Non-gelatin capsule shell formulation
View Patent ↗A film-forming hydrocolloid composition comprising kappa carrageenan, iota carrageenan, a bulking agent, plasticizer and water is described. The ratio of bulking agent to total carrageenan is from about 1:1 to 20:1. Kappa carrageenan is present in an amount of less than or equal to 50% by weight of total carrageenan present. To form the composition, all dry materials are mixed and added to a heated mixture of all liquid materials. The final mixture is heated until a composition free of particulate materials is formed. The formed composition can be cast or extruded into ribbons, films, sheets, tubes or the like, for encapsulating wet or dry materials including medicinal dosage forms, nutritional supplements, cosmetics, bath oils and gels, and paint balls.
1. A method for preparing a film-forming composition comprising:
a) mixing iota carrageenan in an amount of from about 1% to about 15% by weight of the composition, kappa carrageenan in an amount less than 100% by weight of the iota carrageenan and a bulking agent in a ratio of bulking agent to total carrageenan of from about 1:1 to about 20:1 to form a dry mixture;
b) mixing a plasticizer and water to form a liquid mixture;
c) heating the liquid mixture to a temperature of from about 75° C. to about 90° C.;
d) adding the dry mixture to the heated mixture with stirring to form a dispersion; and
e) heating the dispersion with stirring to a temperature of from about 85° C. to about 95° C. to form a uniform dispersion.
2. The method of claim 1 , further comprising casting a ribbon with the uniform dispersion.
3. The method of claim 2 , further comprising feeding the ribbon into a rotary die encapsulation machine.
4. The method of claim 2 , further comprising drying the ribbon to a moisture content of from abut 5% to about 20%.
5. The method of claim 4 , further comprising feeding the dried ribbon into a rotary die encapsulation machine.
6. The method of claim 1 , further comprising extruding the uniform dispersion.
7. The method of claim 6 , wherein the extruded uniform dispersion is in the shape of a film, ribbon, sheet or tube.
8. The method of claim 7 , further comprising feeding the extruded uniform dispersion into a rotary die encapsulation machine.