Hydrocolloid adhesive mass with improved resistance to deterioration of its absorption capacity after being sterilized by radiation
View Patent ↗The present invention relates to novel hydrocolloid adhesive masses consisting of an adhesive mixture based on a low molecular polyisobutylene and a poly(styrene/olefin/styrene) block polymer, and of a cellulose derivative, with which an acrylate polymer with a glass transition temperature below −20° C. is associated for the purpose of increasing the resistance to deterioration of the absorption capacity of said hydrocolloid adhesive mass after radiosterilization. The invention further relates to the use of these novel hydrocolloid adhesive masses for medical, dermatological or cosmetic purposes and particularly for the production of dressings for the treatment of blisters, exudative wounds, burns and superficial, deep, chronic or acute dermo-epidermal lesions.
1. Hydrocolloid adhesive mass for medical purposes, which comprises:
(a) 2 to 15 parts by weight of an acrylate polymer with a glass transition temperature below −20° C.;
(b) 20 to 50 parts by weight of one or more cellulose derivative; and
(c) 32 to 120 parts by weight of an adhesive mixture consisting of one or more low molecular polyisobutylene and one or more poly(styrene/olefin/styrene) block polymer, with which are associated one or more compounds selected from the group consisting of high molecular polyisobutylenes, polybutenes, sticky or “tackifying” resins, butyl rubbers, plasticizers and antioxidants.
2. Hydrocolloid adhesive mass according to claim 1 , wherein the acrylate polymer with a glass transition temperature below −20° C. is a copolymer formed of at least one monomer selected from the group consisting of acrylic acid alkyl esters in which the linear or branched alkyl group of the ester has 1 to 18 carbon atoms, copolymerized with acrylic acid.
3. Hydrocolloid adhesive mass according to claim 1 , wherein the acrylate polymer with a glass transition temperature below −20° C. is a copolymer formed of at least one monomer selected from the group consisting of acrylic acid alkyl esters in which the linear or branched alkyl group of the ester has 4 to 10 carbon atoms, copolymerized with acrylic acid.
4. Hydrocolloid adhesive mass according to claim 1 , wherein the acrylate polymer with a glass transition temperature below −20° C. is a copolymer formed of at least one monomer selected from the group consisting of acrylic acid alkyl esters in which the linear or branched alkyl group of the ester has 4 to 8 carbon atoms, copolymerized with acrylic acid.
5. Hydrocolloid adhesive mass according to claim 2 , wherein the above-mentioned acrylate copolymer is a copolymer formed of at least one monomer selected from the group consisting of n-butyl acrylate, 2-etylhexyl acrylate and isooctyl acrylate, copolymerized with acrylic acid.
6. Hydrocolloid adhesive mass according to claim 2 , wherein the above-mentioned acrylate copolymer is selected from the group consisting of an n-butyl acrylate/acrylic acid copolymer with a glass transition temperature of −39° C. and an n-butyl acrylate/2-ethylhexyl acrylate/acrylic acid copolymer with a glass transition temperature of −31° C.
7. Hydrocolloid adhesive mass according to claim 5 , wherein the above-mentioned acrylate copolymer comprises from 1 to 20% by weight of acrylic acid, expressed relative to the total weight of all the monomers.
8. Hydrocolloid adhesive mass according to claim 1 , wherein the acrylate polymer with a glass transition temperature below −20° C. is a copolymer formed of at least two monomers selected from the group consisting of acrylic acid alkyl esters in which the linear or branched alkyl group of the ester contains 1 to 18 carbon atoms.
9. Hydrocolloid adhesive mass according to claim 1 , wherein the acrylate polymer with a glass transition temperature below −20° C. is a copolymer formed of at least two monomers selected from the group consisting of acrylic acid alkyl esters in which the linear or branched alkyl group of the ester contains 4 to 10 carbon atoms.
10. Hydrocolloid adhesive mass according to claim 1 , wherein the acrylate polymer with a glass transition temperature below −20° C. is a copolymer formed of at least two monomers selected from the group consisting of acrylic acid alkyl esters in which the linear or branched alkyl group of the ester contains 4 to 8 carbon atoms.
11. Hydrocolloid adhesive mass according to claim 1 , wherein the acrylate polymer with a glass transition temperature below −20° C. is a homopolymer whose constituent monomer is selected from the group consisting of acrylic acid alkyl esters in which the alkyl group of the ester is selected from the group consisting of a linear alkyl group containing 2 to 12 carbon atoms, isobutyl, 2-ethylhexyl and isooctyl group.
12. Hydrocolloid adhesive mass according to claim 1 , wherein the acrylate polymer with a glass transition temperature below −20° C. is a homopolymer whose constituent monomer is an n-butyl acrylate homopolymer with a glass transition temperature of 41° C.
13. Hydrocolloid adhesive mass according to claim 1 , which comprises:
(a) 2 to 15 parts by weight of an acrylate copolymer with a glass transition temperature below −20° C.;
(b) 20 to 50 parts by weight of a cellulose derivative;
(c) 10 to 40 parts by weight of a mixture formed of a low molecular polyisobutylene and a poly(styrene/olefin/styrene) block copolymer;
(d) 20 to 50 parts by weight of a tackifying resin;
(e) 2 to 25 parts by weight of a plasticizer; and
(f) 0.1 to 2 parts by weight of at least one antioxidant.
14. Hydrocolloid adhesive mass according to claim 1 , which comprises:
(a) 2 to 15 parts by weight of an acrylate copolymer with a glass transition temperature below −20° C.;
(b) 20 to 50 parts by weight of sodium carboxymethylcellulose;
(c) 10 to 40 parts by weight of a mixture formed from a low molecular weight polyisobutylene and a poly(styrene/styrene/styrene);
(d) 20 to 50 parts by weight of a tackifying resin;
(e) 2 to 25 parts by weight of a plasticizing oil; and
(f) 0to 2 parts by weight of at least one antioxidant.
15. Hydrocolloid adhesive mass according to claim 13 , wherein the above-mentioned plasticizer is a mineral plasticizing oil selected from the group consisting of naphthenic, paraffinic and aromatic compounds.
16. Hydrocolloid adhesive mass according to claim 13 , which comprises:
(a) 2 to 15 parts by weight of an acrylate polymer with a glass transition temperature of −39° C.;
(b) 20 to 50 parts by weight of sodium carboxymethylcellulose;
(c 1 ) 10 to 35 parts by weight of a poly(styrene/olefin/styrene) block copolymer;
(c 2 ) 1 to 20 parts by weight of a low molecular polyisobutylene;
(d) 20 to 50 parts by weight of a tackifying resin;
(e) 2 to 25 parts by weight of a plasticizing oil; and
(f) 0.1 to 2 parts of at least one antioxidant;
wherein the total amount of low molecular weight polyisobutylene and poly(styrene/olefin/styrene) block copolymer is less than 40 parts by weight.
17. Hydrocolloid adhesive mass according to claim 1 , which comprises.
(a) 2 to 15 parts by weight of an acrylate polymer with a glass transition temperature below −20° C.;
(b) 20 to 50 parts by weight of a cellulose derivative;
(c) 5 to 20 parts by weight of a poly(styrene/olefin/styrene) block polymer;
(d) 25 to 50 parts by weight of at least one low molecular polyisobutylene;
(e) 2 to 20 parts by weight of a polybutene; and
(f) 0.1 to 2 parts by weight of at least one antioxidant.
18. Hydrocolloid adhesive mass according to claim 1 , which comprises:
(a) 2 to 15 parts by weight of an acrylate copolymer with a glass transition temperature below −20° C.;
(b) 20 to 50 parts by weight of sodium carboxymethylcellulose;
(c) 10 to 40 parts by weight of a mixture formed from a low molecular weight polyisobutylene and a poly(styrene/isoprene/styrene);
(d) 20 to 50 parts by weight of a tackifying resin;
(e) 2 to 20 parts by weight of a polybutene; and
(f) 0.1 to 2 parts by weight of at least one antioxidant.
19. Hydrocolloid adhesive mass according to claim 1 , wherein the above-mentioned block copolymer is a poly(styrene/isoprene/styrene) with a styrene content of between 14 and 52% by weight, based on the weight of said copolymer.
20. Hydrocolloid adhesive mass according to claim 1 , wherein the cellulose derivative is an alkali metal salt of carboxymethyl cellulose.
21. A dressing for the treatment of blisters, superficial, deep, chronic or acute dermo-epidermal lesions, exudative or burns, said dressing being formed of a support onto which an hydrocolloid adhesive mass according to claim 1 is coated.
22. A dressing for the treatment of blisters, superficial, deep, chronic or acute dermo-epidermal lesions, exudative or burns, said dressing being formed of a support onto which an hydrocolloid adhesive mass according to claim 17 is coated.
23. A dressing for the treatment of blisters, superficial, deep, chronic or acute dermo-epidermal lesions, exudative or burns, said dressing being formed of a support onto which an hydrocolloid adhesive mass according to claim 8 is coated.
24. A dressing for the treatment of blisters, superficial, deep, chronic or acute dermo-epidermal lesions, exudative or burns, said dressing being formed of a support onto which an hydrocolloid adhesive mass according to claim 13 is coated.
25. A dressing for the treatment of blisters, superficial, deep, chronic or acute dermo-epidermal lesions, exudative or burns, said dressing being formed of a support onto which an hydrocolloid adhesive mass according to claim 16 is coated.