View Patent ↗A method of producing boards or panels from cereal straw includes the steps of treating and mechanically refining the straw with steam under elevated pressure which may be in excess of 8 bar (800 kPa). The resulting fiber may then be pressed in to boards or panels without added binder or mixed with a urea formaldehyde or melamine urea formaldehyde binder.
1. A method of producing boards or panels comprising cereal straw, said method comprising the steps of:
(a) cutting the straw crosswise;
(b) treating the straw with steam under elevated pressure;
(c) mechanically refining the straw in a steam pressurized refiner;
(d) mixing the straw fibers with a UF or MUF resin; and
(e) pressing the straw fiber/resin mixture into boards or panels.
2. The method of claim 1 wherein said steam pressure in either step (b) or step (c), or both, is above about 600 kpa.
3. The method of claim 2 wherein said steam pressure is above about 800 kPa.
4. The method of claim 3 wherein said steam pressure is above about 1000 kPa.
5. The method of claim 1 wherein the straw is cut by being hammermilled to lengths less than about 25 mm.
6. The method of claim 1 wherein the straw is mechanically refined with a specific energy consumption of less than about 500 kWh per ton of oven dry straw.
7. The method of claim 6 wherein the straw is mechanically refined with a specific energy consumption of less than about 300 kWh per ton of oven dry straw.
8. The method of claim 1 further comprising the step of adding an acid to said straw fibres after refining the straw and prior to mixing the straw fiber with the resin.
9. A method of producing boards or panels comprising cereal straw, said method comprising the steps of:
(a) cutting the straw crosswise to lengths less than about 25 mm;
(b) treating the straw with steam under pressure in excess of about 1000 kPa;
(c) mechanically refining the straw in a steam pressurized refiner; and
(d) pressing the straw fiber into boards or panels, without binder.
10. The method of claim 9 wherein the straw is mechanically refined with a specific energy consumption of less than about 500 kWh per ton of oven dry straw.
11. The method of claim 10 wherein the straw is mechanically refined at an intensity of less than about 300 kWh per ton of oven dry straw.
12. A board formed without added binder and comprising straw fibre produced from straw treated with steam under pressure in excess of about 1000 kPa and mechanically refined in a steam pressurized refiner.
13. A method of producing boards or panels comprising cereal straw, said method comprising the steps of:
(a) cutting the straw crosswise;
(b) treating and mechanically refining the straw with steam under elevated pressure until the straw fibre pH is less than about 5.5;
(c) pressing the straw fiber into boards or panels, with added UF or MUF binder, or without an added binder.
14. The method of claim 12 wherein the straw is treated and refined with steam under elevated pressure until the straw fibre pH is less than about 5.0.
15. The method of claim 13 wherein the straw fiber is pressed into boards or panel without added resin or binder.