Radically curable urethane prepolymers and their use in dental materials
View Patent ↗The invention relates to urethane prepolymers, obtainable by reaction of: (A) 15 to 85 wt.-% of one or more α,ω-terminated poly(meth)acrylate diols, (B) 0 to 30 wt.-% of one or more radically curable, polyhydroxy-functional compounds, (C) 14 to 60 wt.-% of one or more polyisocyanates, (D) 1 to 40 wt.-% of a monofunctional compound, reactive vis-à-vis isocyanate groups, which also contains one or more radically curable grouping, as well as their use.
1. A radically curable urethane prepolymer, obtained by reaction of:
(A) 15 to 85 wt % of one or more α, ω-terminated poly(meth)acrylate diols,
(B) 0 to 30 wt % of one or more radically curable, polyhydroxy-functional compounds,
(C) 14 to 60 wt % of one or more polyisocyanates,
(D) 1 to 40 wt % of a monofunctional compound, reactive with isocyanate groups, which also comprises one or more radically curable groupings,
wherein the weight percentage is of the total reaction mixture, and further wherein the radically curable urethane prepolymer contains a di- or higher radically curable functionality.
2. The radically curable urethane prepolymer according to claim 1 , wherein component (B) is present, and in which the component (B) exhibits an OH number from 40 to 700 mg KOH/g.
3. The radically curable urethane prepolymer according to claim 1 , in which the component B, is present and is selected from the group consisting of polyhydroxy-group-containing polyester(meth)acrylate prepolymers, polyhydroxy-group-containing polyepoxy(meth)acrylate prepolymers and polyhydroxy-group-containing polyurethane(meth)acrylate prepolymers.
4. The radically curable urethane prepolymer according to claim 1 , in which the component (C) is an aliphatic, cycloaliphatic or aromatic compound having at least two free isocyanate groups.
5. The radically curable urethane prepolymer according to claim 2 , in which the component (C) is an aliphatic, cycloaliphatic or aromatic compound having at least two free isocyanate groups.
6. The radically curable urethane prepolymer of claim 1 , in which the component (C) is at least one diisocyanate X(NCO) 2 , X being selected from the group consisting of an aliphatic hydrocarbon radical with 2 to 12 C atoms, a cycloaliphatic hydrocarbon radical with 5 to 18 C atoms, an aromatic hydrocarbon radical with 6 to 16 C atoms and an araliphatic hydrocarbon radical with 7 to 15 C atoms.
7. The radically curable urethane prepolymer of claim 2 , in which the component (C) is at least one diisocyanate X(NCO) 2 , X being selected from the group consisting of an aliphatic hydrocarbon radical with 2 to 12 C atoms, a cycloaliphatic hydrocarbon radical with 5 to 18 C atoms, an aromatic hydrocarbon radical with 6 to 16 C atoms and an araliphatic hydrocarbon radical with 7 to 15 C atoms.
8. The radically curable urethane prepolymer of claim 3 , in which the component (C) is at least one diisocyanate X(NCO) 2 , X being selected from the group consisting of an aliphatic hydrocarbon radical with 2 to 12 C atoms, a cycloaliphatic hydrocarbon radical with 5 to 18 C atoms, an aromatic hydrocarbon radical with 6 to 16 C atoms and an araliphatic hydrocarbon radical with 7 to 15 C atoms.
9. The radically curable urethane prepolymer of any one of claims 1 to 8 , in which the component (D) comprises a hydroxy group and, as a radically curable group, at least one (meth)acrylate group.
10. A composition comprising:
(C1) 1 to 70 wt % of at least one radically curable urethane prepolymer according to claim 1 ,
(C2) 8.9 to 70 wt % of one or more radically polymerizable monomers,
(C3) 10 to 90 wt % of at least one filler,
(C4) 0.1 to 5 wt % of at least one initiator, and optionally at least one activator,
(C5) 0 to 30 wt % of one or more additives, and optionally pigments, thixotropic auxiliaries and plasticizers;
in which the wt % is a percentage of the total weight of the composition.
11. The composition according to claim 10 , in which component (C2) comprises at least one mono-, di- and/or higher-functional acrylic acid ester, at least one mono-, di- and/or higher-functional methacrylic acid ester, or both.
12. The composition according to claim 11 , in which the acrylic acid ester, methacrylic acid ester or both comprise monomeric, oligomeric or polymeric acrylates, or a mixture thereof.
13. A kit for the preparation of dental materials comprising at least one cartouche with at least two chambers filled with a composition according to one of claims 10 to 12 , and optionally including an applicator for the dispensing of dental materials, and/or optionally including a static mixing set.
14. A composition according to one of claims 10 to 12 that has been cured.
15. An applicator, comprising at least one cartouche that contains a composition according to one of claims 10 to 12 .
16. A method for making a dental filling material, stump build-up material, fixing cement, temporary dental crown material, temporary dental bridge material, dental material, model material, inlay, onlay, facing shell, dental crown or dental bridge comprising polymerizing a composition according to claim 10 .
17. A method for making a dental filling material, stump build-up material, fixing cement, temporary dental crown material, temporary dental bridge material, dental material, model material, inlay, onlay, facing shell, dental crown or dental bridge comprising mixing a radically curable urethane prepolymer according to claim 1 with at least one of:
a) at least one radically polymerizable monomer,
b) at least one filler,
c) at least one initiator, and optionally at least one activator, and
of one or more additives, and optionally pigments, thixotropic auxiliaries and plasticizers, and polymerizing the mixture.
18. A method for gluing or coating a substrate comprising applying the prepolymer of claim 1 to the substrate and polymerizing the prepolymer.
19. A method for preparing a molded article comprising filling a mold with the prepolymer of claim 1 and polymerizing the prepolymer.