Method of making oleochemical oil-based polyols
View Patent ↗A method of making oleochemical oil-based polyols by mixing an acid activated or acid leached clay, an epoxidized oleochemical oil, alcohol, and acid activated or acid leached clay so the epoxidized oleochemical oil reacts with said alcohol to form a oleochemical oil-based polyol, filtering out said clay, stripping off any excess alcohol, and recovering the oleochemical oil-based polyol.
1. A method of making oleochemical oil-based polyols comprising:
A. Mixing an acid activated or acid leached clay;
B. Adding an epoxidized oleochemical oil, and an alcohol, whereby said epoxidized oleochemical oil reacts at a temperature between 60° C. and 70° C. with said alcohol to form a oleochemical oil-based polyol;
C. Filtering out said clay;
D. Stripping off any excess alcohol; and
E. Recovering the oleochemical oil-based polyol.
2. The method of claim 1 wherein said clay is present in an amount of about 1 to about 10% by weight, based upon the weight of the oleochemical oil.
3. The method of claim 1 wherein said clay is present in an amount of about 2 to about 10% by weight, based upon the weight of the oleochemical oil.
4. The method of claim 1 wherein said clay is present in an amount of about 5% by weight, based upon the weight of the oleochemical oil.
5. The method of claim 1 wherein after said clay is filtered out, it is recycled and reused is said process.
6. The method of claim 1 wherein said alcohol is methanol.
7. The method of claim 1 wherein said alcohol is selected from the group consisting of methanol, ethanol, propanol, and isopropanol.
8. The method of claim 1 wherein the alcohol is present in an amount of from about 50% to about 150% by weight based upon the weight of the epoxidized oleochemical oil.
9. The method of claim 1 wherein the epoxidized oleochemical oil has an epoxide content of about 6.0% to about 7.0%.
10. The method of claim 1 wherein the oleochemical oil-base polyol has a hydroxyl content of about 110 mg KOH/g of polyol to about 200 mg KOH/g of polyol.
11. The method of claim 1 wherein the oleochemical oil-base polyol has a hydroxyl content of about 140 mg KOH/g of polyol to about 180 mg KOH/g of polyol.