Sorbents for desulfurization
View Patent ↗Attrition resistant, sorbent compositions for the removal of elemental sulfur and sulfur compounds, such as hydrogen sulfide and organic sulfides, from cracked-gasoline and diesel fuels are prepared by the impregnation of a sorbent support comprising zinc oxide, expanded perlite, and alumina with a promoter such as nickel, nickel oxide or a precursor of nickel oxide followed by reduction of the valence of the promoter metal in the resulting promoter metal sorbent support composition.
1. A sorbent composition comprising:
(a) zinc oxide; and
(b) a promoter metal-zinc aluminate substitutional solid solution characterized by the formula M Z Zn (1-Z) Al 2 O 4
wherein M is a promoter metal selected from the group consisting of nickel, cobalt, iron, manganese, copper, zinc, molybdenum, tungsten, silver, antimony, and vanadium and Z is a numerical value in the range of from 0.01 to 0.99.
2. A sorbent composition in accordance with claim 1 wherein said promoter metal is nickel.
3. A sorbent composition in accordance with claim 1 further comprising a substitutional solid metal solution of said promoter metal and zinc.
4. A sorbent composition in accordance with claim 3 wherein said promoter metal is nickel.
5. A sorbent composition in accordance with claim 1 further comprising expanded perlite.
6. A sorbent composition in accordance with claim 5 wherein said zinc oxide is present in an amount in the range of about 10 to about 90 weight percent and said expanded perlite is present in an amount in the range of about 10 to about 40 weight percent.
7. A sorbent composition in accordance with claim 6 wherein said promoter metal is nickel.
8. An oxidized sorbent composition comprising:
(a) zinc oxide; and
(b) a substitutional solid metal oxide solution wherein said substitutional solid metal oxide solution is characterized by the formula M x Zn y O, wherein M is a promoter metal and X and Y are each numerical values in the range of from 0.01 to 0.99.
9. An oxidized sorbent composition in accordance with claim 8 wherein X is in the range of about 0.50 to about 0.90 and Z is in the range of about 0.10 and 0.50.
10. An oxidized sorbent composition in accordance with claim 9 wherein M is a metal selected from the group consisting of nickel, cobalt, iron, manganese, copper, zinc, molybdenum, tungsten, silver, antimony, and vanadium.
11. An oxidized sorbent composition in accordance with claim 8 wherein X is in the range of about 0.60 and about 0.80 and Y is equal to about (1-X).
12. An oxidized sorbent composition in accordance with claim 11 wherein M is nickel.
13. An oxidized sorbent composition in accordance with claim 8 wherein said zinc oxide is present in an amount in the range of about 10 to about 90 weight percent and said substitutional solid metal oxide solution is present in an amount in the range of about 5 to about 70 weight percent.
14. An oxidized sorbent composition in accordance with claim 8 further comprising a promoter metal-zinc aluminate substitutional solid solution characterized by the formula M Z Zn (1-Z) Al 2 O 4 , wherein M is said promoter metal and Z is a numerical value in the range of from 0.01 to 0.99.
15. An oxidized sorbent composition in accordance with claim 14 wherein M is a metal selected from the group consisting of nickel, cobalt, iron, manganese, copper, zinc, molybdenum, tungsten, silver, antimony, and vanadium.
16. An oxidized sorbent composition in accordance with claim 14 wherein M is nickel.
17. An oxidized sorbent composition in accordance with claim 14 wherein said zinc oxide is present in an amount in the range of about 10 to about 90 weight percent, said substitutional solid metal oxide solution is present in an amount in the range of about 5 to about 70 weight percent, and said promoter metal-zinc aluminate substitutional solid solution is present in an amount in the range of about 2 to about 50 weight percent.
18. An oxidized sorbent composition in accordance with claim 8 further comprising expanded perlite.
19. An oxidized sorbent composition in accordance with claim 13 further comprising expanded perlite in an amount in the range of about 10 to about 20 weight percent.
20. An oxidized sorbent composition in accordance with claim 14 further comprising expanded perlite.
21. An oxidized sorbent composition in accordance with claim 17 further comprising expanded perlite in an amount in the range of about 10 to about 20 weight percent.
22. A reduced sorbent composition comprising:
(a) zinc oxide; and
(b) a substitutional solid metal solution wherein said substitutional solid metal solution is characterized by the formula M A Zn B , wherein M is a promoter metal and A and B are each numerical values in the range of 0.01 to 0.99.
23. A reduced sorbent composition in accordance with claim 22 wherein A is in the range of from about 0.50 to about 0.97 and B is in the range of from about 0.03 to about 0.50.
24. A reduced sorbent composition in accordance with claim 23 wherein M is a metal selected from the group consisting of nickel, cobalt, iron, manganese, copper, zinc, molybdenum, tungsten, silver, antimony, and vanadium.
25. A reduced sorbent composition in accordance with claim 22 wherein A is in the range of from about 0.80 to about 0.95 and B is equal to about (1-A).
26. A reduced sorbent composition in accordance with claim 25 wherein M is nickel.
27. A reduced sorbent composition in accordance with claim 22 wherein zinc oxide is present in an amount in the range of about 10 to about 90 weight percent and said substitutional solid metal solution is present in an amount in the range of about 5 to about 80 weight percent.
28. A reduced sorbent composition in accordance with claim 22 further comprising a promoter metal-zinc aluminate substitutional solid solution characterized by the formula M Z Zn (1-Z) Al 2 O 4 , wherein M is said promoter metal and Z is a numerical value in the range of from 0.01 to 0.99.
29. A reduced sorbent composition in accordance with claim 28 wherein M is a metal selected from the group consisting of nickel, cobalt, iron, manganese, copper, zinc, molybdenum, tungsten, silver, antimony, and vanadium.
30. A reduced sorbent composition in accordance with claim 28 wherein M is nickel.
31. A reduced sorbent composition in accordance with claim 28 wherein said zinc oxide is present in an amount in the range of about 10 to about 90 weight percent, said substitutional solid metal solution is present in an amount in the range of about 5 to about 80 weight percent, and said promoter metal-zinc aluminate substitutional solid solution is present in an amount in the range of from about 2 to about 50 weight percent.
32. A reduced sorbent composition in accordance with claim 22 further comprising expanded perlite.
33. A reduced sorbent composition in accordance with claim 27 further comprising expanded perlite in an amount in the range of from about 2 to about 50 weight percent.
34. A reduced sorbent composition in accordance with claim 28 further comprising expanded perlite.
35. A reduced sorbent composition in accordance with claim 31 further comprising expanded perlite in an amount in the range of from about 2 to about 50 weight percent.