Polyol compositions useful for preparing dimensionally stable, low density water-blown rigid foams and the processes related thereto
View Patent ↗The present invention relates to polyol compositions which can be used to produce dimensionally stable, low density water-blown rigid foams which have acceptable compressive strengths and acceptable k-factors. In one embodiment of the present invention, the polyol compositions are composed of at least one aromatic amine-initiated polyether polyol and at least one polyether polyol having a functionality greater than or equal to 2.5 in which at least 50% by weight of the polyol composition is aromatic amine-initiated polyether polyol and in which no more than 50% by weight of the polyol composition is polyether polyol having a functionality greater than or equal to 2.5. In another embodiment of the present invention, the polyol compositions are composed of at least one aromatic amine-initiated polyether polyol and at least one polyester polyol in which at least 30% by weight of the polyol composition is aromatic amine-initiated polyether polyol and in which no more than 70% by weight of the polyol composition is polyester polyol.
1. A process for preparing a low density, solely water-blown rigid polyurethane foam consisting of reacting:
(1) a polyol composition composed of:
1.) at least 30% by weight, based on the total weight of the polyol composition, of at least one aromatic amine-initiated polyether polyol having a hydroxyl number of from greater than 200 to about 405; and
2.) at least one of the following:
(i) up to 50% by weight, based on the total weight of the polyol composition of a polyether polyol having a functionality greater than or equal to 2.5 which is different from the polyether polyol of 1.); and
(ii) up to 70% by weight, based on the total weight of the polyol composition, of a polyester polyol; with
(2) at least one isocyanate; in the presence of
(3) optionally, at least one catalyst;
(4) water; and
(5) optionally, at least one additive or auxiliary agent selected from internal mold release agents, pigments, cell regulators, flame retarding agents, plasticizers, dyes, fillers or reinforcing agents
wherein the low density, solely water-blown rigid polyurethane foam produced has a closed cell content of at least 80%.
2. The process of claim 1 in which 78% by weight of the polyol composition, based on the total weight of the polyol composition, is aromatic amine-initiated polyether polyol and in which 22% by weight of the polyol composition, based on the total weight of the polyol composition, is polyether polyol having a functionality greater than or equal to 2.5.
3. The process of claim 1 in which 40% by weight of the polyol composition, based on the total weight of the polyol composition, is aromatic amine-initiated polyether polyol and in which 60% by weight, based on the total weight of the polyol composition, is polyester polyol.
4. The process of claim 1 in which 75% by weight of the polyol composition, based on the total weight of the polyol composition, is aromatic amine-initiated polyether polyol and in which 25% by weight, based on the total weight of the polyol composition, is polyester polyol.
5. The process of claim 1 in which the aromatic amine-initiated polyether polyol is produced with o-toluenediamine as a starter.
6. A low density, solely water-blown rigid polyurethane foam produced by reacting:
(1) a polyol composition composed of:
1.) at least 30% by weight, based on the total weight of the polyol composition, of at least one aromatic amine-initiated polyether polyol having a hydroxyl number of from areater than about 200to about 405; and
2.) at least one of the following:
(i) up to 50% by weight, based on the total weight of the polyol composition of a polyether polyol having a functionality greater than or equal to 2.5 which is different from the polyether polyol of 1.); and
(ii) up to 70% by weight, based on the total weight of the polyol composition, of a polyester polyol; with
(2) at least one isocyanate; in the presence of
(3) optionally, at least one catalyst;
(4) water; and
(5) optionally, at least one additive or auxiliary agent selectedJrom internal mold release agents, pigments, cell regulators, flame retarding agents, plasticizers, dyes, fillers or reinforcing agents
wherein the low density, solely water-blown rigid polyurethane foam produced has a closed cell content of at least 80%.
7. The foam of claim 6 which has a density of from about 1 to about 3.0 lbs/ft 3 .
8. The foam of claim 6 which exhibits less than a 10% volume change when stored at 100° C. and at ambient humidity for twenty-four hours.
9. The foam of claim 6 which exhibits less than a 10% volume change when stored at 70° C. and at 100% relative humidity for twenty-four hours.
10. The foam of claim 6 which has a parallel compressive strength within the range of from about 35 to about 50 lbs/in 2 .