyl esters and dienes;
40 to 93% of a stretchable polypropylene (B), stretchability being defined as the ability of a rod extruded at a temperature of between 190° C. and 240° C. and pulled at a pull rate of between 50 and 250 m/min. without breaking;
2 to 30% of an additional polypropylene (C) functionalized by an unsaturated carboxylic acid anhydride;
the MFI of the composition being between 10 and 50 g/10 min. at 230° C./2.16 kg.
2. A structure according to claim 1 , wherein the heat treatment is carried out by infrared radiation, by passing it through a hot air or induction-heating tunnel.
3. A structure according to claim 1 , wherein said structure comprises polypropylene layers ( 7 ) and ( 2 ) having a melting point above the melting point of the binder, the binder layer ( 6 ) being sandwiched between the metal layer or metallized-substrate layer ( 5 ) and the polypropylene layer ( 7 ), the heat treating being at a temperature below the melting temperature of the polypropylene layer ( 7 ).
4. A process of producing the multi-layer structure of claim 3 , comprising the step of extrusion-coating said binder layer at a rate of more than 100 m/min. onto said metal or metallized substrate layer, and heat treating the resultant extrusion coated structure at a temperature above the melting point of the binder layer, said heat treating being at a temperature below the melting temperature of the polypropylene layer ( 2 ).
5. A structure according to claim 3 , wherein said structure is peelable with a peel force for peeling a binder layer ( 6 ) off the polypropylene layer ( 7 , 2 ) of between 8 and 15 N/15 mm.
6. A structure according to claim 1 , wherein the copolymer (A) of the binder comprises an ethylene/alkyl (meth)acrylate copolymer containing from 5 to 40% by weight of alkyl (meth)acrylate, the MFI being between 0.5 and 200 g/10 min. at 190° C./2.16 kg.
7. A structure according to claim 6 , wherein the ethylene/alkyl (meth)acrylate copolymer contains 10-40% by weight of the alkyl acrylate.
8. A structure according to claim 1 , wherein the copolymer (A) of the binder comprises an ethylene/alkyl (meth)acrylate/maleic anhydride copolymer containing from above 0 to 10% by weight of maleic anhydride and from 2 to 40% by weight of alkyl (meth)acrylate, the MFI being between 0.5 and 200 g/10 min. at 190° C./2.16 kg.
9. A structure according to claim 8 , wherein the ethylene/alkyl (meth)acrylate/maleic anhydride copolymer contains 5 to 40% by weight of the alkyl meth(acrylate).
10. A structure according to claim 1 , wherein the copolymer (A) of the binder is a blend of copolymers (A), of an ethylene/alkyl (meth)acrylate copolymer containing 5 to 40% by weight of alkyl (meth)acrylate, and of an ethylene/alkyl (meth)acrylate/maleic anhydride copolymer containing from above 0 to 10% by weight of maleic anhydride and from 2 to 40% by weight of alkyl (meth)acrylate.
11. A structure according to claim 1 , in which the proportion of polypropylene (C) in the binder is between 1.5 and 6% by weight, said polypropylene (C) containing from 1.5 to 6% by weight of maleic anhydride.
12. A structure according to claim 1 , in which the proportion of polypropylene (C) in the binder is between 10 and 25% by weight, said polypropylene (C) containing from 0.8 to 1.5% by weight of maleic anhydride.
13. A structure according to claim 1 , in which the proportion of polypropylene (C) in the binder is between 3 and 5% by weight, said polypropylene (C) containing from 1.5 to 3% by weight of maleic anhydride.
14. A package made with a structure according to claim 1 .
15. A package according to claim 14 , characterized in that it is sterilizable and resistant to food acids and high-performance solvents and greases.
16. A process of producing the multi-layer structure of claim 1 , comprising the step of extrusion-coating said binder layer at a rate of more than 100 m/min. onto said metal or metallized substrate layer, and heat treating the resultant extrusion coated structure at a temperature above the melting point of the binder layer.
17. A structure according to claim 1 , wherein said structure is peelable with a peel force for peeling the binder layer ( 6 ) off the polypropylene layer ( 2 ) of between 8 and 15 N/15 mm.
18. A multilayer structure comprising a metal layer or a metallized-substrate layer ( 5 ) and a binder layer ( 6 ) comprising polypropylene, extrusion-coated at a rate of more than 100 m/min. onto the metal or metallized-substrate layer, said layers ( 6 , 5 ) being made non-delaminable by heat treating the said structure to a temperature above the melting point of the binder layer ( 6 ), and a polypropylene layer ( 2 ) having a melting point above the binder layer ( 6 ) being sandwiched between the metal layer or metallized-substrate layer ( 5 ) and the polypropylene layer ( 2 ), wherein said structure is peelable between binder layer ( 6 ) and polypropylene layer ( 2 ), and said binder layer ( 6 ) comprises a copolymer (A) based on ethylene and carboxylic acid esters, vinyl esters and dienes; polypropylene (B), and additional polypropylene (C) functionalized by an unsaturated carboxylic acid anhydride.
19. A structure according to claim 18 , wherein copolymer (A) is not grafted.
20. A multilayer structure comprising a metal layer or a metallized-substrate layer ( 5 ) and a binder layer ( 6 ) comprising polypropylene, extrusion-coated at a rate of more than 100 m/min. onto the metal or metallized-substrate layer, said structure having been heat treated to a temperature above the melting point of the binder layer ( 6 ), and a polypropylene layer ( 2 ) the binder layer ( 6 ) being sandwiched between the metal layer or metallized-substrate layer ( 5 ) and the polypropylene layer ( 2 ), wherein said structure is peelable between binder layer ( 6 ) and polypropylene layer ( 2 ), and said binder layer ( 6 ) comprises a copolymer (A) based on ethylene and carboxylic acid esters, vinyl esters and dienes; polypropylene (B), and additional polypropylene (C) functionalized by an unsaturated carboxylic acid anhydride.