Method for devulcanizing rubber with an amine
View Patent ↗The invention relates to a method for devulcanizing a sulphur-cured rubber, which rubber contains a network of a polymer, which polymer has a main chain of carbon atoms, in which for the vulcanization per 40 carbon-carbon bonds in the main chain a maximum of 1 unsaturated carbon-carbon bond occurs, by heating the rubber in the presence of a devulcanizing agent. The devulcanizing agent is an amine compound.
1. Method for devulcanizing a sulphur-cured rubber, which rubber contains a network of a polymer, which polymer has a main chain of carbon atoms, in which for the vulcanization per 40 carbon-carbon bonds in the main chain a maximum of 1 unsaturated carbon-carbon bond occurs, said process comprising heating the rubber in the presence of a devulcanizing agent wherein the devulcanizing agent consists of an amine compound selected from the group consisting of octylamine, hexadecylamine, dioctylamine, trioctylamine, benzylamine and 4-piperidinopiperidine.
2. Method according to claim 1 , wherein the quantity of devulcanizing agent is 0.5-10 weight % in respect of the quantity of rubber.
3. Method according to claim 2 , wherein the quantity of devulcanizing agent is 1-6 weight % in respect of the quantity of rubber.
4. Method according to claim 1 , wherein the rubber contains a polymer with a main chain in which per 200 carbon-carbon bonds in the main chain a maximum of 1 unsaturated carbon-carbon bond occurs.
5. Method according to claim 4 , wherein the rubber contains a polymer with a main chain in which per 1000 carbon-carbon bonds in the main chain a maximum of 1 unsaturated carbon-carbon bond occurs.
6. Method according to claim 1 , wherein the rubber is a polymer of ethylene, an α-olefin and at least one non-conjugated diene monomer.
7. Method according to claim 6 , wherein the rubber contains an EPDM polymer.
8. Method according to claim 7 , wherein the third monomer in the EPDM polymer is 5-ethylidene-2-norbornene, vinylnorbornene, dicyclopentadiene, methylnorbornene or 1,4 hexadiene.
9. Method according to claim 1 , wherein the sulphur-cured rubber is heated during devulcanization to a temperature between 200-350° C.
10. Method according to claim 8 , wherein the sulphur-cured rubber is heated during devulcanization to a temperature between 250-350° C.
11. Method for devulcanizing a sulphur-cured rubber, which rubber contains a network of a polymer, which polymer has a main chain of carbon atoms, in which for the vulcanization per 40 carbon-carbon bonds in the main chain a maximum of 1 unsaturated carbon-carbon bond occurs, said process comprising heating the rubber in the presence of a devulcanizing agent wherein the devulcanizing agent is an amine compound and wherein devulcanizing the sulphur-cured rubber is carried out at a pressure between 5-10 MPa.
12. Method according to claim 1 , wherein devulcanizing the sulphur-cured rubber is carried out in an atmosphere from which the oxygen has been removed.
13. Method according to claim 11 wherein the amine compound is octylamine, hexadecylamine, dioctylamine, trioctylamine, benzylamine or 4-piperidinopiperidine.