Monofilament suture and manufacturing method thereof
The present invention relates to a monofilament suture prepared by co-extruding polymers having different Young's moduli and to a process for preparing the same. The suture is prepared in such a form that a polymer having a high Young's modulus surrounds a polymer having a low Young's modulus. The monofilament suture prepared by the present invention has excellent knot security, flexibility and/or knot strength.
1. A monofilament suture, having improved knot security and flexibility, comprising a first absorbable polymer and a second absorbable polymer having a Young's modulus lower than the Young's modulus of the first polymer said first polymer is co-extruded with said second polymer forming a sea/island type suture comprising a plurality of islands wherein the first polymer is the sea component and the second polymer is the island component, and wherein the Young's modulus of the first polymer and the second polymer is 3.0 GPa or less, and wherein the difference of the Young's modulus between the first polymer and the second polymer is 0.3 GPa or more.
2. The monofilament suture of claim 1 , wherein the amount of the first polymer is 10 to 90% by volume and the amount of the second polymer is 10 to 90% by volume.
3. The monofilament suture of claim 1 , wherein the amount of the first polymer is 50 to 90% by volume and the amount of the second polymer is 10 to 50% by volume.
4. The monofilament suture of claim 1 , wherein the first polymer and the second polymer are homopolymers or are copolymers synthesized from monomers selected from the group consisting of glycolide, glycolic acid, lactide, lactic acid, caprolactone, dioxanone, trimethylene carbonate and ethyleneglycol.
5. The monofilament suture of claim 4 , wherein the first polymer is a homopolymer or is a copolymer synthesized from monomers selected from the group consisting of glycolide, glycolic acid, dioxanone and lactide.
6. The monofilament suture of claim 4 , wherein the second polymer is a homopolymer or is a copolymer synthesized from monomers selected from the group consisting of caprolactone, trimethylene carbonate, DL-lactide and ethylene glycol.
7. The monofilament suture of claim 1 , wherein the melting point of the first polymer is higher than the melting point of the second polymer.
8. The monofilament suture of claim 1 , wherein the Young's modulus of the first polymer is 2.0 GPa or less and the Young's modulus of the second polymer is 1.5 GPa or less.
9. The monofilament suture of claim 8 , wherein the Young's modulus of the first polymer is 1.0˜1.5 Gpa and the Young's modulus of the second polymer is 1.2 GPa or less.
10. The monofilament suture of claim 9 , wherein the Young's modulus of the second polymer is 0.4˜1.2 GPa.