Flame-resistant polycarbonate molding compounds for extrusion applications
View Patent ↗A molding composition characterized by its improved processability and flame resistance, suitable especially for extrusion is disclosed. The composition that contains polycarbonate, an impact modifier and a halogen-free phosphous-containing flameproofing agent features flame resistance of V-0 in the UL 94 V fire behavior test at wall thickness ≦1.5 mm and a melt viscosity, measured at 260° C. and a shear rate of 100 s 1 , of ≧600 Pa s
1. A molding composition consisting of
(i) at least one branched or linear polycarbonate derived from at least one compound selected from a the group consisting of resorcinol, dihydroxydiphenols, bis-(hydroxyphenyl)-C 1 -C 5 -alkanes, bis-(hydroxyphenyl)-C 5 -C 6 -cycloalkanes, bis-(hydroxyphenyl) ethers, bis-(hydroxyphenyl) sulfoxides, bis-(hydroxyphenyl) ketones, bis-(hydroxyphenyl)-sulfones and α,α-bis-(hydroxyphenyl)-diisopropyl-benzenes, said polycarbonate having relative solution viscosity ≧1.30 (measured at 25° C. in methylene chloride and in a concentration of 0.5 g/100 ml),
(ii) at least one impact modifier,
(iii) at least one halogen-free phosphorus-containing flameproofing agent selected from the second group consisting of compounds conforming to (A) and (B) wherein
(A) is
and (B) is
wherein R 1 , R 2 , R 3 and R 4 are each independently of the others C 1 - to C 8 -alkyl, or C 5 - to C 6 -cycloalkyl, C 6 - to C 20 -aryl or C 7 - to C 12 -aralky each optionally substituted by alkyl, n are each independently of the others 0 or 1, N represents a number from 0.7 to 5, X represents a mono- or poly-nuclear aromatic radical having from 6 to 30 carbon atoms, or linear or branched aliphatic radical having from 2 to 30 carbon atoms which may be OH-substituted and contain up to 8 ether bonds, q independently one of the others denotes 0,1, 2, 3 or 4,
R 5 and R 6 independently one of the other denote C 1 C 4 -alkyl, and Y represents C 1 -C 7 -alkylidene, C 1 -C 7 -alkylene, C 5 -C 12 -cycloalkyl C 5 -C 12 -cycloalkylidene, —O—, —S—, —SO—, SO 2 or —CO—, and optionally
(iv) one or more members selected from the third group consisting of anti-dripping agent, lubricant and mold-release agent, nucleating agent, antistatic, stabilizer, coloring agent and pigment,
said composition characterized in its UL 94 V-0 flammability rating at wall thicknesses ≦1.5 mm and a melt viscosity, measured at 260° C. and a shear rate of 100 s −1 , of ≧600 Pa s.
2. The molding composition according to claim 1 wherein the flameproofing agent conforms to
3. The molding composition of claim 1 wherein the anti dripping agent is present in an amount of 0.15 to 1 wt. % based on the total composition.
4. The molding composition of claim 3 wherein the anti dripping agent is fluorinated polyolefin, optionally in the form of a coagulate, a pre-compound or a masterbatch with a graft polymer or a vinyl (co)polymer.
5. The molding composition of claim 1 wherein the anti dripping agent is present in an amount of 0.2 to 0.5 wt. % based on the total composition.
6. Moulding compositions according to claim 1 wherein the impact modifier is one or more graft polymers of from 5 to 95 wt. % of at least one vinyl monomer with from 95 to 5 wt. % of at least one graft base having a glass transition temperature <10° C.
7. Moulding compositions according to claim 6 containing graft polymers based on diene, EP(D)M, acrylate or silicone rubbers.
8. The molding composition of claim 6 wherein the graft polymer is an emulsion or mass ABS or mixtures thereof.
9. The molding composition of claim 1 wherein the polycarbonate is branched.
10. The molding composition of claim 4 wherein the polycarbonate is present in an amount of 60 to 98 wt. %, the impact modifier is present in an amount of 0.5 to 30 wt. %, the flameproofing agent is present in an amount of 1 to 20 wt. % , and the fluorinated polyolefin is present in an amount of 0.15 to 1 wt. % the sum of the wt. % of the components being 100.
11. The molding composition of claim 4 wherein the polycarbonate is present in an amount of 75 to 90 wt. %, the impact modifier is present in an amount of 2 to 10 wt. %, the flameproofing agent is present in an amount of 3 to 12 wt. %, and the fluorinated polyolefin is present in a amount of 0.2 to 0.5 wt. % the sum of the wt. % of the components being 100.
12. Process for the preparation of the moulding compositions according to claim 1 , wherein the individual components are mixed and compounded at 200 to 300° C.
13. Moulded bodies or mouldings as well as profiles, sheets, tubes and conduits for electrical installations obtainable from the moulding compositions according to claim 1 .