View Patent ↗In order to remove or decrease fine granular sulfides of Mn, Cr, Mo, etc. (Mn—S, Cr—S, Mo—S, etc.) left on a machined workpiece surface of sulfur free-cutting alloy steel without affecting the form and dimensional accuracy thereof, there is provided a method for treating the sulfur free-cutting alloy steel which comprises a soaking process of the machined workpiece in a solvent and an ultrasonic cleaning process by applying ultrasonic waves of 1.0 to 2.0 W/cm 2 in watt density at a frequency of 40 KHz or a multi frequency in the solvent.
1. A method of treating a machined workpiece of a sulfide-containing free-cutting alloy steel to remove granular sulfides of Mn, Cr and Mo from a surface thereof, comprising the steps of: soaking a machined workpiece of the sulfide-containing free-cutting alloy steel in an aqueous solvent consisting of water or water containing a member selected from the group consisting of an oxidizing agent, an acid, an alkaline agent and a salt, the aqueous solvent containing water having a dissolved oxygen content of no more than 3 ppm; and applying ultrasonic waves having a watt density of 1.0 to 2.0 W/cm 2 and a frequency of 40 kHz or superimposed ultrasonic waves of multi-frequencies of 25-300 kHz to the solvent containing the workpiece following the soaking step.
2. The method of claim 1 , wherein the aqueous solvent contains at least one member selected from the group consisting of an oxidizing agent, an acid, an alkaline agent and a salt.
3. The method of claim 1 , additionally comprising a step of degreasing the workpiece to remove a cutting oil from a surface thereof prior to the soaking step.
4. The method of claim 1 , additionally comprising the steps of rinsing the workpiece after the ultrasonic waves have been applied thereto and drying the rinsed workpiece.
5. The method of claim 1 , wherein the ultrasonic waves are applied to the solvent at a frequency of 40 kHz.
6. The method of claim 1 , wherein superimposed ultrasonic waves are applied to the solvent at multi-frequencies of 25-300 kHz.
7. The method of claim 1 , wherein the aqueous solvent is water.
8. The method of claim 1 , wherein the aqueous solvent is water containing a member selected from the group consisting of an oxidizing agent, an acid, an alkaline agent and a salt.