High performance fire-retardant kraft facing for fiberglass insulation
View Patent ↗A process for preparing a fiberglass insulation product, including the steps of: (a) providing a layer of fire-retardant kraft paper, (b) coating the fire-retardant kraft paper layer with from 2 to 10 pounds of HDPE or of polypropylene per 3000 square feet of the paper to form an HDPE-fire-retardant kraft laminate or a polypropylene-fire-retardant kraft laminate, (c) coating the HDPE-fire-retardant kraft or polypropylene-fire-retardant kraft laminate with from 3 to 10 pounds of LDPE per 3000 square feet of the HDPE-fire-retardant kraft laminate or polypropylene-fire-retardant kraft laminate to form an LDPE-HDPE-fire-retardant kraft laminate or an LDPE-polypropylene-fire-retardant kraft laminate, (d) adjusting the temperature of the LDPE-HDPE-fire-retardant kraft laminate or the LDPE-polypropylene-fire-retardant kraft laminate so that the LDPE becomes tacky while the HDPE or polypropylene remains solid, (e) providing a layer of fiberglass wool, and (f) contacting the LDPE layer of the LDPE-HDPE-fire-retardant kraft laminate or of the LDPE-polypropylene-fire-retardant kraft laminate with the fiberglass wool layer with pressure and cooling to bond the LDPE-HDPE-fire-retardant kraft laminate or LDPE-polypropylene-fire-retardant kraft laminate to the fiberglass wool layer to form a fiberglass insulation product.
1. A process for preparing a fiberglass insulation product which comprises the steps of:
(a) providing a layer of fire-retardant kraft paper,
(b) coating the fire-retardant kraft paper layer with a high melting point polymer to form a high melting point polymer-fire-retardant kraft laminate,
(c) coating the high melting point polymer-fire-retardant kraft laminate with a low melting point polymer to form a low melting point polymer-high melting point polymer-fire-retardant kraft laminate,
(d) adjusting the temperature of the low melting point polymer-high melting point polymer-fire-retardant kraft laminate so that the low melting point polymer becomes tacky while the high melting point polymer remains solid,
(e) providing a layer of fiberglass wool, and
(f) contacting the low molting point layer of the low melting point polymer-high melting point polymer-fire-retardant kraft laminate with the fiberglass wool layer with pressure and cooling to bond said low melting point polymer-high melting point polymer-fire-retardant kraft laminate to said fiberglass wool layer to form a fiberglass insulation product.
2. The process of claim 1 wherein said high melting point polymer is high density polyethylene (HDPE) or polypropylene.
3. The process of claim 2 wherein said low melting paint polymer is low density polyethylene (LDPE).
4. The process of claim 3 which comprises the steps of:
(b) coating the fire-retardant kraft paper layer with from 2 to 10 pounds of HDPE or polypropylene per 3000 square feet of said paper to form the HDPE-fire-retardant kraft laminate or polypropylene-fire-retardant kraft laminate, and
(c) coating the HDPE-fire-retardant kraft laminate or polypropylene-fire-retardant kraft laminate with from 3 to 10 pounds of LDPE per 3000 square feet of said HDPE-fire-retardant kraft laminate or polypropylene-kraft laminate to form the LDPE-HDPE-kraft laminate or LDPE-polypropylene-fire-retardant kraft laminate.
5. The process of claim 1 wherein the temperature is adjusted with an infra-red heater, a microwave heater, or a rotating hot roll.
6. A fiberglass insulation product comprising a layer of fiberglass wool and a flexible planar laminate comprising in sequence an external support layer of fire-retardant kraft paper to which is adhered a central vapor barrier layer of high density polyethylene (HDPE) or polypropylene to which is adhered an internal adhesive layer of low melting point polymer.
7. The fiberglass insulation product of claim 6 wherein the high melting polymer is high density polyethylene (HDPE) or polypropylene.
8. The fiberglass insulation product of claim 7 wherein the low melting point polymer is low density polyethylene (LDPE).
9. The fiberglass insulation product of claim 8 in which the flexible planar laminate comprises from 2 to 10 pounds of HDPE and from3 to 10 pounds of LDPE per 3000 square feet of fire-retardant kraft paper having a weight of 30 to 50 lbs/ft 2 .
10. The fiberglass insulation product of claim 7 in which the flexible planar laminate comprise 7 pounds of HDPE and 5 pounds of LDPE per 3000 square feet of fire-retardant kraft paper having a weight of 30 to 50 lbs/ft 2 .
11. A fiberglass insulating product consisting essentially of:
a flexible planar laminate including, in sequence,
a layer of kraft paper, the kraft paper having an outer surface and an inner surface,
a vapor barrier layer consisting essentially of a high melting point polymer provided on the inner surface of the kraft paper, and
an adhesive layer consisting essentially of a low melting point polymer provided on the vapor barrier layer, and
a layer of fiberglass wool having an inner surface and an outer surface, the inner surface being adhered to the adhesive layer.
12. A fiberglass insulating product according to claim 11 , further consisting essentially of:
a second layer of kraft paper, the second layer of kraft paper being adhered to the outer surface of the layer of fiberglass wool.
13. A fiberglass insulating product according to claim 11 , further consisting essentially of:
a second flexible planar laminate including, in sequence,
an adhesive layer consisting essentially of a low melting point polymer adhered to the outer surface of the layer of fiberglass wool,
a vapor barrier layer provided on the adhesive layer opposite the layer of fiberglass wool, and
a layer of kraft paper having an outer surface and an inner surface, wherein the inner surface contacts the vapor barrier layer.