Thick products made of heat-treatable aluminum alloy with improved toughness and process for manufacturing these products
View Patent ↗The object of the invention is a rolled, forged or extruded aluminum alloy product more than 12 mm thick, heat treated by solutionizing, quenching and artificial aging, with a microstructure characterized by the following parameters: the fraction of recrystallized grains measured between one-quarter thickness and mid-thickness of the final wrought product is smaller than 35% by volume; the characteristic intercept distance between recrystallized areas is greater than 250 μm, preferably greater than 300 μm and most preferably greater than 350 μm.
1. A partially recrystallized, rolled, forged or extruded AA7050 aluminum alloy product more than 12 mm thick,
produced by casting an AA7050 aluminum alloy into a cast ingot having an as cast grain size between 270 and 800 μm, and heat treating the ingot by solution treating, quenching and artificial aging,
a final wrought product produced thereby having a fraction of recrystallized grains measured between one-quarter thickness and mid-thickness less than 35% by volume, and a characteristic intercept distance between recrystallized areas greater than 250 μm.
2. The product according to claim 1 , wherein the as-cast grain size is 270–600 μm.
3. The product according to claim 1 , wherein the characteristic intercept distance is up to 384 μm.