Method of repairing a ceramic coating
View Patent ↗It is a method of repairing a ceramic coating of an article after use of this article in a high temperature environment disclosed. The ceramic coating is removed locally at spalled areas, at the areas where the ceramic coating is removed locally a mixture including a powder of zirconia stabilized with one or a combination of yttria, calcia, scandia, magnesia, ceria and oxides of the rare earth group, and hydrated metallic halides as a binder is applied and the applied ceramic powder is dried.
1. A method of repairing a ceramic coating of an article after damage due to the transport after manufacture or use of the article in a high temperature environment, the method comprising:
removing remnants of the ceramic coating adjacent to and inside of area of an area of spallation to form a repair area;
preparing the repair area for local coating application by a process selected from the group consisting of chemical treatment, abrasive cleaning, and combinations thereof;
applying a mixture on the repair area, the mixture including a powder of zirconia stabilized with a stabilizer selected from the group consisting of yttria, calcia, scandia, magnesia, ceria, oxides of the rare earth group, and combinations thereof, the mixture including hydrated metallic halides as a binder;
after applying said mixture, drying the applied mixture.
2. The method of claim 1 , further comprising;
preparing said mixture as a slurry with water, optionally water in combination with alcohol, wherein said hydrated metallic halides comprises hydrated aluminum chlorides, before said applying.
3. The method of claim 2 , wherein drying comprises drying the slurry at a temperature between 20° C. and 100° C. and finally heat-treated at a temperature between 55° C. and 750°C.
4. The method of claim 2 , wherein preparing said mixture further comprises including hollow zirconia a spheres in said mixture.
5. The method of claim 1 , wherein said hydrated metallic halide binder a component selected from the group consisting of hydrated aluminum chloride, hydrated halides of magnesium, calcium, yttrium, zirconium, strontium, or barium, hydrated halides of the rare earth group, group 11 alkaline halides, and combinations thereof.
6. The method of claim 1 , wherein the sizes of individual powder particles of the stabilized zirconia powder ranges from 5 to 150 m.
7. The method of claim 1 , wherein applying comprises applying said mixture by a process selected from the group consisting of painting, slurry spraying, and as a paste.
8. The method of claim 1 , wherein the article comprises a part of a gas turbine engine including a nickel or cobalt base alloy exposed to a high temperature environment coated with TBC.
9. The method of claim 8 , wherein said part of a gas turbine engine is selected from the group consisting of a turbine blade and a turbine vane.
10. The method of claim 1 , wherein abrasive cleaning comprises a process selected from the group consisting of grit blasting and grinding.