Ink for golf ball
View Patent ↗A golf ball 1 has a core 2 , a cover 3 , a mark layer 4 , and a finishing coat layer 5 . An ink used for the mark layer 4 includes an isocyanate curing agent that contains a diisocyanate trimer, a base material, and a colorant. Preferred curing agent contains an isophorone diisocyanate trimer. The ink includes a diisocyanate curing agent at equal to or greater than 1% by weight and equal to or less than 20% by weight, calculated on the basis of the solid content. The base material includes a polymer having a hydroxyl group as a principal component. The “NCO/OH” value, which is a ratio of isocyanate groups of the isocyanate curing agent and hydroxyl groups of the base material, is equal to or greater than 0.5 and equal to or less than 2.0. The mark layer 4 may be printed on a base coat layer, alternatively, may be printed on a crosslinked rubber. This ink has excellent adhesiveness to a base.
1. A golf ball having a mark layer, said mark layer is formed from an ink which comprises an isocyanate curing agent that contains a diisocyanate trimer, a base material and a colorant.
2. The golf ball according to claim 1 wherein the base of the mark layer is a crosslinked rubber containing polybutadiene as a principal component, or a resin composition containing an ionomer resin as a principal component.
3. The golf ball according to claim 1 wherein the ink has a percentage content of the isocyanate curing agent that is equal to or greater than 1% by weight and equal to or less than 20% by weight, which is calculated on the basis of the solid content.
4. The golf ball according to claim 1 wherein the diisocyanate trimer in the ink is an isophorone diisocyanate trimer.
5. The golf ball according to claim 1 wherein the base material in the ink comprises a polymer having a hydroxyl group as a principal component.
6. The ink for a golf ball according to claim 5 wherein “NCO/OH” value, which is a ratio of isocyanate groups of the isocyanate curing agent and hydroxyl groups of the base material, is equal to or greater than 0.5 and equal to or less than 2.0.