Process for forming layered coated film, and layered coated film
View Patent ↗Disclosed is a three coat one bake coating process for forming an intermediate coated film, a base coated film and a clear coated film on an electrodeposition coated film. The electrodeposition coating composition is a lead-free cationic electrodeposition coating composition which has a volatile organic content of 1% by weight or less, a metal ion content of 500 ppm or less, a neutralizing acid amount of 10 to 30 mg equivalent based on 100 g of binder resin solid content. The intermediate coating composition and/or the base coated composition comprises a specific amount of a nonaqueous dispersion resin as a resin component. In the coating process, a baking step is omitted from the conventional intermediate coating process, or from the conventional base coating process.
1. A process for forming a layered coated film comprising: a step I in which an electrodeposition coated film is formed on a substrate to be coated by an electrodeposition coating process with using a cationic electrodeposition coating composition, and the electrodeposition coated film is heated to form a cured electrodeposition coated film; a step II in which an intermediate coating composition is applied to the cured electrodeposition coated film to form an uncured intermediate coated film; a step III in which a base coating composition is applied to the uncured intermediate coated film to form an uncured base coated film; a step IV in which a clear coating composition is applied to the uncured base coated film to form an uncured clear coated film; and a step V in which the uncured intermediate coated film, base coated film, and clear coated film are simultaneously heated and cured; wherein
the cationic electrodeposition coating composition is a lead-free cationic electrodeposition coating composition which comprises an aqueous medium, a binder resin composed of a cationic epoxy resin and a blocked isocyanate curing agent dispersed or dissolved in the aqueous medium, a neutralizing acid in order to neutralize the cationic epoxy resin, an organic solvent, and a metal catalyst, and which has a volatile organic content of 1% by weight or less, a metal ion content of 500 ppm or less, a neutralizing acid amount of 10 to 30 mg equivalent based on 100 g of binder resin solid content, and
the intermediate coating composition comprises a resin component composed of 10 to 70% by weight solid based on total resin solid of a hydroxyl group containing resin (a), 10 to 70% by weight of a curing agent reactable with hydroxyl group (b), 18 to 50% by weight of a nonaqueous dispersion resin (c), with the proviso (a)+(b)+(c)=100%, and a pigment component.
2. The process for forming a layered coated film according to claim 1 , wherein the metal ion of the lead-free cationic electrodeposition coating composition is one or more selected from the group consisting of cerium ion, bismuth ion, copper ion, zinc ion, molybdenum ion, and aluminium ion.
3. The process for forming a layered coated film according to claim 1 , wherein the neutralizing acid of the lead-free cationic electrodeposition coating composition is one or more selected from the group consisting of acetic acid, lactic acid, formic acid, and sulfamic acid.
4. The process for forming a layered coated film according to claim 1 , wherein the lead-free cationic electrodeposition coating composition further comprises a pigment in a ratio of 1/9 or less by weight based on a resin solid contained in the coating composition.
5. The process for forming a layered coated film according to claim 1 , wherein the intermediate coating composition has a volume shrinkage ratio of not more than 45% in the case of being heated at 140° C. for 30 minutes.
6. The process for forming a layered coated film according to claim 1 , wherein the intermediate coating composition comprises 10 to 70% by weight based on solid in the coating composition of a pigment.
7. The process for forming a layered coated film according to claim 1 , wherein the intermediate coating composition has a nonvolatile solid content of 40 to 70% by weight.
8. A process for forming a layered coated film comprising: a step I in which an electrodeposition coated film is formed on a substrate to be coated by an electrodeposition coating process with using a cationic electrodeposition coating composition, and the electrodeposition coated film is heated to form a cured electrodeposition coated film; a step II in which an intermediate coating composition is applied to the cured electrodeposition coated film to form an uncured intermediate coated film; a step III in which a base coating composition is applied to the uncured intermediate coated film to form an uncured base coated film; a step IV in which a clear coating composition is applied to the uncured base coated film to form an uncured clear coated film; and a step V in which the uncured intermediate coated film, base coated film, and clear coated film are simultaneously heated and cured; wherein
the cationic electrodeposition coating composition is a lead-free cationic electrodeposition coating composition which comprises an aqueous medium, a binder resin composed of a cationic epoxy resin and a blocked isocyanate curing agent dispersed or dissolved in the aqueous medium, a neutralizing acid in order to neutralize the cationic epoxy resin, an organic solvent, and a metal catalyst, and which has a volatile organic content of 1% by weight or less, a metal ion content of 500 ppm or less, a neutralizing acid amount of 10 to 30 mg equivalent based on 100 g of binder resin solid content, and
the base coating composition comprises a resin component composed of 10 to 70% by weight solid based on total resin solid of a hydroxyl group containing resin (d), 10 to 70% by weight of a curing agent reactable with hydroxyl group (e), 5 to 50% by weight of a nonaqueous dispersion resin (f), with the proviso (d)+(e)+(f)=100%, and a pigment component.
9. The process for forming a layered coated film according to claim 8 , wherein the metal ion of the lead-free cationic electrodeposition coating composition is one or more selected from the group consisting of cerium ion, bismuth ion, copper ion, zinc ion, molybdenum ion, and aluminium ion.
10. The process for forming a layered coated film according to claim 8 , wherein the neutralizing acid of the lead-free cationic electrodeposition coating composition is one or more selected from the group consisting of acetic acid, lactic acid, formic acid, and sulfamic acid.
11. The process for forming a layered coated film according to claim 8 , wherein the lead-free cationic electrodeposition coating composition further comprises a pigment in a ratio of 1/9 or less by weight based on a resin solid contained in the coating composition.
12. The process for forming a layered coated film according to claim 8 , wherein the base coating composition has a volume shrinkage ratio of not more than 45% in the case of being heated at 140° C. for 30 minutes.
13. The process for forming a layered coated film according to claim 9 , wherein the base coating composition comprises 1 to 60% by weight based on solid in the coating composition of a pigment.
14. The process for forming a layered coated film according to claim 8 , wherein the base coating composition has a nonvolatile solid content of 30 to 60% by weight.
15. A process for forming a layered coated film comprising: a step I in which an electrodeposition coated film is formed on a substrate to be coated by an electrodeposition coating process with using a cationic electrodeposition coating composition, and the electrodeposition coated film is heated to form a cured electrodeposition coated film; a step II in which an intermediate coating composition is applied to the cured electrodeposition coated film to form an uncured intermediate coated film; a step III in which a base coating composition is applied to the uncured intermediate coated film to form an uncured base coated film; a step IV in which a clear coating composition is applied to the uncured base coated film to form an uncured clear coated film; and a step V in which the uncured intermediate coated film, base coated film, and clear coated film are simultaneously heated and cured; wherein
the cationic electrodeposition coating composition is a lead-free cationic electrodeposition coating composition which comprises an aqueous medium, a binder resin composed of a cationic epoxy resin and a blocked isocyanate curing agent dispersed or dissolved in the aqueous medium, a neutralizing acid in order to neutralize the cationic epoxy resin, an organic solvent, and a metal catalyst, and which has a volatile organic content of 1% by weight or less, a metal ion content of 500 ppm or less, a neutralizing acid amount of 10 to 30 mg equivalent based on 100 g of binder resin solid content, and
the intermediate coating composition comprises a resin component composed of 10 to 70% by weight solid based on total resin solid of a hydroxyl group containing resin (a), 10 to 70% by weight of a curing agent reactable with hydroxyl group (b), 18 to 50% by weight of a nonaqueous dispersion resin (c), with the proviso (a)+(b)+(c)=100%, and a pigment component, and
the base coating composition comprises a resin component composed of 10 to 70% by weight solid based on total resin solid of a hydroxyl group containing resin (d), 10 to 70% by weight of a curing agent reactable with hydroxyl group (e), 5 to 50% by weight of a nonaqueous dispersion resin (f), with the proviso (d)+(e)+(f)=100%, and a pigment component.
16. The process for forming a layered coated film according to claim 15 , wherein the metal ion of the lead-free cationic electrodeposition coating composition is one or more selected from the group consisting of cerium ion, bismuth ion, copper ion, zinc ion, molybdenum ion, and aluminium ion.
17. The process for forming a layered coated film according to claim 15 , wherein the neutralizing acid of the lead-free cationic electrodeposition coating composition is one or more selected from the group consisting of acetic acid, lactic acid, formic acid, and sulfamic acid.
18. The process for forming a layered coated film according to claim 15 , wherein the lead-free cationic electrodeposition coating composition further comprises a pigment in a ratio of 1/9 or less by weight based on a resin solid contained in the coating composition.
19. The process for forming a layered coated film according to claim 15 , wherein the intermediate coating composition has a volume shrinkage ratio of not more than 45% in the case of being heated at 140° C. for 30 minutes.
20. The process for forming a layered coated film according to claim 15 , wherein the intermediate coating composition comprises 10 to 70% by weight based on solid in the coating composition of a pigment.
21. The process for forming a layered coated film according to claim 15 , wherein the intermediate coating composition has a nonvolatile solid content of 40 to 70% by weight.
22. The process for forming a layered coated film according to claim 15 , wherein the base coating composition has a volume shrinkage ratio of not more than 45% in the case of being heated at 140° C. for 30 minutes.
23. The process for forming a layered coated film according to claim 15 , wherein the base coating composition comprises 1 to 60% by weight based on solid in the coating composition of a pigment.
24. The process for forming a layered coated film according to claim 15 , wherein the base coating composition has a nonvolatile solid content of 30 to 60% by weight.