Crosslinkable polyethylene composition
View Patent ↗Composition based on a crosslinkable polyethylene comprising from 0.05 to 0.24 hydrolysable silane groups per 100 —CH 2 — units and having a standard density SD of at least 954 kg/m 3 and a melt flow index MI 5 of less than 1.5 g/10 min. Pipes for the transportation of fluids under pressure, which can be obtained by extruding this composition and then hydrolysing it.
1. A pipe based on a crosslinkable polyethylene comprising from 0.05 to 0.24 hydrolysable silane groups per 100 —CH 2 — units and having a standard density SD of at least 954 kg/m 3 , a melt flow index MI 5 of less than 1.5 g/10 min and a melt flow index HLMI of greater than 2 g/10 min.
2. The pipe according to claim 1 , wherein the crosslinkable polyethylene has a melt flow index MI 2 of less than 0.8 g/10 min and greater than 0.03 g/10 min.
3. The pipe according to claim 1 , wherein the crosslinkable polyethylene has a content of hydrolysable silane groups such that, after hydrolysis, the crosslinked polyethylene has a degree of crosslinking of at least 65% by weight.
4. The pipe according to claim 1 , wherein it is obtained by the melt blending of a base polyethylene having an SD of at least 956 kg/m 3 , an MI 2 of greater than 0.15 g/10 min and an MI 5 of less than 10 g/10 min with from 1.0 to 2.5 parts per 100 parts of base polyethylene of a vinylsilane and from 0.04 to 0.15 part per 100 parts of base polyethylene of a compound capable of generating free radicals.
5. The pipe according to claim 4 , wherein the base polyethylene has an SD of at least 958 kg/m 3 .
6. The pipe according to claim 4 , wherein the base polyethylene has a melt flow index MI 2 of less than 2 g/10 min and greater than 0.16 g/10 min.