Positive active material for non-aqueous electrolyte secondary battery and non-aqueous electrolyte secondary battery comprising same
View Patent ↗A positive active material for a non-aqueous electrolyte secondary battery includes a lithium-nickel composite oxide represented by the compositional formula Li a Ni 1−b−c CO b Mn c O 2 (a≦1.09, 0.05≦b≦0.35, 0.15≦c≦0.35, and 0.25≦b+c≦0.55). By X-ray diffractometry with a CuKα ray, the lithium-nickel composite oxide exhibits an intensity ratio R ((I 012 +I 006 )/I 101 ) of not greater than 0.50, wherein R is the ratio of the sum of the diffraction peak intensity I 012 on the 012 plane and the diffraction peak intensity I 006 on the 006 plane to the diffraction peak intensity I 101 on the 101 plane. The crystallinity of the positive active material of the compositional formula Li a Ni 1−b−c Co b Mn c O 2 can be kept high and it is possible to secure good capacity density and cycle life performance.
1. A positive active material for a non-aqueous electrolyte secondary battery, comprising a lithium-nickel composite oxide represented by the compositional formula Li a Ni 1−b−c Co b Mn c O 2 (in which the suffix a is not greater than 1.09, the suffix b is from not smaller than 0.05 to not greater than 0.25, and the suffix c is from not smaller than 0.2 to not greater than 0.35, and the sum of b and c is from not smaller than 0.25 to not greater than 0.55) having a hexagonal structure, wherein
when subjected to X-ray diffractometry with a CuKα ray, said lithium-nickel composite oxide exhibits an intensity ratio R ((I 012 +I 006 )I 101 ) of not greater than 0.50 and not less than 0.422, R being the ratio of the sum of the diffraction peak intensity I 012 on the 012 plane and the diffraction peak intensity I 006 on the 006 plane to the diffraction peak intensity I 101 on the 101 plane, said positive active material has a mean particle diameter D 50 of from 4 μm to 25 μm and a BET specific surface area of from 0.2 to 1.5 m 2 /g.
2. A non-aqueous electrolyte secondary battery comprising a positive electrode comprising said positive active material defined in claim 1 , a negative electrode comprising a carbon-based material, and a non-aqueous electrolyte.
3. The positive active material for the non-aqueous electrolyte secondary battery according to claim 1 , wherein said positive active material has a mean particle diameter D 50 of from 10.1 to 25 μm.
4. The positive active material for the non-aqueous electrolyte secondary battery according to claim 3 , wherein said positive active material has a BET specific surface area of from 0.37 to 0.69 m 2 /g.
5. The positive active material for the non-aqueous electrolyte secondary battery according to claim 3 , wherein said positive active material has a mean particle diameter D 50 of from 11.5 to 25 μm.
6. The positive active material for the non-aqueous electrolyte secondary battery according to claim 5 , wherein said positive material has a BET specific surface area of from 0.37 to 0.58 m 2 /g.
7. The positive active material for the non-aqueous electrolyte secondary battery according to claim 1 , wherein said positive active material has a BET specific surface area of from 0.37 to 0.69 m 2 /g.
8. The positive active material for the non-aqueous electrolyte secondary battery according to claim 7 , wherein said positive active material has a BET specific surface area of from 0.37 to 0.58 m 2 /g.
9. A positive active material for a non-aqueous electrolyte secondary battery, comprising a lithium-nickel composite oxide represented by the compositional formula Li a Ni 1−b−c−d Co b Mn c M d O 2 (in which M is at least one metal element selected from the group consisting of Al, Ti, W, Nb and Mo, the suffix a is not greater than 1.09, the suffix b is from not smaller than 0.05 to not greater than 0.35, the suffix c is from not smaller than 0.15 to not greater than 0.35, and the suffix d is from greater than 0 to not greater than 0.35, and the sum of b, c and d is from not smaller than 0.25 to not greater than 0.55) having a hexagonal structure, wherein
when subjected to X-ray diffractometry with a CuKα ray, said lithium-nickel composite oxide exhibits an intensity ratio R ((I 012 +I 006 )/I 101 ) of not greater than 0.50, R being the ratio of the sum of the diffraction peak intensity I 012 on the 012 plane and the diffraction peak intensity I 006 on the 006 plane to the diffraction peak intensity I 101 on the 101 plane.
10. The positive active material for the non-aqueous electrolyte secondary battery according to claim 9 , wherein said positive active material has a mean particle diameter D 50 of from 4 μm to 25 μm and a BET specific surface area of from 0.2 to 1.5 m 2 /g.
11. A non-aqueous electrolyte secondary battery comprising a positive electrode comprising said positive active material defined in any one of claims 9 to 10 , a negative electrode comprising a carbon-based material, and a non-aqueous electrolyte.