Activated carbon for use in electric double layer capacitors
View Patent ↗Activated carbon adapted for electric double layer capacitors is provided, which capacitors can give a large power density per unit volume and which capacitors, even when charge-and-discharge cycle is repeated under a large current or a constant voltage is continuously applied for a long time, undergo less decrease in output density. That is, the present invention relates to the activated carbon manufactured by carbonization of coconut shell, which has a BET specific surface area of 2000 m 2 /g to 2500 m 2 /g, an average pore diameter of 1.95 nm (19.5 Å) to 2.20 nm (22 Å) and a pore volume of pores having a pore diameter calculated according to a Cranston-Inkley method of 5.0 nm (50 Å) to 30.0 nm (300 Å), of 0.05 cm 3 /g to 0.15 cm 3 /g.
1. An activated carbon suitable for use in electric double layer capacitors,
said activated carbon being produced by carbonization of a carbonaceous material consisting essentially of coconut shell, wherein said activated carbon is produced by a process comprising:
pulverizing a coconut shell;
carbonizing said coconut shell in an inert atmosphere to produce a coconut shell char; and
heat-treating said coconut shell char at a temperature ranging from 900° C. to 1,100° C. in a steam gas atmosphere containing an inert gas selected from the group consisting of nitrogen, argon, and a combustion exhaust gas, wherein the content of steam in said steam gas atmosphere ranges from 30% by volume to 100% by volume,
wherein said activated carbon has a BET specific surface area of 2000 m 2 /g to 2500 m 2 /g, and an average pore diameter of 1.95 nm (19.5 Å) to 2.20 nm (22 Å),
wherein the pore volume of pores having a pore diameter, as calculated according to a Cranston-Inkley method, of 5.0 nm (50 Å) to 30.0 nm (300 Å) is 0.05 cm 3 /g to 0.15 cm 3 /g,
wherein the amount of oxygen contained per g of said activated carbon is 1.8 mg to 8.1 mg, and
wherein said activated carbon exhibits a spontaneous potential versus a lithium electrode of 2.85 V to 3.03 V in a non-aqueous electrolytic solution.
2. The activated carbon for electric double layer capacitors as claimed in claim 1 , wherein the BET specific surface area is 2000 m 2 /g to 2400 m 2 /g.
3. The activated carbon for electric double layer capacitors as claimed in claim 1 , wherein the BET specific surface area is 2050 m 2 /g to 2250 m 2 /g.
4. The activated carbon for electric double layer capacitors as claimed in claim 1 , wherein the pore volume of pores having a pore diameter, calculated according to a Cranston-Inkley method, of 5.0 nm (50 Å) to 30.0 nm (300 Å) is 0.07 cm 3 /g to 0.13 cm 3 /g.
5. The activated carbon for electric double layer capacitors as claimed in claim 1 , wherein the pore volume of pores having a pore diameter, calculated according to a Cranston-Inkley method, of 5.0 nm (50 Å) to 30.0 nm (300 Å) is 0.08 cm 3 /g to 0.12 cm 3 /g.
6. The activated carbon for electric double layer capacitors as claimed in claim 1 , wherein the average pore diameter is 2.00 nm to 2.15 nm.
7. The activated carbon for electric double layer capacitors as claimed in claim 1 , wherein the average pore diameter is 2.02 nm to 2.15 nm.
8. The activated carbon for electric double layer capacitors as claimed in claim 1 , wherein an oxygen content per g. of the activated carbon is 2.5 mg to 6.1 mg.
9. The activated carbon for electric double layer capacitors as claimed in claim 8 , wherein said pore volume thereof is from 0.08 cm 3 /g to 0.12 cm 3 /g.
10. The activated carbon for electric double layer capacitors as claimed in claim 1 , having a specific surface area of from 2024–2351 m 2 /g.
11. The activated carbon for electric double layer capacitors as claimed in claim 1 , having a total pore volume of 1.00–1.20 cm 3 /g.
12. The activated carbon for electric double layer capacitors as claimed in claim 1 , having an average pore diameter of 2.00–2.03 nm.
13. The activated carbon for electric double layer capacitors as claimed in claim 1 , having a pore volume of pores having a 5.0–30.0 nm diameter of from 0.075–0.130 cm 3 /g.
14. The activated carbon for electric double layer capacitors as claimed in claim 1 , having a spontaneous potential of 2.99–3.02.
15. An electric double layer capacitor, comprising the activated carbon of claim 1 .