Intermetallic compound superconductors and alloy superconductors, and method for their preparation
View Patent ↗There are provided an intermetallic compound superconductor that is high in superconducting transition temperature, and an alloy superconductor that is high in superconducting transition temperature and excels in malleability and ductility, as well as a method of making such a superconductor with good reproducibility and at a low cost of manufacture. This entirely new intermetallic compound superconductor is made of magnesium (Mg) and boron (B) and has a chemical composition expressed by formula: Mg 1 B 2 , has a hexagonal AlB 2 type crystallographic structure and has a superconducting transition temperature (T c ) of 39 K. An alloy containing this intermetallic compound excels in malleability and ductility and constitutes the alloy superconductor having a superconducting transition temperature (T c ) of 39 K. In the method of manufacture, a Mg containing feedstock powder and a B containing feedstock powder are mixed together to form a mixture thereof which is, e.g., hot pressed to produce a semiconductor product.
1. A method of conducting electrical current, comprising the steps of:
providing an intermetallic compound superconductor of a composition expressed by chemical composition formula: Mg 1 B 2 and having a hexagonal AlB 2 type crystallographic structure in which a Mg layer and a B layer lie alternately; and
bringing said compound superconductor to a temperature of 39 K or lower, and
passing electrical current through said compound superconductor.
2. A method of conducting electrical current, comprising the steps of: forming an intermetallic compound superconductor by the steps of:
mixing a Mg containing feedstock powder and a B containing feedstock powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=1/2,
shaping said mixture powder into the form of a pellet, and
heating said pellet in an inert gas to form the intermetallic compound superconductor; bringing said intermetallic compound superconductor to a temperature of 39 K or lower; and passing electrical current through said intermetallic compound superconductor.
3. A method of conducting electrical current as set forth in claim 2 , wherein said heating step is conducted at a temperature of 700 to 2000° C. for a period of several seconds or more.
4. A method of conducting electrical current, comprising the steps of: forming an intermetallic compound superconductor by the steps of:
mixing a Mg containing feedstock powder and a B containing feedstock powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=1/2,
shaping said mixture powder into the form of a pellet, and
heating said pellet in a vacuum to form the intermetallic compound superconductor; bringing said intermetallic compound superconductor to a temperature of 39 K or lower; and passing electrical current through said intermetallic compound superconductor.
5. A method of conducting electrical current as set forth in claim 4 , wherein said heating step is conducted under a pressure of 2×10 −2 Pa or less at a temperature of 650 to 1100° C. for a period of several minutes or more.
6. A method of conducting electrical current, comprising the steps of: forming an intermetallic compound superconductor by the steps of:
mixing a Mg containing feedstock powder and a B containing feedstock powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=1/2,
shaping said mixture powder into the form of a pellet, and
heating said pellet in a pressurized inert gas to form the intermetallic compound superconductor; bringing said intermetallic compound superconductor to a temperature of 39 K or lower; and passing electrical current through said intermetallic compound superconductor.
7. A method of conducting electrical current as set forth in claim 6 , wherein said heating step is conducted under a pressure of 1 to 200 MPa at a temperature of 600 to 1100° C. for a period of several minutes or more.
8. A method of conducting electrical current, comprising the steps of: forming an intermetallic compound superconductor by the steps of:
mixing a Mg containing feedstock powder and a B containing feedstock powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=1/2,
shaping said mixture powder into the form of a pellet, and
pressing and heating said pellet to form the intermetallic compound superconductor; bringing said intermetallic compound superconductor to a temperature of 39 K or lower, and passing electrical current through said intermetallic compound superconductor.
9. A method of conducting electrical current as set forth in claim 8 , wherein said pressing and heating step is conducted under a pressure of 0.1 to 6 GPa at a temperature of 700 to 1400° C. for a period of several minutes or more.