VAD manufacture of optical fiber preforms with improved deposition control
View Patent ↗The specification describes a VAD method for dynamically controlling the growth rate of both the core soot and the cladding soot in response to separate growth monitors.
1. Process for the manufacture of a preform of silica particles the soot preform having a core region and a cladding region comprising:
(a) pulling a support rod;
(b) simultaneously depositing core soot on the support rod and cladding soot on the core soot, wherein the core soot is deposited by:
(i) forming core soot by flowing together: a flow of glass precursor gases, a flow of hydrogen, and a flow of oxygen, to form a first gas mixture, igniting the first gas mixture to form core soot,
(ii) depositing the core soot on the support rod to form the core region of the preform,
(iii) continuously monitoring the rate of deposition of soot in the core region to produce a core monitor signal, and the cladding soot is deposited by:
(iv) forming cladding soot by flowing together: a flow of glass precursor gases, a flow of hydrogen, and a flow of oxygen, to form a second gas mixture, igniting the second gas mixture to form cladding soot,
(v) depositing the cladding soot onto the core soot to form the cladding region of the preform,
(vi) continuously monitoring the rate of deposition of soot in the cladding region to produce a cladding monitor signal.
2. The process of claim 1 wherein the glass precursor gases in the first gas mixture comprise SiCl 4 and GeCl 4 .
3. The process of claim 2 wherein the second gas mixture comprises SiCl 4 , hydrogen and oxygen.
4. The process of claim 1 wherein movement of the support rod is controlled by the core monitor signal.
5. The process of claim 1 wherein the second gas mixture is adjusted in response to the cladding monitor signal.
6. The process of claim 1 wherein the second gas mixture is adjusted in response to the sum of the core monitor signal and the cladding monitor signal.
7. The process of claim 1 wherein the first gas mixture is adjusted in response to the core monitor signal and the second gas mixture is adjusted in response to the cladding monitor signal.
8. The process of claim 1 wherein the rate of deposition of soot in the core region and the rate of deposition of soot in the cladding region are both monitored using a laser beam.
9. The process of claim 1 further including heating the soot preform to consolidate the soot into a solid glass preform.
10. The process of claim 1 wherein step (a) is controlled by both step (iii) and step (vi).
11. Process for the manufacture of optical fibers comprising:
(a) preparing a preform, the preform having a core region and a cladding region comprising pulling a support rod and simultaneously depositing core soot on the support rod and cladding soot on the core soot, wherein the core soot is deposited by:
(i) forming core soot by flowing together: a flow of glass precursor gases, a flow of hydrogen, and a flow of oxygen, to form a first gas mixture, igniting the first gas mixture to form core soot,
(ii) depositing core soot onto the support rod to form the core region of the preform,
(iii) continuously monitoring the rate of deposition of soot in the core region to produce a core monitor signal,
(iv) forming cladding soot by flowing together: a flow of glass precursor gases, a flow of hydrogen, and a flow of oxygen, to form a second gas mixture, igniting the second gas mixture to form cladding soot,
(v) depositing the cladding soot onto the core soot to form the cladding region of the preform,
(vi) continuously monitoring the rate of deposition of soot in the cladding region to produce a cladding monitor signal,
(vii) heating the preform to consolidate the preform into solid glass,
(b) mounting the preform in an optical fiber drawing apparatus,
(c) heating the preform to soften the glass, and
(d) drawing an optical fiber from the preform.