Thermoformable packaging film
View Patent ↗Disclosed are multi-layer thermoformable film constructions. At least one layer of the multi-layer construction is a polymer blend of: (a) 40–95% by weight of an ethylene-acrylic acid or methacrylic acid copolymer or of an ethylene-acrylic acid or methacrylic acid-alkyl acrylate or alkyl methacrylate copolymer with 30–70% of the acid groups of the acrylic acid or methacrylic acid of either copolymer neutralized with metal ions, and (b) 5–60% by weight of a metallocene catalyzed linear polyethylene.
1. A thermoformable film comprising a composite structure comprising at least three layers firmly adhered to one another, a top and bottom layer and an inner layer;
wherein the top and bottom layer of the composite structure comprise a film layer of ethylene-vinyl acetate copolymer consisting essentially of 1 to 25% by weight, based on the weight of the copolymer, of a polymerized vinyl acetate and 75 to 99% by weight, based on the weight of the copolymer, of polymerized ethylene and the inner layer of the composite structure comprises a film of a polymer blend consisting essentially of
(a) 40 to 95% by weight, based on the weight of the polymer blend, of an ethylene based copolymer having a melt index of 0.5 to 200 g/10 minutes determined according to ASTM D 1238 Condition E, said ethylene based copolymer consisting essentially of repeating polymerized units of
(1) 75 to 93% by weight, based on the weight of the copolymer, of ethylene; and
(2) 7 to 25% by weight, based on the weight of the copolymer, of acrylic acid or methacrylic acid; and
wherein 30 to 70% of the acid groups of the acrylic acid or methacrylic acid of the ethylene based copolymer are neutralized with metal ion selected from the group consisting of zinc, magnesium, sodium and lithium; and
(b) 5 to 60% by weight, based on the weight of the polymer blend, of a metallocene catalyzed linear polyethylene.
2. The thermoformable film of claim 1 , wherein the inner layer consists essentially of a polymer blend of 65 to 85% by weight of the ethylene based copolymer and 15 to 35% by weight of the metallocene catalyzed linear polyethylene, based on the weight of the polymer blend.
3. A thermoformable film comprising a composite structure comprising at least three layers firmly adhered to one another, a top and bottom layer and an inner layer;
wherein the top and bottom layer of the composite structure comprise a film layer of ethylene-vinyl acetate copolymer consisting essentially of 1 to 25% by weight, based on the weight of the copolymer, of a polymerized vinyl acetate and 75 to 99% by weight, based on the weight of the copolymer, of polymerized ethylene and the inner layer of the composite structure comprises a film of a polymer blend consisting essentially of
(a) 40 to 95% by weight, based on the weight of the polymer blend, of an ethylene based copolymer having a melt index of 0.5 to 200 g/10 minutes determined according to ASTM D 1238 Condition E, said ethylene based copolymer consisting essentially of repeating polymerized units of
(1) at least 50% by weight based on the weight of the copolymer, of ethylene,
(2) 7 to 25% by weight, based on the weight of the copolymer, of acrylic acid or methacrylic acid; and
(3) 1 to 30% by weight, based on the weight of the copolymer, of an alkyl acrylate or an alkyl methacrylate,
wherein 30 to 70% of the acid groups of the acrylic acid or methacrylic acid of the ethylene based copolymer are neutralized with metal ion selected from the group consisting of zinc, magnesium, sodium and lithium; and
(b) 6 to 60% by weight, based on the weight of the polymer blend, of a metallocene catalyzed linear polyethylene.
4. The thermoformable film of claim 3 , wherein the inner layer consists essentially of a polymer blend of 65 to 85% by weight of the ethylene based copolymer and 15 to 35% by weight of the metallocene catalyzed linear polyethylene, based on the weight of the polymer blend.
5. A thermoformed package comprising a thermoformable film comprising a composite structure comprising at least three layers firmly adhered to one another, a top and bottom layer and an inner layer;
wherein the top and bottom layer of the composite structure comprise a film layer of ethylene-vinyl acetate copolymer consisting essentially of 1 to 25% by weight, based on the weight of the copolymer, of a polymerized vinyl acetate and 75 to 99% by weight, based on the weight of the copolymer, of polymerized ethylene and the inner layer of the composite structure comprises a film of a polymer blend consisting essentially of
(a) 40 to 95% by weight, based on the weight of the polymer blend, of an ethylene based copolymer having a melt index of 0.5 to 200 g/10 minutes determined according to ASTM D 1238 Condition E, said ethylene based copolymer consisting essentially of repeating polymerized units of
(1) 75 to 93% by weight, based on the weight of the copolymer, of ethylene; and
(2) 7 to 25% by weight, based on the weight of the copolymer, of acrylic acid or methacrylic acid; and
wherein 30 to 70% of the acid groups of the acrylic acid or methacrylic acid of the ethylene based copolymer are neutralized with metal ion selected from the group consisting of zinc, magnesium, sodium and lithium; and
(b) 5 to 60% by weight, based on the weight of the polymer blend, of a metallocene catalyzed linear polyethylene,
thermoformed into a shaped structure for holding an object and having a cover positioned on the thermoformed shaped structure and firmly adhered to the film.
6. The thermoformed package of claim 5 in which the cover is a non-woven polyolefin web.
7. A thermoformed package comprising a thermoformable film comprising a composite structure comprising at least three layers firmly adhered to one another, a top and bottom layer and an inner layer;
wherein the top and bottom layer of the composite structure comprise a film layer of ethylene-vinyl acetate copolymer consisting essentially of 1 to 25% by weight, based on the weight of the copolymer, of a polymerized vinyl acetate and 75 to 99% by weight, based on the weight of the copolymer, of polymerized ethylene and the inner layer of the composite structure comprises a film of a polymer blend consisting essentially of
(a) 40 to 95% by weight, based on the weight of the polymer blend, of an ethylene based copolymer having a melt index of 0.5 to 200 g/10 minutes determined according to ASTM D 1238 Condition E, said ethylene based copolymer consisting essentially of repeating polymerized units of
(1) at least 50% by weight, based on the weight of the copolymer, of ethylene,
(2) 7 to 25% by weight, based on the weight of the copolymer, of acrylic acid or methacrylic acid; and
(3) 1 to 30% by weight, based on the weight of the copolymer, of an alkyl acrylate or an alkyl methacrylate,
wherein 30 to 70% of the acid groups of the acrylic acid or methacrylic acid of the ethylene based copolymer are neutralized with metal ion selected from the group consisting of zinc, magnesium, sodium and lithium; and
(b) 5 to 60% by weight, based on the weight of the polymer blend, of a metallocene catalyzed linear polyethylene,
thermoformed into a shaped structure for holding an object and having a cover positioned on the thermoformed shaped structure and firmly adhered to the film.
8. The thermoformed package of claim 7 in which the cover is a non-woven polyolefin web.