Process for producing self-extinguishing cables with low-level production of fumes, and flame-retardant compositions used therein
View Patent ↗Process for producing cables, in particular electrical cables for low-voltage power transmission or for telecommunications, which have self-extinguishing properties and produce a low level of fumes, in which the flame-retardant coating layer is obtained by extruding a flame-retardant composition comprising a polymer base, an inorganic flame-retardant filler and a dehydrating agent. The presence of the dehydrating agent makes it possible to obtain a smooth and uniform flame-retardant layer which is virtually free of pores.
1. Process for producing self-extinguishing cables with low-level production of fumes, which comprises:
(a) preparing a flame-retardant composition comprising a polymer base and an inorganic flame-retardant filler, wherein the polymer base and the inorganic flame-retardant filler are mixed at a predetermined temperature for a predetermined time so as to reduce moisture contained in the inorganic flame-retardant filler, and then a dehydrating agent is added to the resulting composition;
(b) extruding said flame-retardant composition on an electrical conductor, which is optionally precoated with an insulating layer, so as to obtain a flame-retardant coating.
2. Process according to claim 1 , in which the dehydrating agent is added during phase (a) of preparation of the flame-retardant composition.
3. Process according to claim 1 , in which the dehydrating agent is added to the flame-retardant composition in divided form.
4. Process according to claim 1 , in which the dehydrating agent is added to the flame-retardant composition after first being dispersed in a polymer material.
5. Process according to claim 1 , in which the flame-retardant composition is extruded at a predetermined temperature which depends on the extrusion rate to be obtained.
6. Process according to claim 5 , in which the flame-retardant composition is extruded at a temperature of between 160° C. and 320° C.
7. Process according to claim 6 , in which the flame-retardant composition is extruded at a temperature of between 200° C. and 280° C.
8. Process according to claim 1 , in which the dehydrating agent is chosen from: calcium oxide, calcium chloride, anhydrous alumina, zeolites, magnesium sulphate, magnesium oxide, barium oxide, the like, and mixtures thereof.
9. Process according to claim 8 , in which the dehydrating agent is chosen from: calcium oxides, zeolites, and mixtures thereof.
10. Process according to claim 1 , in which the dehydrating agent is added to the flame-retardant composition in an amount of between 0.5 and 15% by weight relative to the weight of the flame-retardant filler.
11. Process according to claim 10 , in which the dehydrating agent is added to the flame-retardant composition in an amount of between 1 and 10% by weight relative to the weight of the flame-retardant filler.
12. Process according to claim 1 , in which the flame-retardant filler is chosen from: hydroxides, hydrated oxides, salts, and hydrated salts of metals.
13. Process according to claim 12 , in which the flame-retardant filler is chosen from: magnesium hydroxide, alumina trihydrate, hydrated magnesium carbonate, magnesium carbonate, hydrated calcium and magnesium carbonate, calcium and magnesium carbonate, and mixtures thereof.
14. Process according to claim 13 , in which the flame-retardant filler is magnesium hydroxide.
15. Process according to claim 13 , in which the flame-retardant filler is magnesium hydroxide of natural origin.