High sensitivity, directional dc-SQUID magnetometer
View Patent ↗A solid state dc-SQUID includes a superconducting loop containing a plurality of Josephson junctions, wherein an intrinsic phase shift is accumulated through the loop. In an embodiment of the invention, the current-phase response of the dc-SQUID sits in a linear regime where directional sensitivity to flux through the loop occurs. Changes in the flux passing through the superconducting loop stimulates current which can be quantified, thus providing a means of measuring the magnetic field. Given the linear and directional response regime of the embodied device, an inherent current to phase sensitivity is achieved that would otherwise be unobtainable in common dc-SQUID devices without extrinsic intervention.
1. A method of producing a SQUID magnetometer, comprising:
depositing a seed layer on a substrate;
depositing a first buffer layer on the seed layer;
etching the seed layer and the first buffer layer to form a boundary separating (i) a first portion having the seed layer and the first buffer and, (ii) a second portion where the seed layer and the first buffer are substantially removed, wherein the boundary includes a first part and a second part and wherein the first part of the boundary is not collinear with the second part of the boundary;
depositing a second buffer layer on the second portion;
depositing a superconducting material on the first buffer layer and the second buffer layer; and
etching the superconducting material to form a SQUID loop across said boundary thereby forming said SQUID magnetometer, the SQUID loop comprising a plurality of Josephson junctions, wherein
a first Josephson junction in the plurality of Josephson junctions is defined by the first part of the boundary, and
a second Josephson junction in the plurality of Josephson junctions is defined by the second part of the boundary.
2. The method of claim 1 , wherein the substrate is of sapphire.
3. The method of claim 1 , wherein the substrate is of SrTiO 3 .
4. The method of claim 1 , wherein the seed layer is of MgO.
5. The method of claim 1 , wherein the first buffer layer is of CeO 2 .
6. The method of claim 1 , wherein the second buffer layer is of CeO 2 .
7. The method of claim 1 , wherein the superconducting material is YBa 2 Cu 3 O 7−x where x is greater than or equal to 0 and less than about 0.6.
8. The method of claim 1 , wherein the superconducting material is Bi 2 Sr 2 Ca n−1 Cu n O 2n−4, where n is an integer.
9. The method of claim 1 , wherein the superconducting material is Sr 2 RuO 4 .
10. The method of claim 1 , wherein depositing the seed layer is performed bi-epitaxially.
11. The method of claim 1 , wherein depositing the first buffer layer is performed bi-epitaxially.
12. The method of claim 1 , wherein depositing the second layer is performed bi-epitaxially.
13. The method of claim 1 , wherein depositing the superconducting material is performed bi-epitaxially.
14. The method of claim 1 , wherein etching the seed layer and the first buffer layer is accomplished with a milling process.
15. The method of claim 1 , wherein etching the superconducting material is accomplished with a milling process.
16. The method of claim 1 wherein a superconducting current in the SQUID loop experiences an accumulated intrinsic phase shift over the path of the SQUID loop.
17. The method of claim 1 wherein,
the first part of the boundary is perpendicular to a current path in the SQUID loop, and
the second part of the boundary is not perpendicular to a current path in the SQUID loop.
18. The method of claim 17 wherein the first Josephson is a π/2-phase shift grain boundary Josephson junction and the second Josephson junction is a 0-junction.