Method of manufacture of polyester molding compositions and articles produced therefrom
View Patent ↗A thermoplastic molding composition comprises a resin composition having 50 to about 90 weight percent of a polyester, about 8 to about 48 weight percent of a polyetherimide, about 2 to about 25 weight percent of a high rubber graft impact modifier, each based on the total resin composition, and up to about 15 weight percent of a particulate filler. A making the composition comprises pre-melt compounding a polyester, a polyetherimide, and a high rubber graft impact modifier to form a pre-compounded blend, wherein the pre-compounded blend has a Tg of greater than or equal to about 110° C.; and dry-blending a crystallized polyester with the pre-compounded blend to form the molding composition. Such molding compositions are particularly useful in blow-molding container for liquids such as beer.
1. A method for the manufacture of a molding composition, comprising
pre-melt compounding a blend polyester portion, a polyetherimide, and a high rubber graft impact modifier to form a pre-compounded blend, wherein the pre-compounded blend has a Tg greater than or equal to about 100° C.; and
dry-blending a crystallized polyester portion with the pre-compounded blend to form a molding composition comprising
50 to about 90 wt % of total polyester, said total polyester including both the blend polyester portion and the crystallized polyester portion;
about 10 to about 48 wt % of the polyetherimide; and
about 2 to about 25 wt % of the high rubber graft impact modifier, each based on the total combined weight of the total polyester, the polyetherimide, and the impact modifier.
2. The method of claim 1 , further comprising drying the pre-compounded blend at a temperature less than or equal to the Tg of the pre-compounded blend.
3. The method of claim 1 , further comprising drying the molding composition at a temperature less then or equal to the Tg of the pre-compounded blend.
4. The method of claim 1 , wherein the Tg of the pre-compounded blend is greather than about 120° C.
5. The method of claim 1 , wherein the polyetherimide comprises greater than or equal to about 30 wt % of the pre-compounded blend, based on the total combined weight of the blend polyester portion, the polyetherimide, and the impact modifier in the pre-compounded blend.
6. The method of claim 1 , wherein the polyetherimide comprises greater than or equal to about 40 wt % of the pre-compounded blend, based on the total combined weight of the blend polyester portion, the polyetherimide, and the impact modifier in the pre-compounded blend.
7. A method of molding an article, comprising
dry blending a crystallized polyester portion with a pre-compounded blend having a Tg of greater than or equal to about 100° C., said pre-compounded blend comprising a blend polyester portion, a polyetherimide, and a high rubber graft impact modifier, to form a molding composition comprising 50 to about 90 wt % of total polyester, said total polyester including both the blend polyester portion and the crystallized polyester portion; about 10 to about 48 wt % of the polyetherimide; and about 2 to about 25 wt % of the high rubber graft impact modifier, each based on the total combined weight of the total polyester, the polyetherimide, and the impact modifier; and
molding the molding composition to form an article having a Tg lower than the Tg of the pre-compounded blend.
8. The method of claim 7 , further comprising drying the pre-compounded blend at a temperature less than or equal to the Tg of the pre-compounded blend.
9. The method of claim 7 , further comprising drying the molding composition at a temperature less than or equal to the Tg of the pre-compounded blend.
10. The method of claim 7 , wherein the Tg of the pre-compounded blend is greather than about 120° C.
11. The method of claim 7 , wherein the polyetherimide comprises greater than or equal to about 30 wt % of the pre-compounded blend, based on the total combined weight of the blend polyester portion, the polyetherimide, and the impact modifier in the pre-compounded blend.
12. The method of claim 7 , wherein the polyetherimide comprises greater than or equal to about 40 wt % of the pre-compounded blend, based on the total combined weight of the blend polyester portion, the polyetherimide, and the impact modifier in the pre-compounded blend.