Magnetic roller and methods of producing the same
View Patent ↗A magnetic roller for electrophotography comprises a foamed resin magnetic material. A method of producing a magnetic roller comprises the steps of providing magnetic filler, a resin binder and a foaming agent in a closed mold; activating the foaming agent in the closed mold; and removing the resulting formed roller from the mold.
1. A magnet roller comprising a foamed mixture of resin and magnetic material having no bubbles of said foam at the outside of said roller.
2. The magnetic roller of claim 1 , wherein the foamed resin magnetic material comprises from about 80 to about 95 weight percent of magnetic filler and from about 5 to about 20 weight percent of resin binder.
3. The magnetic roller of claim 2 , wherein the magnetic filler comprises a ferrite filler.
4. The magnetic roller of claim 2 , wherein the magnetic filler comprises barium ferrite, strontium ferrite, a rare earth-cobalt alloy, a rare earth iron-boron alloy, or mixtures thereof.
5. The magnetic roller of claim 2 , wherein the resin binder comprises nylon.
6. The magnetic roller of claim 2 , wherein the resin binder comprises nylon-6, nylon-12, nylon-6/6, nylon 6/10, nylon 6/12, polyvinyl chloride or polypropylene.
7. The magnetic roller of claim 4 , where the ferrite filler comprises strontium ferrite filler.
8. The magnet roller of claim 2 , wherein the foamed mixture of resin binder and magnetic material further comprises glass fibers, carbon filler, or mixtures thereof.
9. The magnetic roller of claim 1 , wherein the roller contains at least 5 weight percent less of said magnetic filler and said resin binder as compared with the same sized roller formed from non-foamed said magnetic filler and said resin binder and exhibits substantially equivalent magnetic performance as such a same sized roller.
10. The magnetic roller of claim 2 , wherein the roller contains at least 5 weight percent less of said magnetic filler and said resin binder as compared with the same sized roller formed from non-foamed said magnetic filler and said resin binder and exhibits substantially equivalent mechanical strength as such a same sized roller.