Granted Patent B2

US 6,846,535 · App. 10/130,371 · Granted Jan 25, 2005

Abstract

Claims (27)

1. A kink resistant medical tube, manufactured from a polymer composition comprising

a) a random polypropylene copolymer; and

b) a block copolymer comprising at least two vinyl aromatic polymer blocks and at least one hydrogenated conjugated diene polymer block, wherein the hydrogenated conjugated diene polymer block has a vinyl content before hydrogenation of at least 50 mol %;

wherein no kinking occurs when the tube is bent to a circumference of greater than 13 cm.

2. The kink resistant medical tube according to claim 1 , wherein said random polypropylene copolymer contains from 0.5 to 10 weight percent of ethylene or butylene.

3. The kink resistant medical tube according to claim 2 , wherein the block copolymer is a linear triblock copolymer of the structure ABA, wherein A is a styrene polymer block and B is a hydrogenated conjugated diene polymer block.

4. The kink resistant medical tube according to claim 3 , wherein the hydrogenated conjugated diene polymer block is a hydrogenated butadiene polymer block.

5. The kink resistant medical tube according to claim 4 , wherein the hydrogenated butadiene polymer block has a vinyl content of from 60 to 70% before hydrogenation.

6. The kink resistant medical tube according to claim 1 , wherein the weight ratio between random polypropylene copolymer and block copolymer in the polymer corriposition is from 80:20 to 30:70.

7. The kink resistant medical tube according to claim 6 , also containing between 5 and 50 parts by weight of a medicinal oil per 100 parts by weight of the total weight of said block copolymer and random polypropylene copolymer.

8. The kink resistant medical tube of claim 2 wherein said random polypropylene copolymer is a propylene/ethylene copolymer having a melt flow rate of 10 to 13 dg/min as measured according to ASTM D1238.

9. The kink resistant medical tube of claim 8 wherein said random polypropylene copolymer has an ethylene content of 2 to 8 weight percent.

10. The kink resistant medical tube of claim 5 wherein the total number average molecular weight of said block copolymer is from 50,000 to 150,000.

11. The kink resistant medical tube of claim 1 wherein:

a) said block copolymer is a linear ABA block copolymer wherein said A block is a polystyrene block, and said B block is a hydrogenated butadiene polymer block having a vinyl content of 60 to 70 mol percent prior to hydrogenation, said ABA block copolymer having a total number average molecular weight of 50,000 to 150,000; and

b) said random polypropylene copolymer is a propylene/ethylene random copolymer having an ethylene content of 2 to 8 weight percent and a melt flow rate of 10 to 13 dg/min as measured according to ASTM D1238.

12. A kink resistant medical tube manufactured from a polymer composition consisting essentially of

a) a random polypropylene copolymer having an ethylene content of 2 to 8 weight percent;

b) a block copolymer comprising at least two vinyl aromatic polymer blocks and at least one hydrogenated conjugated diene polymer block having a vinyl content before hydrogenation of 50 to 70 mol %; and

c) from 0 to 50 parts by weight of a medicinal oil per 100 parts by weight of the total weight of said block copolymer and random polypropylene;

wherein no kinking occurs when the tubs is bent to a circumference of greater than 13 cm.

13. The kink resistant medical tube according to claim 12 , wherein the hydrogenated conjugated diene polymer block is a hydrogenated butadiene block.

14. The kink resistant medical tube according to claim 13 , wherein the hydrogenated butadiene polymer block has a vinyl content of from 60 to 70% before hydrogenation.

15. The kink resistant medical tube according to claim 13 , wherein the hydrogenated butadiene polymer black has a vinyl content of from 65 to 70% before hydrogenation.

16. The kink resistant medical tube according to claim 12 wherein the weight ratio between the random polypropylene copolymer and block copolymer in the polymer composition is from 80:20 to 30:70.

17. The kink resistant medical tube according to claim 12 wherein the said block copolymer is a linear ABA block copolymer having a total number average molecular weight of 50,000 to 150,000, and wherein said A block is a polystyrene block, and said B block is a hydrogenated polybutadiene block.

18. The kink resistant medical tube according to claim 12 wherein the random polypropylene copolymer has a melt flow rate of 10 to 13 dg/min as measured according to ASTM D1238.