High yields, high purity melamine manufacturing process
View Patent ↗The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquors of melamine crystallisation comprising the following steps: a) addition to a melamine and OAT containing aqueous solution at high temperature of an alkaline agent until the solution pH reach a value equal or higher than 11; b) most of melamine crystallisation by solution cooling; c) separation and recovery of precipitated melamine; d) acidification of the obtained solution, after precipitated melamine separation, in order to reach a pH of about 7; e) the suspension obtained in d) above after precipitated melamine recovery, is subject to filtration according to tangential filtration technique obtaining a clear permeate which contains as a solution all melamine which did not precipitate in step b) and a retentate comprising of OAT dispersion; f) OAT deprived mother liquors from e) are recycled to row melamine solution preparation step; in such a way almost the total amount of melamine, which did not precipitate in step b), is recovered; g) OAT are recovered from step e) retentate by using any conventional separation technics.
1. A process to recover bosh melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization comprising the following steps:
a) adding an alkaline agent to a melamine and OAT containing aqueous solution at high temperature until a pH of a resulting solution reaches a value of at least approximately 11;
b) crystallizing at least a portion of the melamine to obtain precipitated melamine by cooling the resulting solution;
c) separating and recovering the precipitated melamine from the mother liquor;
d) acidifying the mother liquor with a suitable acid to reach a pH of approximately 7 resulting in precipitation of the OAT to obtain a suspension;
e) filtering the suspension using tangential filtration to obtain a permeate containing all of the melamine not precipitated in step b) and a retentate comprising an OAT dispersion having an OAT concentration at least fifteen times an original OAT concentration;
f) recycling the permeate to recover an amount of melamine not precipitated in step b); and
g) recovering OAT from the retentate.
2. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 1 wherein the alkaline agent solution treatment of stage a) takes place at a temperature higher than approximately 130° C.
3. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 1 wherein the melamine is crystallized in step b) by cooling the solution to a temperature in the range of approximately 40° to 50° C.
4. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 1 wherein the pH in step d) is between approximately 6.5 and 7.5.
5. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 1 wherein a surface filtering material is used for tangential filtration and is resistant to pressure and chemical agents.
6. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 1 wherein a surface filtering material is used for tangential filtration and is selected from among alumina, silico-alumina, zirconia, titania, boria, zeolites, thoria and mixtures thereof.
7. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 6 wherein the surface filtering material used for tangential filtration according step e) comprises a high purity alumina.
8. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 1 wherein a surface filtering material is used for tangential filtration and exhibits a porosity lower than 5 micron.
9. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 8 wherein the surface filtering material used for tangential filtration exhibits a porosity lower than 0.2 micron.
10. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 8 wherein the surface filtering material used for tangential filtration exhibits a porosity in the range of 20 to 100 nanometers.
11. A process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization comprising the following steps:
a) adding an alkaline agent to a melamine and OAT containing aqueous solution at high temperature until a pH of a resulting solution reaches a value of at least approximately 11;
b) crystallizing at least a portion of the melamine to obtain precipitated melamine by cooling the resulting solution;
c) separating and recovering the precipitated melamine from the mother liquor;
d) acidifying the resulting solution to reach a pH of about 7 resulting in precipitation of the OAT to obtain a suspension;
e) filtering the suspension using tangential filtration to obtain a permeate containing all of the melamine not precipitated in step b), and a retentate comprising an OAT dispersion having an OAT concentration at least fifteen times an original OAT concentration;
f) recycling the permeate to recover an amount of melamine not precipitated in step b); and
g) recovering OAT from the retentate.
12. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 11 wherein the melamine is crystallized in step b) by cooling the solution to a temperature in the range of approximately 40° to 50° C.
13. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 12 wherein the pH in step d) is between approximately 6.5 and 7.5.
14. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 13 wherein a surface filtering material is used for tangential filtration and is resistant to pressure and chemical agents.
15. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 14 wherein a surface filtering material is used for tangential filtration and is selected from among alumina, silico-alumina, zirconia, titania, boria, zeolites, thoria and mixtures thereof.
16. The process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization according to claim 15 wherein the surface filtering material used for tangential filtration according step e) comprises a high purity alumina.
17. In a process to recover both melamine and oxyaminotriazines (OAT) from the mother liquor of melamine crystallization comprising the following steps:
a) adding an alkaline agent to a melamine and OAT containing aqueous solution at high temperature until a pH of a resulting solution reaches a value of at least approximately 11;
b) crystallizing at least a portion of the melamine to obtain precipitated melamine by cooling the resulting solution;
c) separating and recovering the precipitated melamine from the mother liquor;
d) acidifying the mother liquor with a suitable acid to reach a pH of approximately 7 resulting in precipitation of the OAT to obtain a suspension;
e) separating the suspension obtained in d) to obtain a permeate comprising as a solution all of the melamine not precipitated in step b) and a retentate comprising an OAT in form of a colloidal precipitate; and
f) recovering OAT from the retentate, the improvement comprising:
using a tangential filtration, as a separation technology according to step e), resulting in an OAT concentration in the retentate being maintained at a value of at least fifteen times an original OAT concentration.