Method for making one-container rigid foam
View Patent ↗A method of making a one-container foam by dissolving a polymer in liquified gas at a pressure greater than the vapor pressure of the liquified gas and than rapidly decreasing the pressure within approximately 60 seconds to foam a foam. The foam can be rigid and also have adhesive properties. The liquified gas used is CF 3 l or mixtures thereof.
1. A method of making a one-container foam, comprising:
dissolving at least one polymer in a liquefied gas with vapor pressure p v to form a mixture in a sealable container at elevated pressure P; and
vaporizing the liquefied gas by decreasing the elevated pressure P to a value below p v to form a one-container foam.
2. The method of claim 1 wherein said polymer is selected from polystyrene, a polystyrene copolymer, a poly(alphamethylstyrene), a poly(methylmethacrylate), a poly(n-butyl methacrylate), a poly(isobutylmethacrylate), a poly(t-butylaminoethylmethacrylate), a styrene ethylene-butylene triblock copolymer, a styrene-ethylene-butylene copolymer, a styrene-butadiene-styrene triblock copolymer, a styrene-isoprene-styrene triblock copolymer, a polybutadiene, a methacrylate copolymer, polyisoprene, polyethylene oxide, an epoxy polymer and a polyurethane polymer.
3. The method of claim 2 wherein the polystyrene copolymer is a polystyrene/butadiene copolymer.
4. The method of claim 2 wherein the methacrylate copolymer is a polybutylmethacrylate/isobutyl methacrylate copolymer.
5. The method of claim 1 wherein the liquefied gas comprises CF 3 l and mixtures thereof.
6. The mixture of claim 5 wherein the liquefied gas comprises a mixture of CF 3 l and a miscible gas cosolvent that is not a solvent for said polymer.
7. The method of claim 1 wherein the liquefied gas comprises a mixture of CF 3 l and CF 3 CFH 2 .
8. The method of claim 1 wherein the elevated pressure P is greater than approximately 100 psi.
9. The method of claim 1 wherein the elevated pressure P is less than approximate 150 psi.
10. The method of claim 1 wherein the mixture is heated to a temperature of less than approximately 60° C.
11. The method of claim 2 wherein the polystyrene has a molecular weight of greater than approximately 200,000 grams/mole.
12. The method of claim 2 wherein the polystyrene has a molecular weight of less than approximately 300,000 grams/mole.
13. The method of claim 1 wherein said mixture further comprises a plasticizer.
14. The method of claim 13 wherein said plasticizer is selected from the group consisting essentially of diethylene glycol dibenzoate, dipropylene glycol dibenzoate, polyethylene glycol 200 dibenzoate, dimethyl isophthalate, tetrahydrofurfuryl oleate, chloroparaffin, 2-ethylhexyl di-phenylphosphate, tricresyl phosphate, triphenyl phosphate, butyl benzyl phthalate, butyl octal phthalate, dicapryl phthalate, di-(2-ethylhexyl) phthalate, diethyl phthalate, diisobutyl phthalate, disodecyl phthalate, diisooctyl phthalate, dimethyl phthalate, ditridecyl phthalate, dibutyl sebacate, di-(2-ethylhexyl sebacate), dimethyl sebacate, n-butyl stearate, and n-ethyl-o,p-toluene sulfonamide.
15. The method of claim 1 wherein said mixture further comprises a surfactant.
16. The method of claim 1 wherein said mixture further comprises a lubricant.
17. The method of claim 16 wherein said lubricant is a fluorosurfactant.
18. The method of claim 1 wherein said one-container foam is inflammable.
19. The method of claim 1 wherein said at least one polymer is formed from mixing a diepoxy compound with a diamine curative.
20. The method of claim 1 wherein said at least one polymer is formed front mixing a diisocyanate with a diol.
21. The method of claim 1 wherein said one-container foam functions as a spray adhesive.
22. The method of claim 1 wherein said one-container foam is formed within less than approximately 60 seconds.
23. The method of claim 1 wherein the elevated pressure P is achieved by adding an inert gas to the sealable container.